Microstructural Study on the Stress Corrosion Cracking of Alloy 690 in Simulated Pressurized Water Reactor Primary Environment

  • Wenjun KuangEmail author
  • Miao Song
  • Chad M. Parish
  • Gary S. Was
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

This study was aimed at investigating the intergranular attack near a stress corrosion crack (SCC) of alloy 690 in simulated pressurized water reactor (PWR) primary water environment. Solution annealed alloy 690 was evaluated for its SCC initiation susceptibility in 360 °C hydrogenated pure water using slow strain rate tensile technique. After the test, a grain boundary showing SCC initiation was sampled with Focused Ion Beam (FIB) milling. The microstructure and elemental distribution near the crack tip were studied using transmission electron microscopy (TEM) and scanning transmission electron microscopy (STEM). The results show that intergranular oxidation occurs ahead of the crack tip and is preceded by diffusion induced grain boundary migration. The oxides at the crack tip are mainly composed of NiO and Cr2O3 which maintain rigid orientations with the neighboring grains. The adjacent migration zone is free of oxidization as a compact layer of Cr2O3 dominates at the oxide/substrate interfaces and the very tip region.

Keywords

Alloy 690 SCC PWR Intergranular oxidation Boundary migration 

Notes

Acknowledgements

The authors gratefully acknowledge financial support through the DOE I-NERI program contract 2011-01-K. The authors would like to thank Young Suk Kim and Sung Soo Kim from Korea Atomic Energy Research Institute for providing the materials for this study, and Alex Flick from the University of Michigan for his assistance with preparation of the high temperature autoclave systems. This research was performed, in part, using instrumentation provided by the Department of Energy, Office of Nuclear Energy, Fuel Cycle R&D Program and the Nuclear Science User Facilities.

References

  1. 1.
    K. Smith et al., Inconel 690: A Material with Improved Corrosion Resistance for PWR Steam Generator Tubes, in Proceedings of the Second International Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (American Nuclear Society, Monterey, California, 1985), pp. 319–328Google Scholar
  2. 2.
    K. Norring, J. Engstrom, and P. Norberg, Intergranular Stress Corrosion Cracking in Steam Generator Tubing. Testing of Alloy 690 and Alloy 600 Tubes, in Proceedings of the 3rd International Symposium Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors (Traverse City, Michigan, 1987), p. 587Google Scholar
  3. 3.
    J.J. Kai, C.H. Tsai, G.P. Yu, The IGSCC, sensitization, and microstructure study of Alloys 600 and 690. Nucl. Eng. Des. 144, 449–457 (1993)CrossRefGoogle Scholar
  4. 4.
    W. Kuang, G.S. Was, The effects of grain boundary carbide density and strain rate on the stress corrosion cracking behavior of cold rolled Alloy 690. Corros. Sci. 97, 107–114 (2015)CrossRefGoogle Scholar
  5. 5.
    M.B. Toloczko, M.J. Olszta, and S.M. Bruemmer, One dimentional cold rolling effects on stress corrosion crack growth in Alloy 690 tubing and plate materials, in 15th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-water reactors, Colorado Springs, Colorado, USA, 2011, pp. 91–106Google Scholar
  6. 6.
    K. Arioka et al., Dependence of stress corrosion cracking of alloy 690 on temperature, cold work, and carbide precipitation—role of diffusion of vacancies at crack tips. Corrosion 67, 035006-1–035006-18 (2011)CrossRefGoogle Scholar
  7. 7.
    D.J. Paraventi, W.C. Moshier, Primary water stress corrosion crack growth in cold worked Alloy 690 plate, in 16th international conference on environmental degradation of materials in nuclear power systems-water reactors, Asheville, North Carolina, USA, 2013Google Scholar
  8. 8.
    P.L. Andresen, M.M. Morra, K. Ahluwalia, Effect of deformation temperature, orientation and carbides on SCC of Alloy 690, in 16th international conference on environmental degradation of materials in nuclear power systems-water reactors, Asheville, North Carolina, USA, 2013Google Scholar
  9. 9.
    L.E. Thomas, S.M. Bruemmer, High-resolution characterization of intergranular attack and stress corrosion cracking of alloy 600 in high-temperature primary water. Corrosion 56, 572–587 (2000)CrossRefGoogle Scholar
  10. 10.
    S.M. Bruemmer, L. Thomas, in Insights into Stress Corrosion Cracking Mechanisms from High-Resolution Measurements of Crack-tip Structures and Compositions, MRS Proceedings, p. 1264 (2010)Google Scholar
  11. 11.
    M. Sennour, P. Laghoutaris, C. Guerre, R. Molins, Advanced TEM characterization of stress corrosion cracking of Alloy 600 in pressurized water reactor primary water environment. J. Nucl. Mater. 393, 254–266 (2009)CrossRefGoogle Scholar
  12. 12.
    Y.S. Lim, H.P. Kim, S.S. Hwang, Microstructural characterization on intergranular stress corrosion cracking of Alloy 600 in PWR primary water environment. J. Nucl. Mater. 440, 46–54 (2013)CrossRefGoogle Scholar
  13. 13.
    T.E. Moss, Stress corrosion crack initiation of alloy 600 and alloy 690 in hydrogenated supercritical water (Ph.D. thesis, The University of Michigan, 2015)Google Scholar
  14. 14.
    W. Kuang, G.S. Was, The effects of strain rate and carbon concentration on the dynamic strain aging of cold rolled Ni-based alloy in high temperature water. Scripta Mater. 107, 107–110 (2015)CrossRefGoogle Scholar
  15. 15.
    M.J. Olszta et al., Alloy 690 surface nanostructures during exposure to PWR primary water and potential influence on stress corrosion crack initiation, in The 16th international conference on environmental degradation of materials in nuclear power systems-water reactors, Asheville, North Carolina, USA, 2013Google Scholar
  16. 16.
    M.J. Olszta et al., Penetrative internal oxidation from alloy 690 surface and stress corrosion crack walls during exposure to PWR primary water, in 15th Int. Conf. on Environmental Degradation of Materials in Nuclear Power Systems-water reactors, Colorado Springs, Colorado, USA, 2011. pp. 331–342Google Scholar
  17. 17.
    R.W. Balluffi, J.W. Cahn, Mechanism for diffusion induced grain boundary migration. Acta Metall. 29, 493–500 (1981)CrossRefGoogle Scholar
  18. 18.
    T. Moss, G.S. Was, Accelerated Stress Corrosion Crack Initiation of Alloys 600 and 690 in Hydrogenated Supercritical Water. Metall. Mat. Trans. A, 1–16 (2017)Google Scholar
  19. 19.
    T. Moss, G. Cao, G.S. Was, Oxidation of alloy 600 and alloy 690: experimentally accelerated study in hydrogenated supercritical water. Metall. Mat. Trans. A, 1–17 (2017)Google Scholar
  20. 20.
    D.K. Schreiber et al., Grain boundary characterization of alloy 600 prior to and after corrosion by atom probe tomography and transmission electron microscopy, in The 16th international conference on environmental degradation of materials in nuclear power systems-water reactors, Asheville, North Carolina, USA, 2013Google Scholar
  21. 21.
    G. Bertali, F. Scenini, M.G. Burke, The effect of residual stress on the preferential intergranular oxidation of alloy 600. Corros. Sci. 111, 494–507 (2016)CrossRefGoogle Scholar
  22. 22.
    D.K. Schreiber, M.J. Olszta, S.M. Bruemmer, Grain boundary depletion and migration during selective oxidation of Cr in a Ni–5Cr binary alloy exposed to high-temperature hydrogenated water. Scripta Mater. 89, 41–44 (2014)CrossRefGoogle Scholar
  23. 23.
    M. Sennour et al., A detailed TEM and SEM study of Ni-base alloys oxide scales formed in primary conditions of pressurized water reactor. J. Nucl. Mater. 402, 147–156 (2010)CrossRefGoogle Scholar
  24. 24.
    W. Kuang et al., The oxidation of alloy 690 in simulated pressurized water reactor primary water. Corros. Sci. 126, 227–237 (2017)CrossRefGoogle Scholar
  25. 25.
    W. Kuang et al., The mechanism of oxide film formation on Alloy 690 in oxygenated high temperature water. Corros. Sci. 53, 3853–3860 (2011)CrossRefGoogle Scholar
  26. 26.
    W. Kuang, X. Wu, E.-H. Han, Influence of dissolved oxygen concentration on the oxide film formed on alloy 690 in high temperature water. Corros. Sci. 69, 197–204 (2013)CrossRefGoogle Scholar
  27. 27.
    B. Beverskog, I. Puigdomenech, Pourbaix diagrams for the ternary system of iron-chromium-nickel. Corrosion 55, 1077–1087 (1999)CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  • Wenjun Kuang
    • 1
  • Miao Song
    • 1
  • Chad M. Parish
    • 2
  • Gary S. Was
    • 1
  1. 1.Department of Nuclear Engineering and Radiological SciencesUniversity of MichiganAnn ArborUSA
  2. 2.Oak Ridge National Laboratory, Materials Science and Technology DivisionOak RidgeUSA

Personalised recommendations