Recent Development of Chemical Resistant Styrenic Polymers for the Refrigerator

  • Kyung H. Ahn
  • Sang S. Woo

Abstract

Environmental issue on ozone layer destruction is regulating the use of CFC11, which is known as a Freon gas, depending on the economic level of each country. All the materials and the processes using CFC11 have been destined for change. Refrigerator is an example. As a blowing agent, CFC11 has long been used. Recently HCFC-141b and cyclopentane are being used as alternatives. However, the former deteriorates the mechanical properties of current plastics and liners in the refrigerator, while the latter does not harm the material but very explosive. Novel material is under development, but still not commercial. Feasible way is to increase the chemical resistance of the plastic parts, which is mostly made of acrylonitrile-butadiene-styrene (ABS) resin, enough to resist the chemical attack of HCFC-141b. In this paper, the change of blowing agents and new technologies to enhance the chemical resistance of styrenic polymers will be presented. First, historical perspectives on the environmental issues will be summarized. The requirements of styrenic polymers for the new blowing agents will also be mentioned. And then, the key technologies to enhance the chemical resistance of ABS resin, and the accompaning problems as well as the way to evaluate the chemical resistance of a plastic will be discribed. Finally, future prospects for the styrenic polymers in relation to the refrigerator industry will be mentioned.

Keywords

Critical Strain Chemical Resistance Rubber Particle Monomer Composition Styrenic Polymer 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
  2. 2.
  3. 3.
  4. 4.
    Y. Aoki and K. Nakayama, Dynamic viscoelastic properties of ABS polymers in the molten state III. Effects of the composition of grafted AS copolymer, J. Soc.Rheol.Jpn. 9: 39 (1981).Google Scholar
  5. 5.
    M. Bertin, G. Marin, and J. Montfort, Viscoelastic properties of acrylonitrile-butadienestyrene (ABS) polymers in the molten state, Polym.Eng.Sci. 35(17): 1394 (1995).CrossRefGoogle Scholar
  6. 6.
    Y. Aoki, Dynamic viscoelastic properties of ABS polymers in the molten state. 5. Effect of grafting degree, Macromolecules 20: 2208 (1987).CrossRefGoogle Scholar
  7. 7.
    M.C.O. Chang and R.L. Nemeth, Rubber particle agglomeration phenomena in acrylonitrile-butadiene-styrene (ABS) polymers. II. Rubber particle agglomeration elucidated by a thermodynamic theory, J. Polym.Sci. B: Polym.Phys. 35: 553 (1997).CrossRefGoogle Scholar
  8. 8.
    R. Hasegawa, Y. Aoki, and M. Doi, Optimum graft density for dispersing particles in polymer melts, Macromolecules 29: 6656 (1996).CrossRefGoogle Scholar
  9. 9.
    ASTM D 543: Standard test method for resistance of plastics to chemical reagents. 10. ASTM F1248: Standard test method for determination of environmental stress crack resistance (ESCR) of polyethylene pipe.Google Scholar
  10. 11.
    T.J. Stolki, Environmental stress and strain testing, SPE Journal, Oct. 48 (1967).Google Scholar
  11. 12.
    R.R. Dixon, Environmental stress testing of ABS materials, SPE-ANTEC 12: XXIX–2 (1966).Google Scholar
  12. 13.
    C.J. Singleton, E. Roche, and P.H. Geil, Environmental stress cracking of polyethylene, J. Appl.Polym.Sci. 21: 2319 (1977).CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media New York 1998

Authors and Affiliations

  • Kyung H. Ahn
    • 1
  • Sang S. Woo
    • 2
  1. 1.R&D Center, Chemicals DivisionCheil Industries Inc.Kyoungki-DoKorea
  2. 2.R&D CenterSamsung General Chemicals Co., Ltd.TaejeonKorea

Personalised recommendations