Advances in Cryogenic Engineering Materials pp 541-546 | Cite as
Magnetic Properties of the YBaCuO-System Superconductors
Chapter
Abstract
A large single domain of the Ag-doped YBaCuO-system superconductor was prepared. To estimate the effect of the Ag adding, the Jc and the trapped magnetic field were measured. The entire sample was uniformly magnetized and the trapped magnetic field formed a single dome shape. The Jc value decreased with the increase of the Ag content. The decrease rate of the Jc value was calculated by assuming that the Ag was not effective in the flux pinning. The calculated decrease rate is approximately equal to the experimental results.
Keywords
Magnetic Bearing Flux Pinning Trap Magnetic Flux Trap Magnetic Field Single Dome
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.
Preview
Unable to display preview. Download preview PDF.
References
- 1.Y. Yanagi, Y. Itoh, T. ()ka, H. Tanaka, S. Takashima, Y. Yamada and U. Mizutani. Advances in Superconductivity 5, Proc of the 5th International Symposium on Superconductivity (ISS’92), Springer-Verlag (1992) 799.Google Scholar
- 2.F. Mizuno, H. Masada, 1. Hirabayashi and S. Tanaka, Jpn. J. Appt. Phys., 28. (1989) L780.Google Scholar
- 3.S. Kohayashi, S. Yoshizawa, N. Hirano, S. Nagaya and It. Kojima, Phvsica U., 234 (1995) 249.ADSGoogle Scholar
- 4.C. P. Bean, Phys. Rev. Lett., 8 (1989) 250.Google Scholar
- 5.S. Kohayashi, Y. Ishikawa, S. Yoshizawa and H. Kojima. Advances in Superconductivity 3, Proc of the 5th International Symposium on Superconductivity (ISS’92), Springer-Verlag (1992) 795.Google Scholar
- 6.S. Kohayashi, Y. Ishikawa, S. Yoshizawa and H. Kojima, Advances in Superconductivity 5: Proc of the 5th International Symposium on Superconductivity (ISSv)2). Springer-Verlag (1992) 795Google Scholar
Copyright information
© Springer Science+Business Media New York 1998