Thermally Stable Acrylic Polymer for Profile Modification Applications

  • R. G. Ryles
  • R. E. Neff
Chapter

Abstract

Profile modification is a process in which flooding water is diverted from highly permeable zones into less permeable oil-bearing layers within a subterranean reservoir. In recent years this has been achieved by the use of polymeric hydrogels in yhich the water-soluble polymer is cross-linked by a multivalent metal ion1. The latter may be generated in situ from a redox couple, e.g., sodium dichromate/sodium metabisulfite or as a complexed reagent, e.g., aluminum citrate. This enables the gelation process to be retarded until the aqueous polymer solution has been placed deep into the thief zone.

Keywords

Acrylic Acid Storage Modulus Reactivity Ratio Sodium Acrylate Aqueous Polymer Solution 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    J.E. Hessert and P.D. Fleming, “Gelled Polymer Technology for the Control of Water in Injection and Production Wells,” presented at the 3rd Tertiary Oil Recovery Conference, Wichita, April 25–26, 1979.Google Scholar
  2. 2.
    P.M. DiGiacomo and C.M. ?pram, “Mechanism of Polyacrylamide Gel Synthesis Determined by C NMR,” SPE 11787, presented at the International Symposium on Oilfield and Geothermal Chemistry, Denver, CO, June 1–3, 1983.Google Scholar
  3. 3.
    R.G. Ryles and J.V. Cicchiello, “New Polymers for EOR Applications,” SPE/DOE 14947, presented at the 5th Symposium on Enhanced Oil Recovery, Tulsa, OK, April 20–23, 1986.Google Scholar
  4. 4.
    D.W. Behnken, J. Polymer Sci., Vol. 2, 645, (1964).Google Scholar
  5. 5.
    S. Ponratnam and S.L. Kapur, Makromol. Chem., 178, 1029 (1977).CrossRefGoogle Scholar
  6. 6.
    J. Sourdais, Bull. Soc. Chim. Fr., 485, (1955).Google Scholar
  7. 7.
    W.E. Cabaness, T. Yen Chin Lin, C. Parkanyi, J. Poly. Sci., Part A-1, 9, 2155, (1971).CrossRefGoogle Scholar
  8. 8.
    R.K. Prud’homme, J.T. Uhl, J.P. Poinsatte and F. Halverson, Soc. Pet. Eng. J., 23 (5), (1983).Google Scholar
  9. 9.
    Moradi-Araghi, A. and Doe, P.H., “Stability of Polyacrylamides in Harsh Brines at Elevated Temperatures,” SPE 13033 presented at the 59th Annual Technical Conference, Sept. 16–19, 1984.Google Scholar

Copyright information

© Springer Science+Business Media New York 1988

Authors and Affiliations

  • R. G. Ryles
    • 1
  • R. E. Neff
    • 1
  1. 1.Chemical Research LaboratoriesAmerican Cyanamid CompanyStamfordUSA

Personalised recommendations