Structure and Properties of Tire Rubbers Prepared by Anionic Polymerization

  • S. L. Aggarwal
  • I. G. Hargis
  • R. A. Livigni
  • H. J. Fabris
  • L. F. Marker

Abstract

The two functional properties of tire tread rubbers of prime importance today are low rolling resistance and high wet traction during braking. Rolling resistance and wet traction are related to low tan δ and Tg, respectively. In most of the conventional synthetic rubbers, high Tg is accompanied with high tan δ. Studies on polybutadiene rubbers prepared with anionic catalysts showed that the rubbers containing a high percent of vinyl structure provide exceptions to this general rule. This work demonstrates that vinyl groups in vinyl BR’s do not contribute significantly to tan δ in the frequency/temperature regime corresponding to the rubber plateau region. Guided by our results, a number of experimental rubber compositions were developed for tire treads. These compositions have the desirable combination of high traction and low rolling resistance.

Keywords

CROSSLINK Density Rolling Resistance Anionic Polymerization Tire Rubber Rubber Vulcanizate 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    K. H. Nordsiek, Kautsch. Gummi Kunstst., 38, 178 (1983).Google Scholar
  2. 2.
    R. Bond, Proc. Royal Soc., London, A399, 1 (1985).MathSciNetGoogle Scholar
  3. 3.
    N. Yoshimura, M. Okuyama, and K. Yamagishi: Tire Rolling Resistance, D. J. Schuring, ed., Rubber Division Meeting, Am. Chem. Soc., 1983.Google Scholar
  4. 4.
    A. Schallamach, Int. Polym. Sci. Techni., 6, T44, T63 (1975).Google Scholar
  5. 5.
    E. Southern and A. G. Thomas, Rubber Chem. Technol., 52, 1008 (1979).CrossRefGoogle Scholar
  6. 6.
    A. N. Gent and C. T. R. Pulford, J. Appl. Polym. Sci., 28, 943 (1983).CrossRefGoogle Scholar
  7. 7.
    J. D. Ferry, Viscoelastic Properties of Polymers, 2nd ed., Wiley, New York, 1970.Google Scholar
  8. 8.
    H. L. Hsieh, R. C. Farrar, and K. Udipi, in Anionic Polymerization, J. E. McGrath, ed., Symposium Series No. 166, Am. Chem. Soc., Washington, D.C., 1981.Google Scholar
  9. 9.
    I. G. Hargis, R. A. Livigni, and S. L. Aggarwal, in Elastomers and Rubber Elasticity, J. E. Mark and J. Lal, eds., Symposium Series No. 193, Am. Chem. Soc., Washington, D. C., 1982.Google Scholar
  10. 10.
    T. Antkowiak, A. E. Oberster, A. F. Halasa, and D. P. Tate, J. Polym. Sci., Part A-10, 10, 1319 (1972).CrossRefGoogle Scholar
  11. 11.
    D. D. Werstler, Rubber Chem. Technol., 53(5) 1114 (1980).Google Scholar
  12. 12.
    V. D. Mochel and B. L. Johnson, Rubber Chem. Technol., 43(5) 1138 (1970).Google Scholar
  13. 13.
    MTS 830 Elastomer Test System by MTS System Corp., Box 24012, Minneapolis, MN 55424.Google Scholar
  14. 14.
    F. L. Yerzley, Rubber Age, 104, 27 (1972).Google Scholar
  15. 15.
    D. J. Schuring, Rubber Chem. Technol., 53, 600 (1980).Google Scholar
  16. 16.
    British Standards Institution, British Standard No. 903; 1950, part 22, Methods of Testing Vulcanized Rubber, London (1950).Google Scholar
  17. 17.
    J. M. Giustino and R. J. Emerson, Instrumentation of the British Portable Skid Tester, Paper No. 76, 123rd Meeting Rubber Division, Inc., Am. Chem. Soc., May 10–12 (1983).Google Scholar
  18. 18.
    E. W. Duck and J. M. Locke, J. Inst. Rubber Ind., 2(5), 223 (1968).Google Scholar
  19. 19.
    K. H. Nordsiek and K. M. Kiepert, Kautsch. Gummi Kunstst., 33, 251 (1980).Google Scholar
  20. 20.
    R. E. Railsback and N. A. Stumpe, Jr., Rubber Age, 107, 27 (1975).Google Scholar
  21. 21.
    R. G. Mancke and J. D. Ferry, Trans. Soc. Rheol., 12, 335 (1968).CrossRefGoogle Scholar
  22. 22.
    J. M. Carella, W. W. Graessley, and L. J. Fetters, Macromolecules, 17, 2775 (1984).ADSCrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media New York 1986

Authors and Affiliations

  • S. L. Aggarwal
    • 1
  • I. G. Hargis
    • 1
  • R. A. Livigni
    • 1
  • H. J. Fabris
    • 1
  • L. F. Marker
    • 1
  1. 1.GenCorpResearch DivisionAkronUSA

Personalised recommendations