Abstract
Inorganic nanofibers are widely used in wastewater treatment for its excellent chemical corrosion resistance and large specific surface area. In order to meet the requirements for high adsorption effect, the specific surface area of inorganic nanofibers needs to be further improved. In this study, internal dense porous SiO2 nanofibers were prepared using the electrospinning technique combined with the anti-solvent method. The effects of receiving distances on the composite nanofibers’ morphology and diameter were investigated. The diameter distribution and pore size distribution of porous nanofibers were statistically characterized. Results indicated that internal dense porous SiO2 nanofibers could be prepared by electrospinning combined with the anti-solvent method. With the increase of the receiving distance from 10 to 17 cm, the average diameter of the PS/SiO2 composite nanofibers decreased from 1264.4 to 766.8 nm. When the receiving distance was 10 cm, the average diameter of the nanofibers was 906.4 nm and the average surface hole was 181.7 nm after calcination. And the BET surface area of the nanofibers was 78.94 m2/g. Such porous nanofibers have potential applications in adsorbents and oil–water separation.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
S. Barth, Synthesis and applications of one-dimensional semiconductors. Prog. Mater Sci. 55(6), 563–627 (2010)
Y. Tang, Positively charged and flexible SiO2@ZrO2 nanofibrous membranes and their application in adsorption and separation. RSC Adv. 8(23), 13018–13025 (2018)
J. Gao, Facile preparation of hybrid microspheres for super-hydrophobic coating and oil-water separation. Chem. Eng. J. 326, 443–453 (2017)
W. Qin, Fabrication of porous chitosan membranes composed of nanofibers by low temperature thermally induced phase separation, and their adsorption behavior for Cu2+. Carbohyd. Polym. 178, 338–346 (2017)
H. Wang, Synthesis of SnO2 versus Sn crystals within N-doped porous carbon nanofibers via electrospinning towards high-performance lithium ion batteries. Nanoscale 8(14), 7595–7603 (2016)
A. Baji, One-dimensional multiferroic bismuth ferrite fibers obtained by electrospinning techniques. Nanotechnology 22(23), 235702 (2011)
A.E. Danks, The evolution of ‘sol–gel’ chemistry as a technique for materials synthesis. Mater. Horiz. 3(2), 91–112 (2016)
A. Raza, In situ cross-linked superwetting nanofibrous membranes for ultrafast oil–water separation. J. Mater. Chem. A 2(26), 10137–10145 (2014)
A.K. An, PDMS/PVDF hybrid electrospun membrane with superhydrophobic property and drop impact dynamics for dyeing wastewater treatment using membrane distillation. J. Membr. Sci. 525, 57–67 (2017)
H. Fashandi, Pore formation in polystyrene fiber by superimposing temperature and relative humidity of electrospinning atmosphere. Polymer 53(25), 5832–5849 (2012)
J.Y. Park, Preparation of electrospun porous ethyl cellulose fiber by THF/DMAc binary solvent system. J. Ind. Eng. Chem. 13(6), 1002–1008 (2007)
D. Yu, Mesoporous vanadium pentoxide nanofibers with significantly enhanced Li-ion storage properties by electrospinning. Energy Environ. Sci. 4(3), 858–861 (2011)
R. Zhang, Nanoporous fibers built with carbon-bound SiO2 nanospheres via electrospinning and calcination. Mater. Des. 130, 231–238 (2017)
X. Liao, Effect of porous structure on mechanical properties of C/PLA/nano-HA composites scaffold. Frontier Symp. China Postductors Mater. Sci., 748–751 (2009)
G. Arran, The effect of pore structure on the CO2 adsorption efficiency of polyamine impregnated porous carbons. Microporous Mesoporous Mater. 208, 129–139 (2015)
W. Luo, Electrospun porous ZnCo2O4 nanotubes as a high-performance anode material for lithium-ion batteries. J. Mater. Chem. 22(18), 8916–8921 (2012)
M. Bognitzki, Nanostructured fibers via electrospinning. Adv. Mater. 13(1), 70–72 (2001)
S. Megelski, Micro-and nanostructured surface morphology on electrospun polymer fibers. Macromolecules 35(22), 8456–8466 (2002)
H.S. Bae, Fabrication of highly porous PMMA electrospun fibers and their application in the removal of phenol and iodine. J. Polym. Res. 20(7), 1–7 (2013)
Acknowledgements
The authors would like to acknowledge the support from the National Natural Science Foundation of China (No. 51572217), the China Postdoctoral Science Foundation (No. 2015M582689) and the Postdoctoral Science Foundation of Shaanxi Province (No. 2016BSHEDZZ03).
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2019 Springer Nature Singapore Pte Ltd.
About this paper
Cite this paper
Liu, Z., Tang, Y., Chen, W., Zhao, K. (2019). Fabrication of Porous SiO2 Nanofibers by Electrospinning with the Anti-solvent Process. In: Han, Y. (eds) Physics and Techniques of Ceramic and Polymeric Materials. CMC 2018. Springer Proceedings in Physics, vol 216. Springer, Singapore. https://doi.org/10.1007/978-981-13-5947-7_4
Download citation
DOI: https://doi.org/10.1007/978-981-13-5947-7_4
Published:
Publisher Name: Springer, Singapore
Print ISBN: 978-981-13-5946-0
Online ISBN: 978-981-13-5947-7
eBook Packages: Physics and AstronomyPhysics and Astronomy (R0)