Abstract
Quantum-size ZnMgSSe/ZnSe/ZnMgSSe nanostructures were studied by X-ray diffraction analysis. It was found that the ZnMgSSe solid solution decomposes into two phases with close lattice parameters. As the lattice-parameter mismatch between zinc selenide and barrier layers increases, the decomposition is accompanied by simultaneous broadening of peaks of each phase. It was found that almost pure ZnSe grows in the first stages of metastable barrier layer growth, thus thickening the well (ZnSe).
Similar content being viewed by others
References
H. Mariette, F. Dal’bo, N. Magnea, et al., Phys. Rev. B 38, 12443 (1988).
P. Peyla, Y. Merle d’Aubigne, A. Wasiela, et al., Phys. Rev. B 46, 1557 (1992).
C. Hsu Tran Min Duc and J. P. Faurie, Phys. Rev. Lett. 58, 1127 (1987).
T.W. Kim and H. L. Park, J. Cryst. Growth. 159, 467 (1996).
A. D. Katani and G. Margaritongo, Phys. Rev. B 28, 1944 (1983).
S. Itoch, K. Nakano, and A. Ishibashi, J. Cryst. Growth. 214/215, 1029 (2000).
D. C. Grillo, J. Han, M. Ringle, et al., Electron Lett. 30, 2131 (1994).
M. D. Tiberi and I. Kozlovskiy, Proc. SPIE 5740, 60 (2005).
I. P. Kazakov, V. I. Kozlovskii, V. P. Martovitskii, et al., Kvant. Elektron. 37, 857 (2007).
A. C. Tropper, H. D. Foremand, A. Garnache, et al., J. Phys. D 37, R75 (2004).
Author information
Authors and Affiliations
Additional information
Original Russian Text © A.N. Georgobiani, V.P. Martovitskii, E.V. Perlov, V.P. Tokareva, 2010, published in Kratkie Soobshcheniya po Fizike, 2010, Vol. 37, No. 4, pp. 39–44.
About this article
Cite this article
Georgobiani, A.N., Martovitskii, V.P., Perlov, E.V. et al. X-ray diffraction analysis of quantum-size ZnMgSSe/ZnSe/ZnMgSSe nanostructures. Bull. Lebedev Phys. Inst. 37, 119–122 (2010). https://doi.org/10.3103/S1068335610040068
Received:
Published:
Issue Date:
DOI: https://doi.org/10.3103/S1068335610040068