Phase Transformations in an Fe-Based Bulk Amorphous Alloy inside a Ball Mill

  • N. P. DiakonovaEmail author
  • E. A. Zakharova
  • T. A. Sviridova
  • T. R. Chueva


The possibility of using a ball mill to obtain an amorphous state in bulk amorphous Fe61.4Ni3.6Cr3.2Si2.4Nb7.8Mn3.6B18 alloy is studied. The presence of a metastable phase in the initial reagents allows the rate of amorphization to be notably accelerated with an almost full transformation to the amorphous state. Compared to a quench-hardened tape, however, the content of the amorphous state obtained via mechanical milling is distinguished by a reduced content of boron and therefore a lower temperature of crystallization.



  1. 1.
    Inoue, A., Kong, F.L., Zhu, S.L., and Al-Marzouki, F., J. Alloys Compd., 2017, vol. 707, p. 12.CrossRefGoogle Scholar
  2. 2.
    Inoue, A., Acta Mater., 2000, vol. 48, p. 279.CrossRefGoogle Scholar
  3. 3.
    Koch, C.C., J. Non-Cryst. Solids, 1990, vols. 117–118, p. 670.ADSCrossRefGoogle Scholar
  4. 4.
    Bakker, H., Zhou, G.F., and Yang, H., Mater. Sci. Forum, 1995, vols. 179–181, p. 47.CrossRefGoogle Scholar
  5. 5.
    Courtney, T.H., Mater. Trans. JIM, 1995, vol. 36, no. 2, p. 110.CrossRefGoogle Scholar
  6. 6.
    Molokanov, V.V., Shalygin, A.N., Petrzhik, M.I., et al., Perspekt. Mater., 2003, no. 1, p. 5.Google Scholar
  7. 7.
    Vorgol’skaya, M.A., D’yakonova, N.P., Sviridova, T.A., et al., Tezisy dokladov na konferentsii “Strukturnye osnovy modifikatsii materialov metodami netraditsionnykh tekhnologii” (Proc. Conf. “Structural Foundations of Material Modification with Nontraditional Technologies”), Obninsk, 2003, p. 29.Google Scholar
  8. 8.
    Sviridova, T.A., Shelekhov, E.V., Bazilyan, V.I., et al., J. Alloys Compd., 2014, vol. 586, p. 73.CrossRefGoogle Scholar
  9. 9.
    Shelekhov, E.V. and Sviridova, T.A., Met. Sci. Heat Treat., 2000, vol. 42, no. 8, p. 309.ADSCrossRefGoogle Scholar
  10. 10.
    Rietveld, H.M., J. Appl. Crystallogr., 1969, vol. 2, p. 65.CrossRefGoogle Scholar
  11. 11.
    Sviridova, T.A., Chueva, T.R., Gorshenkov, M., et al., J. Alloys Compd., 2016, vol. 658, p. 525.CrossRefGoogle Scholar
  12. 12.
    Svipidova, T.A., Kpivko, O.A., D’yakonova, N.P., and Molokanov, V.V., Materialovedenie, 2008, no. 1, p. 45.Google Scholar
  13. 13.
    Stokłosa, Z., Rasek, J., Kwapulinski, P., et al., Phys. Status Solidi A, 2010, vol. 207, no. 2, p. 452.ADSCrossRefGoogle Scholar

Copyright information

© Allerton Press, Inc. 2019

Authors and Affiliations

  • N. P. Diakonova
    • 1
    Email author
  • E. A. Zakharova
    • 1
  • T. A. Sviridova
    • 1
  • T. R. Chueva
    • 2
  1. 1.National University of Science and Technology (MISiS)MoscowRussia
  2. 2.Baikov Institute of Metallurgy and Materials Science, Russian AcademyMoscowRussia

Personalised recommendations