Improving concrete resistance to low temperature sulfate attack through carbonation curing

Abstract

Carbonation curing of concrete can accelerate cement hydration and convert gaseous CO2 into embedded calcium carbonates. However, it’s commonly understood that concrete containing high amounts of calcium carbonates, as in the case of Portland limestone cement (PLC), is highly susceptible to low temperature sulfate attack. Therefore, this study investigated whether the same vulnerability applies to carbonation-cured concrete prepared from either ordinary Portland cement or PLC. It was found that calcium carbonates introduced through carbonation improved sulfate durability, unlike the compromising limestone additive in PLC. This was demonstrated by resilience against sulfate-induced spalling, expansion, and strength reduction. Gypsum, thaumasite and brucite were detected in severely damaged hydrated PLC specimens upon low temperature sulfate exposure. However, they were not found in the carbonated PLC specimens. Enhanced resistance to low temperature sulfate attack was attributed to reduction in permeability; consumption of calcium hydroxide; and decrease in the pH value of the pore solution.

This is a preview of subscription content, access via your institution.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13

References

  1. 1.

    Zhang D, Ghouleh Z, Shao Y (2017) Review on carbonation curing of cement-based materials. J CO2 Util 21 (Supplement C):119–131. https://doi.org/10.1016/j.jcou.2017.07.003

  2. 2.

    Rostami V, Shao Y, Boyd AJ (2011) Durability of concrete pipes subjected to combined steam and carbonation curing. Constr Build Mater 25(8):3345–3355. https://doi.org/10.1016/j.conbuildmat.2011.03.025

    Article  Google Scholar 

  3. 3.

    Zhang D, Shao Y (2018) Surface scaling of CO2-cured concrete exposed to freeze-thaw cycles. J CO2 Util 27:137–144. https://doi.org/10.1016/j.jcou.2018.07.012

  4. 4.

    Zhang S, Ghouleh Z, Shao Y (2020) Effect of carbonation curing on efflorescence formation in concrete paver blocks. J Mater Civ Eng 32(6):04020127. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003210

    Article  Google Scholar 

  5. 5.

    Zhang D, Shao Y (2019) Enhancing chloride corrosion resistance of precast reinforced concrete by carbonation curing. ACI Mater J 116(3):3–12

    Google Scholar 

  6. 6.

    Sotiriadis K, Mácová P, Mazur AS, Viani A, Tolstoy PM, Tsivilis S (2020) Long-term thaumasite sulfate attack on Portland-limestone cement concrete: a multi-technique analytical approach for assessing phase assemblage. Cem Concr Res 130:105995. https://doi.org/10.1016/j.cemconres.2020.105995

    Article  Google Scholar 

  7. 7.

    Shi C, Wang D, Behnood A (2012) Review of thaumasite sulfate attack on cement mortar and concrete. J Mater Civ Eng 24(12):1450–1460. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000530

    Article  Google Scholar 

  8. 8.

    Irassar E (2009) Sulfate attack on cementitious materials containing limestone filler—a review. Cem Concr Res 39:241–254. https://doi.org/10.1016/j.cemconres.2008.11.007

    Article  Google Scholar 

  9. 9.

    Rahman MM, Bassuoni MT (2014) Thaumasite sulfate attack on concrete: mechanisms, influential factors and mitigation. Constr Build Mater 73:652–662. https://doi.org/10.1016/j.conbuildmat.2014.09.034

    Article  Google Scholar 

  10. 10.

    Marchand J, Odler I, Skalny JP (2001) Sulfate attack on concrete. CRC Press, Boca Raton

    Google Scholar 

  11. 11.

    Kakali G, Tsivilis S, Skaropoulou A, Sharp JH, Swamy RN (2003) Parameters affecting thaumasite formation in limestone cement mortar. Cem Concr Compos 25(8):977–981. https://doi.org/10.1016/S0958-9465(03)00119-7

    Article  Google Scholar 

  12. 12.

    Tsivilis S, Sotiriadis K, Skaropoulou A (2007) Thaumasite form of sulfate attack (TSA) in limestone cement pastes. J Eur Ceram Soc 27(2):1711–1714. https://doi.org/10.1016/j.jeurceramsoc.2006.05.048

    Article  Google Scholar 

  13. 13.

    Skaropoulou A, Kakali G, Tsivilis S (2012) Thaumasite form of sulfate attack in limestone cement concrete: the effect of cement composition, sand type and exposure temperature. Constr Build Mater 36:527–533. https://doi.org/10.1016/j.conbuildmat.2012.06.048

    Article  Google Scholar 

  14. 14.

    CSA A3004-C8, Physical Test Methods for Cementitious Materials for Use in Concrete and Masonry (2013) Test method for determination of expansion of blended hydraulic cement mortar bars due to external sulphate attack, vol A3004. Canadian Standards Association

  15. 15.

    Monkman S, Shao Y (2006) Assessing the carbonation behavior of cementitious materials. J Mater Civ Eng 18(6):768–776

    Article  Google Scholar 

  16. 16.

    Hartshorn SA, Sharp JH, Swamy RN (1999) Thaumasite formation in Portland-limestone cement pastes. Cem Concr Res 29(8):1331–1340. https://doi.org/10.1016/S0008-8846(99)00100-3

    Article  Google Scholar 

  17. 17.

    Hossack AM, Thomas MDA (2015) The effect of temperature on the rate of sulfate attack of Portland cement blended mortars in Na2SO4 solution. Cem Concr Res 73:136–142. https://doi.org/10.1016/j.cemconres.2015.02.024

    Article  Google Scholar 

  18. 18.

    Heng M, Murata K (2004) Aging of concrete buildings and determining the pH value on the surface of concrete by using a Handy semi-conductive pH meter. Anal Sci 20(7):1087–1090. https://doi.org/10.2116/analsci.20.1087

    Article  Google Scholar 

  19. 19.

    Pigeon M, Pleau R (1995) Durability of concrete in cold climates. In: Modern concrete technology series, 1st edn. E. & F.N. Spon, London

  20. 20.

    MacDonald KA, and Lukkarila, M.R. Freezing and thawing resistance of dry compacted segmental retaining wall units. In: the Twenty-second international conference on cement microscopy, Montreal, Quebec, Canada, 2000. International Cement Microscopy Association, pp 225–239

  21. 21.

    Crammond NJ (2003) The thaumasite form of sulfate attack in the UK. Cem Concr Compos 25(8):809–818. https://doi.org/10.1016/S0958-9465(03)00106-9

    Article  Google Scholar 

  22. 22.

    Gaze ME, Crammond NJ (2000) The formation of thaumasite in a cement:lime:sand mortar exposed to cold magnesium and potassium sulfate solutions. Cem Concr Compos 22(3):209–222. https://doi.org/10.1016/S0958-9465(00)00002-0

    Article  Google Scholar 

  23. 23.

    Engbrecht DC, Hirschfeld DA (2016) Thermal analysis of calcium sulfate dihydrate sources used to manufacture gypsum wallboard. Thermochim Acta 639:173–185. https://doi.org/10.1016/j.tca.2016.07.021

    Article  Google Scholar 

  24. 24.

    Giampaolo C (1986) Dehydration kinetics of thaumasite at ambient pressure. Neues Jahrb Mineral Monatsh 3:126–134

    Google Scholar 

  25. 25.

    Scrivener K, Snellings R, Lothenbach B (2016) A practical guide to microstructural analysis of cementitious materials: a practical guide to microstructural analysis of cementitious materials. CRC Press, Boca Raton

    Google Scholar 

  26. 26.

    Nahdi K, Rouquerol F, Trabelsi Ayadi M (2009) Mg(OH)2 dehydroxylation: a kinetic study by controlled rate thermal analysis (CRTA). Solid State Sci 11(5):1028–1034. https://doi.org/10.1016/j.solidstatesciences.2009.02.013

    Article  Google Scholar 

  27. 27.

    Bonen D, Cohen MD (1992) Magnesium sulfate attack on portland cement paste-I: microstructural analysis. Cem Concr Res 22(1):169–180. https://doi.org/10.1016/0008-8846(92)90147-N

    Article  Google Scholar 

  28. 28.

    Goto S, Suenaga K, Kado T, Fukuhara M (1995) Calcium silicate carbonation products. J Am Ceram Soc 78(11):2867–2872

    Article  Google Scholar 

  29. 29.

    Bukowski JM, Berger RL (1979) Reactivity and strength development of CO2 activated non-hydraulic calcium silicates. Cem Concr Res 9(1):57–68. https://doi.org/10.1016/0008-8846(79)90095-4

    Article  Google Scholar 

  30. 30.

    Bellmann F, Stark J (2008) The role of calcium hydroxide in the formation of thaumasite. Cem Concr Res 38(10):1154–1161. https://doi.org/10.1016/j.cemconres.2008.04.005

    Article  Google Scholar 

  31. 31.

    Harrisson AM (2019) 4 - Constitution and specification of Portland cement. In: Hewlett PC, Liska M (eds) Lea's chemistry of cement and concrete, 5th edn, Butterworth-Heinemann, Oxford, pp 87–155. https://doi.org/10.1016/B978-0-08-100773-0.00004-6

  32. 32.

    Ghouleh Z, Guthrie RIL, Shao Y (2017) Production of carbonate aggregates using steel slag and carbon dioxide for carbon-negative concrete. J CO2 Util 18:125–138. https://doi.org/10.1016/j.jcou.2017.01.009

  33. 33.

    Rostami V, Shao Y, Boyd AJ, He Z (2012) Microstructure of cement paste subject to early carbonation curing. Cem Concr Res 42(1):186–193. https://doi.org/10.1016/j.cemconres.2011.09.010

    Article  Google Scholar 

Download references

Acknowledgements

The financial support by Natural Science and Engineering Research Council (NSERC) of Canada is greatly appreciated.

Funding

This study was funded by Natural Science and Engineering Research Council (NSERC) of Canada.

Author information

Affiliations

Authors

Corresponding author

Correspondence to Yixin Shao.

Ethics declarations

Conflict of interest

The authors declare that they have no conflict of interest.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Zhang, S., Ghouleh, Z., Azar, A. et al. Improving concrete resistance to low temperature sulfate attack through carbonation curing. Mater Struct 54, 37 (2021). https://doi.org/10.1617/s11527-021-01626-9

Download citation

Keywords

  • Thaumasite sulfate attack
  • Carbonation curing
  • Portland limestone cement
  • Concrete durability