Towards a more effective and reliable salt crystallization test for porous building materials: state of the art
- 1k Downloads
The durability of building materials with respect to salt crystallization is commonly determined by accelerated weathering tests, carried out in the laboratory. An effective laboratory weathering test should assess the durability and, in the case of conservation of historic buildings, the compatibility of repair materials with those existing. Besides, the test should provide reliable results within a reasonable period of time, accelerating the deterioration process without however altering its mechanism. Despite several national and international standards, recommendations and guidelines, a commonly accepted testing protocol does not yet exist. Researchers often develop and apply their own procedure, a fact that complicates comparison between different studies. The RILEM Technical Committee 271 ASC has been set up with the scope of developing improved test procedures for the assessment of the behaviour of materials under the influence of salt crystallization, which should overcome the limitations of existing standards and recommendations. This paper constitutes one of the first results of the work of the Technical Committee. It critically reviews the literature on salt crystallization tests, identifies advantages and limitations of the several test protocols and provides new ideas for the development of improved salt crystallization procedures.
KeywordsLiterature review Salt damage Salt crystallization test Porous materials RILEM
Salt crystallization is a major cause of damage in porous building materials (e.g. [1, 2, 3]). Despite extensive on-going research in this field, the complexity of the problem has hindered the use of theoretical models for forecasting decay due to salt crystallization. Indeed, in the practice of construction and conservation, the durability of materials with respect to salt crystallization, when not well-known from past field experience, is generally determined by accelerated weathering laboratory tests.
An effective laboratory weathering test should assess the durability of a material and, in the case of conservation of historic buildings, the compatibility of repair materials with pre-existing ones. Besides, the test should provide reliable results within a reasonable period of time, accelerating the deterioration process without altering its mechanism.
Moreover, none of the existing standards prescribes an accurate, reliable and quantitative method or technique for monitoring damage development during the test. Another limitation of current standards consists in the scarce validation of the results from the accelerated test through comparison with field data, e.g. in terms of damage type and severity .
The RILEM Technical Committee 271-ASC (Accelerated laboratory test for the assessment of the durability of materials with respect to salt crystallization), initiated in 2016, aims at overcoming the above-mentioned limitations by the development of improved test procedures for the assessment of the behaviour of building materials with respect to salt crystallization.
Providing an overview of existing standards and other test procedures;
Identifying advantages and limitations of different test procedures;
Providing input for the development of improved test procedures.
This review, as well as the to-be-developed test, focuses on the simulation of salt damage triggered by capillary transport of salt solution and evaporation at the surface, which is the situation most often observed in practice. Test procedures simulating sea-salt spray will not be considered, as standard tests in this field are quite well-accepted.
Specimen type, shape, size and number of replicates;
Salt type and amount;
Salt contamination procedure;
Methods for the assessment of damage and criteria for the evaluation of decay.
Based on the review, ideas are provided for the development of effective salt crystallization procedures.
2.1 Single material or combination
Most standards and guidelines prescribe the use of single material specimens (EN 12370, WTA 2005, RILEM 1980, RILEM MS-A.1 1998) [4, 5, 6, 7, 8]. Similarly, much of the experimental research reported in the literature has been carried out on single materials. However, although testing single materials may resemble practice in the case of objects like statues, in general, different materials are assembled in structures and the interaction between them can affect the durability of each material and of the whole structure.
For natural stone, the orientation of the bedding plane is another variable to consider. Smith and MacGreevy  and Cnudde et al.  showed how this orientation can affect decay type and development.
2.2 Number, size and shape
The number of replicate specimens specified in standard crystallization tests is generally larger than what is actually used by researchers. EN 12370  prescribes the use of at least 6 replicates, whilst RILEM MS-A.1  suggests 10. However, in the literature, the number of replicates is mostly limited to a maximum of three. In a few cases, more replicates are used, especially when damage is monitored with destructive techniques [23, 24, 25].
The size of the test specimens varies considerably: for single materials, EN 12370  prescribes the use of 40 mm side cubic specimens; RILEM MS-A.2 (for brick units)  suggests the use of prismatic specimens (entire brick units) with a maximum length of 120 mm between the absorption and the test (crystallization) faces. In general, except when small masonry units are used (ca. 200 × 200 × 100 mm3 [6, 14]), the specimen size is less than 1 dm3. The use of small specimens not only saves material, but it can considerably speed up the test, as it reduces the absorption and drying times [15, 26].
The size of the specimen is sometimes chosen based also on the selected assessment method. Cubic or prismatic specimens are most often used in laboratory tests. Sometimes, cylinders are used; this shape has the advantage of reducing corner effects and stress concentrations [27, 28]. Additionally, when using X-ray CT to monitor the weathering dynamically, cylinders allow the analysis of a larger volume at a specific resolution [23, 29].
The choice of the shape is also affected by other factors, such as the contamination procedure (e.g. elongated specimens are generally used in continuous partial immersion tests) and the assessment method. For example, Nunes et al.  used 40 × 40 × 160 mm3 mortar prisms to enable measurement of the flexural strength before and after the crystallization test.
In general, the concept of a representative elementary volume (i.e. the smallest volume over which a measurement can be made that will yield a value representative of the material properties and of the length scale over which salt crystallization damage may occur [31, 32]) might be used to define the minimum size of the specimen.
3.1 Single salts
In laboratory tests, mainly single salts are used; in buildings, however, salt mixtures are commonly found, rather than individual salts.
Like sodium sulphate, magnesium sulphate has multiple hydrated forms with different solubilities, and hence, it can be very aggressive. Several researchers [22, 38, 41, 42, 43], compared the aggressiveness of magnesium sulphate to other salts using different laboratory tests and all confirmed that magnesium sulphate can cause severe damage. Ruiz-Agudo et al. , underline that sodium and magnesium sulphates lead to different weathering patterns due to differences in solution properties and crystallization behaviour: in the case of Na2SO4 scale formation was observed in the tested calcarenites, whereas MgSO4 caused crack development throughout the bulk of the stone. These differences are confirmed by Balboni et al.  and Espinosa-Marzal and Scherer . Despite its aggressiveness, magnesium sulphate is used much less commonly than sodium sulphate in laboratory studies.
Another salt often used in laboratory tests is NaCl. This salt is generally reported to be much less damaging than Na2SO4. When comparing the aggressiveness of NaCl to that of other salts, Goudie et al.  found that NaCl could not produce any damage in immersion tests. Different results were obtained by Kwaad , who reported that NaCl produced some damage in granites, albeit less than that caused by Na2SO4, MgSO4 and Na2CO3. Rodriguez Navarro and Doehne  compared the effect of NaCl and Na2SO4 on the weathering of oolitic limestone, at two RH conditions, under continuous capillarity solution supply. Also in these experiments, NaCl was considered much less aggressive than Na2SO4, as damage was negligible at any RH. Gentilini et al.  studied masonry specimens contaminated with Na2SO4 and NaCl solutions at low concentrations. They found that in specimens contaminated with NaCl efflorescences were spread on the surface, not leading to any significant visible damage, whereas in samples affected by Na2SO4 efflorescences were concentrated in the mortar joints and edges of the specimens, causing exfoliation and flaking of the brick corners. Stefanidou and Papayanni  studied air-lime and pozzolanic mortars contaminated with sodium sulphate and sodium chloride solutions at different concentrations, using the weathering procedure of EN 12370 : they found that sodium sulphate produced severe damage in the form of cracks in the bulk of the mortar, whereas in the case of NaCl some sanding and scaling of the surface was observed.
The literature shows that there is a striking discrepancy between the limited damage observed in laboratory and the severe decay occurring in the field when materials are contaminated with NaCl (Fig. 1b). When considering damage due to salt crystallization in pores, the lower destructive potential of NaCl in laboratory tests has been attributed to its low tendency to supersaturate (e.g. [46, 49]) and high tendency to form efflorescence rather than subflorescence [17, 46]. Some authors focused on the development of a laboratory crystallization test specific for NaCl, able to reproduce more effectively the decay observed in the field. Lubelli  developed a test which first enhanced the accumulation of salt just beneath the surface of the material and then subjected the specimen to RH cycles between 0 and 96% RH. When using this procedure, damage was obtained in NaCl laden materials in a relatively short time . Diaz-Goncalves and Delgado-Rodrigues  compared the resistance of painted and unpainted plasters to NaCl and Na2SO4 crystallization. Dissolution and crystallization cycles were produced both by rewetting with water and drying at variable temperature and RH. In these test conditions, NaCl proved to be more aggressive than Na2SO4.
Nitrates (mostly NaNO3), carbonates (mostly Na2CO3), and other sulphates (mostly gypsum) have occasionally been used. Goudie  carried out salt crystallization experiments with different salts using continuous absorption followed by drying at temperatures between 22 and 55 °C. He reports Na2CO3 to be the most aggressive salt under the studied conditions, followed by MgSO4 and Na2SO4. In contrast, De Freece et al. , in an experiment consisting of crystallization/dissolution induced by RH changes, found Na2CO3 to be less aggressive than Na2SO4 and attributed its lower aggressiveness to its slower rate of response to RH variations. The aforementioned discrepancies are most probably due to the differences between the test procedures used.
3.2 Salt mixtures
The use of salt mixtures is less common in salt weathering tests. WTA recommendation  prescribes the use of a mixture of NaCl, Na2SO4 and NaNO3 for testing the salt resistance of renovation plasters.
Some researchers choose the composition of the brine for salt weathering tests based on the analysis of the salt present in naturally weathered building materials  to reproduce as well as possible a specific field condition. Other authors compare the aggressiveness of single salts to that of their mixtures.
The aggressiveness of sea salt mixtures has been compared to that of NaCl  and Na2SO4 . With only a few exceptions, the decay observed in specimens contaminated with sea salts was slightly more severe than in those laden with NaCl alone. Williams and Robinson  investigated the aggressiveness of salts common in efflorescence on rock outcrops in Central Europe: next to gypsum, potassium alum, ammonium alum, a combined potassium alum and alunogen were tested, both as single salts and as combinations. In these tests alunogen was “ineffective”, whereas the three alums were highly destructive; gypsum as a single salt caused minimal weathering, but the addition of gypsum significantly enhanced the damage caused by alums. The same authors  also tested NaCl and combinations of alums with NaCl and alunogen. They concluded that some combinations of salts can significantly enhance weathering, while other combinations are less damaging; however, no explanation is given for these differences. De Clercq [58, 59] investigated the effect of NaNO3, KNO3 and K2SO4 on the crystallization damage caused by sodium sulfate and concluded that the deteriorating effect of Na2SO4 was diminished due to the formation of double salts. The formation of different types of double salts and their different effects on pore clogging is reported also by Godts et al. , who investigated the behaviour of sodium and magnesium sulfate and mixtures of both at different environmental conditions.
Menendez and Petřánová  performed tests using three different salts (NaCl, Na2SO4 and CaSO4) and a mixture of them. They concluded that the mixture induced less damage than the single salts, and highlighted the complexity of the possible influencing factors, e.g. alteration of salt accumulation and drying rates, in the case of mixtures.
4 Salt contamination
4.1 Salt contamination procedure
Experiments using full immersion techniques prevail in the literature (often some variant of EN 12370 (e.g. ). Some authors (e.g. ) argue that, while this is not a common condition in practice, it reduces the dispersion of the results. Full immersion is not considered suitable to test specimens with surface treatments; in this case, contamination (and possibly rewetting) by partial immersion from the side opposite to the treated one (e.g. [65, 66]) is a better option.
In repeated total or partial immersion tests, salt can either be introduced only in the first cycle (further re-wetting is carried out with water), e.g. [16, 67, 68, 69], or at every re-wetting, e.g. [4, 18, 70, 71, 72, 73, 74].
The introduction of a fixed amount of salt can be advantageous to study the response of a material to a specific salt amount in relation to its pore volume ; this can prove useful, e.g. to establish salt contents below which a surface treatment can be safely applied [58, 76, 77, 78, 79]. By adjusting the concentration of the solution to the porosity of the material, and defining the amount of solution as that sufficient for the wetting front to reach the evaporation surface during imbibition by capillarity, the amount of salt in the specimen can be easily controlled. This procedure can favour the development of deterioration at the surface (more representative of the situation in practice). However, introducing a given amount of salt can be virtually impossible in some cases, e.g. restoration plasters with water repellent additives. In the European project COMPASS (EU project Compatibility of plasters and renders with salt loaded substrates in historic buildings, EVK4-CT-2001-00047) several procedures were developed to overcome the aforementioned disadvantages. To assess the performance of plasters applied on a substrate, a fixed amount of solution, sufficient to just saturate the substrate, was introduced [15, 17, 80]. In this case the amount of salt and its distribution in the plaster layer will depend on the moisture transport properties of the substrate/plaster combination.
4.2 Properties of the salt solution
Another important variable in salt contamination procedures is the concentration of the salt solution. The use of highly concentrated or saturated solutions of Na2SO4 [4, 81, 82, 83], and NaCl [68, 84, 85] is common in salt crystallisation tests. The same solution concentration is often used for different salt types , regardless of their different solubility. As pointed out by Goudie , a procedure comprising the continuous or repeated immersion of specimens in saturated salt solutions may simulate the effect of inundation in saline pan environments, but this is a marginal occurrence in practice.
The concentration of the salt solution affects the location of salt accumulation and crystallization and thus damage type and severity. Given the same amount of salt in a specimen, damage is more likely to develop if salt accumulates in a thin layer of material rather than if it is homogeneously distributed in the specimen, because pores become more completely filled, which leads to the development of a higher crystallization pressure . One of the drawbacks of using very high salt concentrations is that the solution viscosity increases, favouring deeper crystallization of the salt in the material . As explained by Ruiz-Agudo et al. , the physical properties of the salt solution, i.e. density, surface tension and, in particular, viscosity, have a critical effect on the dynamics of solution flow and evaporation, and therefore, on where and in which pores crystallization occurs, thus determining the damage type and severity. Higher salt concentrations can also favour pore clogging, depending on the type of salt, specimen pore structure  and drying conditions . Pore clogging can subsequently reduce the drying rate and favour subflorescences (i.e. crystallization beneath the surface) . Besides, a high salt solution concentration slows down the evaporation rate because the difference in vapour pressure between the material and the environment is reduced .
Little attention has been paid to reporting the details about the solution preparation procedure, e.g. density, freshly prepared or aged solution . This aspect can be particularly relevant when using (nearly) saturated solutions. The re-utilization of salt solution may also be an issue, particularly in the case of materials that contain a significant amount of exchangeable ions resulting in change in the actual composition of the salt solution . EN 12370 prescribes the use of a fresh solution for each cycle but some researchers opt to change the solution only every 5 cycles . For salts with solubility highly dependent on temperature, such as sodium sulphate, it is also important to control the temperature of both the solution and the specimen .
4.3 Dissolution/crystallization cycles
Deliquescence/dissolution/crystallization events are required for damage to develop. Only in a few cases, and especially when using sodium sulphate, damage has been observed after one single crystallization cycle [95, 96, 97]; most often, repeated cycles are needed for damage to occur. The results from extensive NaCl crystallization tests suggest that wetting and drying of the salt loaded specimens can be more relevant for the development of damage than the total amount of salt in the specimens . Similarly, Balboni et al. , who studied the damage mechanisms of magnesium sulphate salts in limestone, showed that specimens can also undergo significant deformations at low salt contents, provided they are subjected to several drying-rewetting cycles. These observations are possibly related to salt accumulation in a thin layer of the material, as a result of the repeated wet-dry cycles.
After the first salt contamination phase, dissolution/re-crystallization cycles can be achieved by re-wetting the specimens with a salt solution or with pure water (liquid or vapour). Re-wetting can take place either from the same surface as in the initial contamination with salt solution (most usual), or from the evaporation surface, opposite to the contamination surface, e.g. [60, 62, 99, 100]. A risk related to re-wetting from the top might be the transport of the salt back into the core of the specimen [99, 101].
Re-wetting with salt solution is often proposed to speed up the development of damage ; this can be effective and realistic, provided that the concentration of the solution is not too high. Conversely, repeated immersion in highly concentrated solutions is expected to: (1) favour pore clogging (e.g. ), (2) slow down the drying thus limiting the number of cycles which can be carried out in a given period of time, and (3) hinder salt transport and accumulation close to the evaporation surface, possibly leading to cracking and/or bursting in the bulk of the specimen, a type of damage that is not representative of the field situation.
Producing salt dissolution/crystallization cycles in specimens by rewetting with water, in liquid [6, 7] or vapour form, can be very effective, while still keeping the salt content within realistic values. Several studies have been carried out in an effort to keep the salt amount at a realistic level and increase the number of dissolution/re-crystallisation cycles by re-wetting with water [50, 88, 98, 102, 103]. Indeed, for salts with multiple anhydrous and hydrated forms with differing solubility (e.g. Na2SO4), wet-dry cycles with liquid water can be very damaging [97, 103]. Damage in this case is believed to be caused by the dissolution of the anhydrous phase (thenardite) followed by the rapid re-crystallization of the hydrated phase (mirabilite) [35, 104]. Recently, the possible role of heptahydrate in the damage induced by sodium sulphate has been investigated .
Even if damage in specimens contaminated with sodium sulfate can occur through RH cycles alone , re-wetting of thenardite with water vapour has been reported to be less damaging than re-wetting with liquid water [37, 97]. In contrast, in the case of sodium chloride, wet-dry cycles obtained by varying the RH of the air around the equilibrium RH of the salt can produce several crystallization-dissolution cycles in a short period of time and lead to damage, provided that the salts have accumulated near the surface of the specimen and are, hence, responsive to RH changes . This behaviour can be attributed to the fast hygroscopic uptake of the salt at high RH and to the growth of pure high-quality large crystals from a highly supersaturated solution . In the case of Na2SO4, damage is less likely to occur in deliquescence-crystallization cycles due to the lower hygroscopicity of this salt and because the growth of isolated hydrated crystals is slow and their life time is short .
Continuous partial immersion tests, i.e. simultaneous absorption and drying (wick-effect), are used to simulate the condition in which materials are permanently exposed to rising damp. In this case, no dissolution/re-crystallization cycles of the salt are simulated and damage is caused by the accumulation and crystallization of salts at the drying front. The results of this procedure seem to be highly dependent on the type of salt used and on the environmental conditions. Benavente et al.  compared the standard test EN 12370  (wet-dry cycles by total immersion) with the continuous partial immersion of stone in a Na2SO4 solution with cycles of temperature and RH (implying thenardite-mirabilite conversion). They observed significant differences in the extent and type of damage between the two test procedures. The continuous partial immersion test gave a distribution and type of damage more similar to that observed in the field than cycles of total immersion. The authors concluded that continuous partial immersion tests were probably a better way to simulate damage resulting from rising damp. Besides, they underlined that this procedure can be easily automated. However, other authors consider that continuous partial immersion might lead to unrealistic conditions: the existence of a permanently saturated surface on which salts crystallize in forms rarely or never seen in buildings, namely large near-equilibrium crystal shapes forming transparent crusts or cauliflower-like agglomerates . This might help explain why the continuous partial immersion test is generally ineffective for those salts, such as NaCl, which tend to effloresce. Moreover, depending on the concentration of the salt solution, an unrealistically high salt content might be reached in the specimen. Using NaCl, Wijffels and Lubelli  observed that wet-dry cycles with a fixed amount of NaCl (1.5 wt%) introduced by partial immersion in specimens composed of a brick substrate and a salt resistant plaster promoted higher salt accumulation close to the plaster surface (thus increasing the risk of salt damage) than continuous immersion in a NaCl solution (10 wt%). The authors concluded that a procedure allowing as many as possible repeated wet-dry cycles should, therefore, be preferred for this type of salt and substrates.
5 Drying conditions
The drying and cooling conditions used in salt crystallization tests have a major influence on the nature, location and rate of salt crystallization, and thus the type of damage induced. Goncalves and Brito  provide a summary of the key theoretical stages of drying involved in porous building materials. Stage 1 occurs when moisture contents are high and the evaporation front is at the surface (causing a constant drying rate and efflorescence). Stage 2 occurs when moisture contents are lower, and the evaporation front is located within the porous material (declining drying rate and subflorescence result during this stage). However, in practice a transitional phase can also occur, and the presence of salts can complicate any simple drying curves. Pel et al.  studied the drying of fired-clay brick specimens contaminated with NaCl solution in an NMR set-up. They reported that the salt laden specimens showed no receding drying front throughout the duration of the drying experiment (14 days) which was attributed to both the low drying rate conditions used and the wetting properties of the NaCl solution. Goncalves et al.  pointed out that when soluble salts are present, the drying kinetics is not only slower but also more irregular, and drying curves show higher dispersion than for pure water. The authors believe this occurs because salts amplify the dispersion effect that material heterogeneity has on the drying kinetics.
Factors affecting drying rates are temperature, air movement and relative humidity within the experimental set-up. As the complete drying of specimens may require a very long time, particularly when they are salt-contaminated, drying is often accelerated by the use of high temperatures, low RH and high air speed. The way that high temperatures are obtained can also influence the results. Gomez Heras and Fort  investigated whether heating by radiation and convection caused different effects. They found that radiation favoured subflorescence more than convective heating despite identical temperature cycling regimes. When drying occurs in an oven, low reproducibility between different laboratories has been reported  which suggests that, as well as temperature, other conditions (e.g. RH and air flow) should also be specified to improve the reproducibility of the test.
Crystallization experiments using full immersion techniques are very common in the literature (e.g. [4, 12, 110]). In these experiments, a short period of immersion in saline solution (often 2 h) is followed by an extended period of drying (usually 16–20 h), which in turn is usually followed by a short period of cooling (2–8 h). In most cases, the three stages together add up to 24 h, and this diurnal cycle is repeated several times. Drying temperatures between 60 and 105 °C are generally used, with cooling under room conditions, despite it being known that temperatures higher than 50–60 °C can cause microfissures in some stone types (see e.g. ). West  suggests that the EN12370  procedure might be improved by lowering the drying temperature to 65 °C, as done in the Australian standard AS/NZS 4456:2003 (“Masonry units, segmental pavers and flags—Methods of test”) .
Angeli et al.  studied the effect of different drying and cooling conditions (5 °C, room temperature, and 50 °C) on the severity and type of decay of sedimentary stone types contaminated with different concentrations of sodium sulphate solution. They report that higher damage developed at low cooling temperatures and attributed this result to the lower solubility of sodium sulphate at low temperatures, which allows fast supersaturation and thus very fast decay.
Some papers report on complex experiments, such as those carried out by Yu and Oguchi and Menendez and David who used different temperature and RH conditions, in order to investigate the aggressiveness of different forms of Na2SO4  and CaSO4  on the weathering. In both studies, the key role played by drying and cooling conditions on salt damage was confirmed.
Full immersion experiments can also involve more complex drying regimes when they aim to predict the behaviour of different materials under specific field conditions. Geomorphological researchers in particular utilise this approach. Smith et al.  provide an example of an experimental study designed to evaluate the importance of stress histories to the behaviour of rocks on desert surfaces. After immersion in NaCl for 48 h groups of pristine and pre-stressed limestone and sandstone blocks were air dried for 96 h at 20 °C, and then exposed in an environmental cabinet to cycles of convective temperature with bursts of radiative heating to simulate warming by solar radiation; significant damage was registered. Other experiments interrupt the drying stage to spray deionized water onto the samples to simulate fog (e.g. ), or use extreme temperature and humidity cycling to simulate diurnal cycles of solar heating and dew deposition, e.g. . Arizzi et al.  used purpose-designed drying conditions, with temperature and RH cycles and fog events (spraying water on the evaporation surface), to study the performance of different mortar mixes.
In partial immersion experiments, samples are contaminated with salts initially through the base of the sample, then dried and re-wetted with deionized water or salt solution, either from the top of the specimen, i.e. evaporation surface, (simulating rain or fog) or from its bottom (simulating rising damp) (see Sect. 4.3). Godts et al.  contaminated limestone with MgSO4, Na2SO4, and a mixture of the two, then dried them at either 25 °C and 35% RH or 25 °C and 70% RH for 14 days, then applied more water to the top and dried them for a further 14 days. The authors report that the use of low RH favours pore clogging and the formation of a salt crust which consequently delays drying.
Lubelli et al.  used partial immersion methods to contaminate plasters with NaCl and then dried them under four different scenarios of temperature and RH. The specimens were re-wetted through the side opposite to the evaporation surface when 80% of the initially applied water had evaporated. The results showed that temperature and air flow have a very important effect on the drying rate and that repeated wet-dry cycles favour migration of the salts towards the evaporation surface. The same author  proposes the use of temperature and RH cycles (between 60 °C/0%RH and 20 °C/95%) during drying to speed up the drying process and, at the same time, increase the number of dissolution/crystallization cycles. In this way, damage can be significantly accelerated in NaCl contaminated specimens.
In studies involving the evaluation of mortar performance in composite samples, a possible role of the wetting cycles in the curing of the mortars was highlighted (e.g. [47, 54]), which makes the interpretation of the salt effect more complex.
In experiments involving the continuous partial immersion of specimens in salt solution, different ranges of drying conditions are used. For example, Benavente et al.  used partial immersion of limestone and sandstone specimens in Na2SO4 and a two stage drying: 12 h at 40 °C and 80% RH, followed by 12 h at 10 °C and 70% RH. Goudie  used cycles of 7 h at 55 °C and 17 h at 22 °C (with no control of RH) in his study of the ‘wick effect’ of a range of salt solutions on sandstone.
The selection of the drying conditions is sometimes determined by the goals of the experiment. Cardell et al.  used temperature and humidity regimes to reproduce natural conditions in Granada, southern Spain, while Rodriguez-Navarro and Doehne  used low (35%) and medium–high (60%) RH conditions at 20 °C to compare the effects of mirabilite and thenardite, crystallizing at RH > 50% and at RH < 50%, respectively.
Another relevant parameter is the use of free or constrained drying conditions. Under free conditions, evaporation can occur from all the faces of the specimen, whilst under constrained conditions 4 or 5 faces are sealed to prevent evaporation. Sealing can be obtained either by applying a tape, film or adhesive, or by applying an impermeable coating (usually an epoxy resin) or placing blocks within polystyrene ‘moulds’ or other devices, which may also exert a mechanical constraint or thermal insulation on blocks.
6 Assessment method
Many, more or less complex, methods and techniques are used for the assessment of the results of salt crystallization tests. The occurrence of damage is mostly assessed by comparison between the situation before and after the test. The methods used depend on the aims of the study and, sometimes, also on the available laboratory equipment.
6.1 Visual and photographic observations and weight change
Standards and recommendations suggest simple assessment methods, which can be carried out at any laboratory, without the need for specific facilities. RILEM Tests No. V.1a, b (total immersion)  and EN 12370  prescribe reporting the mass change or the number of cycles needed to completely destroy the samples (in case complete disintegration occurs in less than 15 cycles). A photographic record of the specimen condition is required only at the beginning and at the end of the test. RILEM Test No. V.2 (partial immersion)  requires a “visual (photographic) evaluation” only, and recording the mass change is stated to be “less suitable” in this case. Similarly, RILEM MS-A.1  suggests recording the visual changes (by photographs and description) and the number of units that have failed after each cycle. The criterion of “failure” must be specified in every individual case. Thus, a comparison between different materials and units is difficult and might be biased by subjective considerations.
All in all, as “visual (photographic) evaluation” is highly affected by subjectivity, mass change is the only measurable and quantitative property proposed in the standard tests. However, recording the mass change has important limitations: mass change is a combination of mass increase due to repeated salt contamination and mass loss due to damage. Besides, when damage occurs as cracking of the specimen without any material loss, it becomes impossible to use mass change as the only criterion.
In most scientific studies of salt decay, the development of damage is usually monitored by weighing the specimen after each drying cycle in combination with visual and photographic record. Several authors further developed the mass change criterion to extract relevant and objective information on the weathering and its evolution. Some authors collected the debris after dissolution of the salt to monitor more precisely the loss of material (e.g. [39, 50]). As salt can cement loose particles, some authors suggested brushing the specimen after the wetting phase to facilitate removal of debris  or immersing it in water at the end of the test . Goudie et al.  classified the material loss according to the size of the fragments in order to gain quantitative information on the type of damage (e.g. splitting or granular disintegration). The same author some years later  used four different parameters to express the nature of stone breakdown: (a) weight of the largest remaining particle, expressed as a percentage of the initial weight; (b) combined weight of detached particles above 2 g as a percentage of the initial weight; (c) number of detached particles above 2 g and (d) weight percentage of particles less than 1 mm in diameter. On particles weighing less than 2 g, a granulometry study was performed. A combination of these parameters was used by the same author to define an Index of Disintegration. Later on, other authors also tried to define indices to facilitate the comparison between specimens: e.g. Angeli et al.  established the Alteration Index, i.e. the number of the cycle during which one can see the first sign of damage, and the Alteration Velocity, i.e. the slope of the plot representing the weight loss in percentage as a function of the cycle number, allowing assessment of the dynamics of the weathering process.
In some studies, photographic recording has been replaced by time-lapse videos, which allows a better representation of the evolution of damage over time . In some others, a more standardized description of the damage has been attempted in order to make visual assessment more objective (e.g. [25, 69]).
6.2 Other methods
6.2.1 Non-destructive techniques
In most studies, visual/photographic inspection and mass change measurement are complemented with more or less complex investigation techniques. Some of these are non-destructive and allow monitoring of damage during the test, while some others are destructive and are, therefore, generally carried out only at the end of the test.
6.2.2 Destructive techniques
Among the destructive techniques for the study of the effect of salt crystallization on a material, mercury intrusion porosimetry (MIP) is one of the most commonly used. The measurement of changes in porosity and pore size distribution by MIP is considered to provide information on the location of salt deposition (if carried out after the test and prior to desalination) and on the damage (if carried out after the test on desalinated samples) (e.g. [42, 46, 47, 62, 98, 110, 129, 130]. The limitations of MIP are well known (e.g. ): the instrument measures the pore throat and not the actual pore size, thus possibly leading to misinterpretation of data; assumptions are made on contact angle values and pore shape which may strongly affect the results. Despite these limitations, the ease of data collection and elaboration has contributed to the diffusion of the use of this method.
In some studies, the difference in mechanical (flexural, tensile and/or compressive) strength of the material before and after the crystallization test is used as a measure of decay , sometimes in combination with NDT methods. For example, Akin and Ozsan  determined the UCS of travertine stones with different porosity after an increasing number of crystallization cycles and showed that repeated magnesium and sodium sulphate crystallization significantly reduce the compressive strength. Similarly, Ludovico-Marques  determined the evolution of mechanical properties of sandstone blocks during a crystallization test. Aly et al.  characterized the UCS of partially immersed stone samples after different times of treatment.
One of the limitations of mechanical strength measurements is that the combined effect of salt accumulation in pores (increasing the material strength ), moisture, and damage (decreasing the material strength), complicate the interpretation of the results.
Microscopy techniques, including optical [134, 135] and (environmental) electron scanning microscopy, sometimes equipped with energy dispersive X-ray spectrometry (e.g. [46, 55, 101, 135, 136]), are also often used to study damage due to salt crystallization. Generally, microscopic observations are carried out at the end of the test, without prior desalination of the sample, to assess the presence and type of damage and relate this to the salt distribution in the specimen (e.g.  and the location of salt in pores [50, 133]).
Sometimes, destructive methods are used to assess quantitatively the distribution of salt in the specimens during and/or at the end of the test. The technique usually encompasses the slicing or grinding of the specimen along its length or powder-drilling of the samples at different depths. The salt content in the samples can then be measured by the hygroscopic moisture content method [137, 138], or by ion chromatography (IC) [17, 50, 51, 98] or electrical conductivity . Modestou et al.  used the drilling resistance measurement system (DRMS) and the scratch tool to monitor the salt crystallization front in salt weathered limestone, both in the laboratory and in situ. Arizzi et al.  analyzed by IC the amount of soluble cations present in mortar specimens at the end of a crystallization test with sodium sulfate.
The precision of the salt distribution analysis is determined by the thickness of each sampling interval. Given the importance of salt distribution in the development of damage, its assessment is of crucial importance for designing a salt crystallization test, namely regarding the contamination procedure and the drying regime. Besides, salt distribution can be used to determine the risk of future damage in those specimens showing no decay at the end of the test: a high accumulation of salt directly beneath the surface implies a higher risk than a homogenous distribution of salt throughout the depth of the specimen. A similar approach was followed by other researchers for assessing the risk of damage due to accumulation of salts behind the consolidated layers in bricks  and limestone , such accumulation possibly leading to spalling of the treated layer.
7 Discussion and conclusions
This review highlights that a wide range of accelerated salt weathering procedures has been proposed in the literature, due to both the limitations of current standard methods and the different goals of the studies.
Focussing on the assessment of material durability and repair material compatibility, the first key step in the establishment of an accelerated test is the choice of the type of specimen, which should be representative of the situation in practice. The review highlights for many situations the importance of testing combinations of different materials (assembled specimens), and of taking into account material peculiarities, such as bedding planes in natural stones. Small size specimens should be preferred to speed up the wetting and drying steps. However, the size of the specimen should be large enough to be representative of the material properties and of the simulated damage process. The shape of the specimen often depends on the damage assessment method. Generally, cylinders have the advantage of limiting the corner effects present in prismatic specimens. Although standards and recommendations suggest a high number of replicates (6 in , 10 in ), 3 (or even fewer) replicates are generally used in laboratory tests; requiring a much larger number of replicates seems therefore impractical. A compromise should nevertheless be found between practical issues and reliability of the results.
The assessment of the reviewed references shows that single salts (mainly Na2SO4 and NaCl) are most commonly used in crystallization tests. Salt mixtures are rarely adopted, probably because of the complexity in the interpretation of the results and because mixtures were often found to be less damaging than single salts. Salts with multiple hydrates with different solubility (such as sodium and magnesium sulphate) are the most damaging ones in accelerated weathering tests. However, this conclusion might be partially biased by the test procedures generally used in literature (immersion-drying cycles promoting the rapid re-crystallization of the hydrated forms after dissolution of the anhydrous one), as the kind of cycle is decisive for the measured aggressiveness of a salt. In fact, salts like sodium chloride have also proven to be very damaging, provided that effective weathering conditions are selected (frequent dissolution/crystallization cycles of the salt due to RH changes). These observations suggest that the most effective procedure depends on the type of salt used.
Often, a very high salt content in the specimens is used in salt crystallization tests, but this literature review suggests that this might be counter-productive in some cases, leading to unrealistic damage type without necessarily speeding up the occurrence of damage.
The large variety of contamination and drying procedures reported in the literature, and the fact that they are rarely compared with each other, makes it difficult to draw conclusions on their relative effectiveness and reliability. However, it is clear that contamination and drying procedures can affect the durability ranking of the tested materials. In fact, the contamination procedure (amount, concentration and supply of salt solution) and the drying conditions affect the salt accumulation in the material. The degree of pore filling and the crystallization pressure, together with the (micro)mechanical properties of the material, determine the onset of the damage .Extreme drying conditions are very often used in laboratory weathering tests, because of the need to accelerate the damage process; however these conditions often lead to damage types (e.g. cracks in the bulk of the sample, complete disintegration) that are far from representative of reality. As the decay type depends on the location of salt crystallization, it is important in a crystallization test that salt accumulation occurs where this is to be expected in the field, i.e. near the surface of the material, for a test to be reliable and significant. This can be favoured by the use of unsaturated solutions, initial saturation of the specimen by capillarity and not too extreme drying regimes.
This review shows that several techniques can be used to assess and monitor the decay, qualitatively and quantitatively, destructively and non-destructively, with different levels of complexity, precision and cost. Generally, visual observation and mass change are used for monitoring the decay, sometimes complemented by additional techniques. In the definition of a standard crystallization test and prescription of assessment methods, preference should be given to economically affordable and preferably non-destructive monitoring methods and techniques, which are easily accessible for most laboratories and do not require very specialized expertise.
Existing standards and recommendations provide no criteria for the classification of the durability of the tested material. In publications, conclusions are drawn only by comparison between the different tested materials (relative ranking). Providing criteria for such a classification would confer an additional value to the to-be-developed salt crystallization procedure.
In conclusion, this paper provides an overview of existing literature on accelerated salt crystallization tests, underlines open questions and suggests directions for the to-be developed salt crystallization procedure. These ideas, together with those resulting from research on modelling of salt transport and crystallization pressure , will contribute to the definition of improved procedures for the assessment of the durability of materials with respect to salt crystallization.
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
- 1.Goudie AS, Viles HA (1997) Salt weathering hazards. Wiley, ChichesterGoogle Scholar
- 4.CEN (1999) EN 12370 Natural stone test methods. Determination of resistance to salt crystallizationGoogle Scholar
- 5.RILEM (1980) Recommended tests to measure the deterioration of stone and to assess the effectiveness of treatment methods, Test V.1a—crystallization test by total immersion (for untreated stone); Test V.1b—crystallization test by total immersion (for treated stone); Test V.2—crystallization test by partial immersion. Mater Struct 13(75):175–253Google Scholar
- 8.WTA Merkblatt 2-9-04/D (2005) Sanierputzsysteme/Renovation mortar systems. WTA Publications, StuttgartGoogle Scholar
- 9.West D (2000) Brard’s test into the 21st century: sodium sulphate soundness testing of dimension stone. In: McNally GH, Franklin BJ (eds) Sandstone city: Sydney’s dimension stone and other sandstone geomaterials. Proceedings of a symposium held on 7th July 2000, during the 15th Australian geological convention at the University of Technology, Sydney. Geological Society of Australia, Environmental, Engineering and Hydrology Specialist Group, Monograph 5, pp 138–148Google Scholar
- 10.Doehne E, Selwitz C, Carson D (2002) The damage mechanism of sodium sulphate in porous stone. In: Proceedings of the SALTeXPERT meeting, pp 27–146Google Scholar
- 11.Lubelli B, Van Hees RPJ, Nijland TG (2014) Salt crystallization damage: how realistic are existing ageing tests? In: De Clercq H (ed) Proceedings of the international conference on salt weathering of buildings and stone sculptures (SWBSS 2014), Aedificatio Publishers, Brussels, pp 259–273Google Scholar
- 13.Van Hees RPJ, Brocken HJP (2001) Interaction of the SBW treatment with Na2SO4, NaCl and NaNO3. In: De Witte E (ed) Salt compatibility of surface treatment (SCOST), final report, EU Contract No. ENV4-CT98-0710, pp 109–119Google Scholar
- 15.Wijffels T, Lubelli B (2006) Development of a new accelerated salt crystallization test. Heron 51(1):63–79Google Scholar
- 16.Velosa AL, Veiga MR (2006) Development of artificial ageing tests for renders: application to conservation mortars. In: Thompson G (ed) Proceedings of the 7th international masonry conference, British Masonry Society, LondonGoogle Scholar
- 17.Gonçalves TD (2007) Salt crystallisation in plastered or rendered walls. Ph.D. dissertation, Instituto Superior Técnico da Universidade Técnica de LisboaGoogle Scholar
- 20.Groot CJWP (1993) Effect of water on mortar-brick bond. Ph.D. dissertation, Delft University of TechnologyGoogle Scholar
- 21.Wijffels TJ, Van Hees RPJ (2000) The influence of the loss of water of the fresh mortar to the substrate on the hygric characteristics of so-called restoration plaster. In: Verhoef L, Wittman F (eds) Proceedings of the international workshop on urban heritage and building maintenance VII, Aedificatio Publishers, Freiburg, pp 49–54Google Scholar
- 25.Kyriakou L, Theodoridou M, Ioannou I (2017) Assessment of the durability of lime renders with Phase Change Material (PCM) additives against salt crystallization. In: Laue S (ed) Proceedings of the fourth international conference on salt weathering of buildings and stone sculptures (SWBSS 2017), University of Applied Sciences, Potsdam, pp 81–89Google Scholar
- 26.Diaz Gonçalves T, Brito V, Musacchi J, Pel L, Saidov T, Delgado Rodrigues J, Costa D, Mimoso JM (2014) Drying of porous building materials possibly contaminated with soluble salts: summary and findings of the DRYMASS research project. In: De Clercq H (ed) Proceedings of the international conference on salt weathering of buildings and stone sculptures (SWBSS 2014), Aedificatio Publishers, Brussels, pp 1–15Google Scholar
- 31.Bachmat Y, Bear J (1987) On the concept and size of a representative elementary volume (rev). In: Bear J, Corapcioglu MY (eds) Advances in transport phenomena in porous media. NATO ASI series (Series E: applied sciences), vol 128. Springer, DordrechtGoogle Scholar
- 33.ASTM Subcommittee D18.17 (2013) ASTM 5240 standard test method for evaluation of durability of rock for erosion control using sodium sulfate or magnesium sulfateGoogle Scholar
- 38.Goudie A, Cooke R, Evans I (1970) Experimental investigation of rock weathering by salts. Area 2(4):42–48Google Scholar
- 39.Kwaad FJPM (1970) Experiments on the granular disintegration of granite by salt action. Fysisch Geografisch Bodemkundig Laboratorium From Field to Laboratory 16:67–80Google Scholar
- 48.Stefanidou M, Papayanni I (1999) Resistance of repair mortars of historic structures to wetting-drying salt cycles. In: Arun G (ed) Proceedings of the international symposium studies on historical heritage (SHH07), Yıldız Technical University, Istanbul, pp 347–354Google Scholar
- 50.Lubelli B (2006) Sodium chloride damage to porous building materials. Ph.D. dissertation, Delft University of TechnologyGoogle Scholar
- 58.De Clercq H (2008)The effect of other salts on the crystallization damage to stone caused by sodium sulfate. In: Proceedings of the SWBSS2008 conference, Copenhangen, 2008, pp 307–315Google Scholar
- 60.Godts S, Hendrickx R, De Clercq H (2014) The crystallization behavior of sodium magnesium sulfate in limestone. In: De Clercq H (ed) Proceedings of the third international conference on salt weathering of buildings and stone sculptures (SWBSS 2014), Aedificatio Publishers, Brussels, pp 167–182Google Scholar
- 68.Henriques FMA, Charola AE (2000) Development of lime mortars with improved resistance to sodium chloride crystallization. In: Fassina V (ed) Proceedings of the 9th international conference on deterioration and conservation of stone, vol 2. Elsevier, Venice, pp 335–342Google Scholar
- 74.Franzoni E, Gentilini C, Graziani G, Bandini S (2014) Towards the assessment of the shear behaviour of masonry in on-site conditions: a study on dry and salt/water conditioned brick masonry triplets. Constr Build Mater 65:405–416. https://doi.org/10.1016/j.conbuildmat.2014.05.002 CrossRefGoogle Scholar
- 75.Van Hees RPJ, Brocken H (2003) The salt crystallisation method. In: De Witte E (ed) Salt compatibility of surface treatment (SCOST), final report, EU Contract No. ENV4-CT98-0710, institution? city?, pp 35–37Google Scholar
- 76.Miquel A, Bromblet P, Vergès-Belmin V (2003) Compatibility of SBW treated substrates with Na2SO4. In: De Witte E (ed) Salt compatibility of surface treatment (SCOST), final report, EU Contract No. ENV4-CT98-0710, institution? city? pp 73–95Google Scholar
- 77.De Clerq H, De Witte E (2003) Interaction of the type of treatment with different types of salt. In: De Witte E (ed) Salt compatibility of surface treatment (SCOST), final report, EU Contract No. ENV4-CT98-0710, institution? city? pp 142–144Google Scholar
- 78.De Clercq H (2005) Performance of single materials treated with a water repellent and contaminated with a salt mix. In: Silfwerbrand J (ed) Proceedings of the 4th international conference on water repellent treatment of building materials (Hydrophobe IV), Aedificatio Publishers, Brussels, Aedificatio Publishers, Freiburg, pp 171–184Google Scholar
- 79.De Clercq H (2008) Performance of limestone contaminated with binary mixtures of sodium sulphate and treated with a water repellent. In: De Clercq H (ed) Proceedings of the 5th international conference on water repellent treatment of building materials (Hydrophobe V), Aedificatio Publishers, Brussels, pp 107–116Google Scholar
- 80.Vergès-Belmin V, Wijfels T, Gonçalves TD, Nasraoui M (2005) The COMPASS salt crystallization test as a way to figure out how salts migrate and accumulate in renovation plasters. In: Van Hees RPJ (ed) Compatibility of plasters and renders with salt loaded substrates in historic buildings, final report, EU Contract No. EVK4-CT-2001-0047-DGXII, institution? city? pp 157–168Google Scholar
- 83.Sassoni E, Franzoni E, Graziani G, Sagripanti F (2014) Limestone resistance to sodium sulfate degradation after consolidation by hydroxyapatite and TEOS. In: De Clercq H (ed) Proceedings of the international conference on salt weathering of buildings and stone sculptures (SWBSS 2014), Aedificatio Publishers, Brussels, pp 335–345Google Scholar
- 85.Aly N, Gomez-Heras M, Hamed A, Alvarez de Buergo M, Soliman F (2014) Porosity changes after different temperature regimes for a salt weathering simulation test on Mokkattam limestone (Egypt). In: De Clercq H (ed) Proceedings of the international conference on salt weathering of buildings and stone sculptures (SWBSS 2014), Aedificatio Publishers, Brussels, pp 247–257Google Scholar
- 90.Derluyn H, Boone MA, Boone MN, De Kock T, Desarnaud J, Peetermans S, Molari L, De Miranda S, Shahidzadeh N, Cnudde V (2015) Salt crystallization dynamics in building rocks: a 4D study using laboratory X-ray micro-CT. In: Long B (ed) Proceedings of the 2nd international conference on tomography of materials and structures (ICTMS 2015), Québec, pp 565–568Google Scholar
- 95.Delgado Rodrigues J, Ferreira Pinto A, Nunes C (2007) Preparation of aged samples for testing stone treatments. In: Proceedings of the 23th international convention Scienza e Beni Culturale—Il Consolidamento degli Apparati Architettonici e Decorativi, Arcadia Ricerche, Marghera Venezia, pp 597–605Google Scholar
- 97.Stahlbuhk A, Nissen J, Linnow K, Steiger M (2014) Influence of the salt concentration on the damage potential of mirabilite and thenardite. In: De Clercq H (ed) Proceedings of the international conference on salt weathering of buildings and stone sculptures (SWBSS 2014), Aedificatio Publishers, Brussels, pp 35–48Google Scholar
- 103.MacWilliam K (2017) Aging tests to assess the durability of building materials to salt crystallization—towards a more realistic and effective use of sodium sulfate. M.Sc. dissertation, Czech Technical University in PragueGoogle Scholar
- 107.Desarnaud J, Bertrand F, Shahidzadeh-Bonn N (2011) Dynamics of salt crystallization. In: Ioannou I, Theodoridou M (eds) Proceedings of the international conference on salt weathering of buildings and stone sculptures (SWBSS 2011), University of Cyprus, Limassol, pp 23–29Google Scholar
- 111.Siegesmund S, Ruedrich J, Weiss T (2004) Marble deterioration. In: Prikryl R (ed) Dimension stone. Taylor & Francis, London, pp 211–217. ISBN 90-5809-675-0Google Scholar
- 112.Australian standard AS/NZS 4456:2003 (2003) Masonry units, segmental pavers and flags—methods of testGoogle Scholar
- 117.Angeli M, Bigas J-P, Menéndez B, Hébert R, David C (2006) Influence of capillary properties and evaporation on salt weathering of sedimentary rocks. In: Fort R, Alvarez de Buergo M, Gomez-Heras M, Vazquez-Calvo C (eds) Proceedings of the international conference on heritage, weathering and conservation, Taylor & Francis, Leiden, pp 253–259Google Scholar
- 119.Binda L, Baronio G, Ferrieri ED (1997) Durability of brick masonry surface treatments to salt crystallization. In: Proceedings of the 11th international brick/block masonry conference, Tongji University, Shanghai, pp 732–741Google Scholar
- 120.Gomez-Heras M, Smith BJ, Viles HA, Meneely J, McCabe S (2008) High definition laser scanning for the evaluation of salt decay laboratory simulations of building limestone. In Proceedings of the salt weathering on buildings and stone sculptures (SWBSS 2008), Technical University of Denmark, Copenhagen, pp 149–158Google Scholar
- 122.Dewanckele J, De Kock T, Boone MA, Cnudde V, Brabant L, Boone MN, Fronteau G, Van Hoorebeke L, Jacobs P (2012) 4D imaging and quantification of pore structure modifications inside natural building stones by means of high resolution X-ray CT. Sci Total Environ 416:436–448. https://doi.org/10.1016/j.scitotenv.2011.11.018 CrossRefGoogle Scholar
- 123.Derluyn H, Griffa M, Mannes D, Jerjen I, Dewanckele J, Vontobel P, Sheppard A, Derome D, Cnudde V, Lehmann E, Carmeliet J (2013) Characterizing saline uptake and salt distributions in porous limestone with neutron radiography and X-ray micro-tomography. J Build Phys 36(4):353–374. https://doi.org/10.1177/1744259112473947 CrossRefGoogle Scholar
- 124.Derluyn H (2012) Salt transport and crystallization in porous limestone: neutron—X-ray imaging and poromechanical modeling, Dissertation ETH No. 20673, ETH Zurich, Switzerland. https://doi.org/10.3929/ethz-a-007578301
- 125.Derluyn H, Dewanckele J, Boone MN, Cnudde V, Derome D, Carmeliet J (2014) Crystallization of hydrated and anhydrous salts in porous limestone resolved by synchrotron X-ray microtomography. Nucl Instrum Methods Phys Res, Sect B 324:102–112. https://doi.org/10.1016/j.nimb.2013.08.065 CrossRefGoogle Scholar
- 128.Aly N, Hamed A, Gomez-Heras M, Benavente D, Alvarez de Buergo M (2016) The effect of salt crystallisation on the mechanical properties of limestone: statistical correlations between non-destructive and destructive techniques. In: Hughes J, Howind T (eds) Science and art: a future for stone—proceedings of the 13th international congress on the deterioration and conservation of stone, vol 1, University of the West of Scotland, Paisley, pp 225–231Google Scholar
- 133.Stefanidou MA (2009) A contribution to salt crystallization into the structure of traditional repair mortars through capillarity. In: Fernandes I (ed) Proceeding of the 11th euroseminar on microscopy applied to building materials (EMABM), Elsevier, Amsterdam, pp 106–112Google Scholar
Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.