Structure and photocatalytic properties of Bi25FeO40 crystallites derived from the PEG assisted sol-gel methods

Abstract

Sillenite Bi25FeO40 crystallites have been fabricated via a sol-gel approach. X-ray diffraction results show that single-phase Bi25FeO40 can be synthesized at the annealing temperature of 600 oC with the help of PEG additive. The amount of additives and the annealing temperature has great effects on the formation of phase pure Bi25FeO40 crystallites. The morphologies of Bi25FeO40 crystallites were observed by SEM techniques. UV-vis diffuse reflectance spectroscopy indicated the good visible light absorption of Bi25FeO40 crystallites. The photo-catalytic activity of Bi25FeO40 powders was evaluated by the degradation of methyl orange solution assisted by H2O2 under UV-Vis light and Vis-only light irradiation, which suggested that Bi25FeO40 crystallites are potential photocatalytic materials.

This is a preview of subscription content, access via your institution.

References

  1. 1.

    A. Fujishima and K. Honda, Nature 238, 37–38 (1972).

  2. 2.

    S.C. Abraiiams, P.B. Jamieson and J.L. Bernstein, Journal of Chemical Physics 47, 4034–4041 (1967).

  3. 3.

    C.H. He and M.Y. Gu, Scripta Materialia 55 (5), 481–484 (2006).

    CAS  Article  Google Scholar 

  4. 4.

    C.H. He and M.Y. Gu, Scripta Materialia 54 (7), 1221–1225 (2006).

    CAS  Article  Google Scholar 

  5. 5.

    H.P. Zhang, M.K. Lü, S.W. Liu, Z.L. Xiu, G.J. Zhou, Y. Y. Zhou, Z.F. Qiu, A.Y. Zhang and Q. Ma, Surface and Coatings Technology 202 (20), 4930–4934 (2008).

    CAS  Article  Google Scholar 

  6. 6.

    X.P. Lin, F.Q. Huang, W.D. Wang and J.L. Shi, Scripta Materialia 56 (3), 189–192 (2007).

    CAS  Article  Google Scholar 

  7. 7.

    D.C. Craig and N.C. Stephenson, Journal of Solid State Chemistry 15 (1), 1–8 (1975).

    CAS  Article  Google Scholar 

  8. 8.

    S.F. Radaev, L.A. Muradyan and V.I. Simonov, Acta Crystallographica Section B 47, 1–6 (1991).

  9. 9.

    J.M. Li, J.Y. Song, J.G. Chen, S.W. Yu, D.G. Jin and J.R. Cheng, presented at the 2009 MRS Fall Meeting, San Francisco, 2009 (unpublished).

  10. 10.

    C.Y. Zhang, H.J. Sun, W. Chen, J. Zhou, B. Li and Y. B. Wang, presented at the 18th IEEE International Symposium, 2009 (unpublished).

  11. 11.

    C.Y. Zhang, MHA, Thesis, Wuhan University of Technology, 2010.

  12. 12.

    W.F. Yao, H. Wang, X.H. Xu, J.T. Zhou, X.N. Yang, Y. Zhang, S.X. Shang and M. Wang, Chemical Physics Letters 377 (5–6), 501–506 (2003).

  13. 13.

    D.A. Chang, P. Lin and T.Y. Tseng, J. Appl. Phys. 77, 4445–4451 (1995)

  14. 14.

    S.I. Stepanov, Rep. Prog. Phys. 57 (1), 39–110 (1994).

    CAS  Article  Google Scholar 

  15. 15.

    H.Y. Zhu, R. Jiang, Y.J. Guan, Y.Q. Fu, L. Xiao and G.M. Zeng, Separation and Purification Technology 74, 187–194 (2010).

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to Shundong Bu.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Bu, S., Cai, D., Li, J. et al. Structure and photocatalytic properties of Bi25FeO40 crystallites derived from the PEG assisted sol-gel methods. MRS Online Proceedings Library 1324, 1605 (2011). https://doi.org/10.1557/opl.2011.843

Download citation