Onset of magnetic interface exchange interactions in epitaxially grown Mn/Co(001)


Manganese (Mn) grows in a metastable expanded (c/a > 1) face-centered-tetragonal (fct) phase on thin fct-Co(001) template films. A layer-by-layer growth mode is observed for small Mn thicknesses. Antiferromagnetism (AFM) of fct-Mn is evidenced by the observation of shifted magnetization loops antiparallel to the cooling field direction (negative bias) and enhanced coercive fields for Co/Mn bilayers. At low temperature, magnetic exchange interactions are detected at the Co/Mn interface for nominal Mn thicknesses as low as 1.4 monolayer (ML), indicating the onset of AFM in 2-ML-thick Mn islands. However, between 2- and 5-ML Mn, a positive bias of the magnetization loops is observed in a certain temperature range below the blocking temperature (TB) of the films. This peculiar behavior is explained by the dependence of TB on both the local Mn ML thickness and the Mn island size, leading to a unidirectional coercivity enhancement in a temperature range where both blocked and unblocked regions coexist in the Mn layers.

This is a preview of subscription content, access via your institution.


  1. 1.

    J. Nogués and I.K. Schuller: Exchange bias. J. Magn. Magn. Mater. 192, 203 (1999).

    Article  Google Scholar 

  2. 2.

    A.E. Berkowitzand K. Takano: Exchange anisotropy—A review. J. Magn. Magn. Mater. 200, 552 (1999).

    Article  Google Scholar 

  3. 3.

    J. Nogués, J. Sort, V. Langlais, V. Skumryev, S. Suriñach, J.S. Muñoz, and M.D. Baró: Exchange bias in nanostructures. Phys. Rep. 422, 65 (2005).

    Article  Google Scholar 

  4. 4.

    J. Hafnerand D. Spišák: Ab initio investigation of the magnetism of tetragonal Mn: Bulk, surface, ultrathin films, and multilayers. Phys. Rev. B 72, 144420 (2005).

    Article  Google Scholar 

  5. 5.

    J.T. Kohlheppand W.J.M. de Jonge: Stabilization of metastable expanded face-centered-tetragonal manganese. Phys. Rev. Lett. 96, 237201 (2006).

    Article  Google Scholar 

  6. 6.

    A.K. Schmidand J. Kirschner: In situ observation of epitaxial growth of Co thin films on Cu(100). Ultramicroscopy 42, 483 (1992).

    Article  Google Scholar 

  7. 7.

    H. Wieldraaijer, W.J.M. de Jonge, and J.T. Kohlhepp: Monolayer resolved oscillating hyperfine fields in epitaxial face-centered-tetragonal Co(001) films. Phys. Rev. Lett. 93, 177205 (2004).

    CAS  Article  Google Scholar 

  8. 8.

    H. Wieldraaijer, W.J.M. de Jonge, and J.T. Kohlhepp: Electric-field gradients in thin face-centered-tetragonal Co films observed by nuclear magnetic resonance. Phys. Rev. B 72, 155409 (2005).

    Article  Google Scholar 

  9. 9.

    W.L. O’Brien and B.P. Tonner: Surface-enhanced magnetic moment and ferromagnetic ordering of Mn ultrathin films on fcc Co(001). Phys. Rev. B 50, 2963 (1994).

    Article  Google Scholar 

  10. 10.

    C. Leighton, J. Nogués, B.J. Jönsson-Åkerman, and I.K. Schuller: Coercivity enhancement in exchange biased systems driven by interfacial magnetic frustration. Phys. Rev. Lett. 84, 3466 (2000).

    CAS  Article  Google Scholar 

  11. 11.

    T. Gredig, I.N. Krivorotov, P. Eames, and E.D. Dahlberg: Unidirectional coercivity enhancement in exchange-biased Co/CoO. Appl. Phys. Lett. 81, 1270 (2002).

    CAS  Article  Google Scholar 

Download references

Author information



Corresponding author

Correspondence to J. T. Kohlhepp.

Additional information

This paper was selected as the Outstanding Meeting Paper for the 2006 MRS Spring Meeting Symposium Q Proceedings, Vol. 941E. DOI: 10.1557/JMR.2007.0074

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Kohlhepp, J.T., Wieldraaijer, H. & de Jonge, W.J.M. Onset of magnetic interface exchange interactions in epitaxially grown Mn/Co(001). Journal of Materials Research 22, 569–572 (2007). https://doi.org/10.1557/jmr.2007.0074

Download citation