Growth of Co Nanoclusters on SiC Honeycomb Templates

Abstract

A honeycomb-like SiC reconstructed surface with regular, periodic porosity in the nano-scale range has been used as an effective template for the formation of monodispersed Co nanoclusters. In-situ scanning tunneling microscopy (STM) was used to study the nucleation process of the Co nanoclusters on this template. The deposition of Co at different substrate temperature was investigated by STM. It is found that the failure in the deposition of Co nanoclusters on the SiC honeycomb template with substrate temperatures higher than room temperature (RT) might be due to the high desorption rate of the adsorbed Co atoms.

This is a preview of subscription content, access via your institution.

References

  1. [1]

    J. V. Barth, J. Weckesser, C. Cai, P. Günter, L. Bürgi, O. Jeandupeux, and K. Kern, Angew. Chem. Int. Ed. 39, 1230 (2000).

    CAS  Article  Google Scholar 

  2. [2]

    J. Weckesser, A. De Vita, J.V. Barth, C. Cai, and K. Kern, Phys. Rev. Lett. 87, 096101 (2001).

    CAS  Article  Google Scholar 

  3. [3]

    H. Spillmann, A. Dmitriev, N. Lin, P. Messina, J. V. Barth, and K. Kern, J. Am. Chem.Soc. 125, 10725 (2003).

    CAS  Article  Google Scholar 

  4. [4]

    J. V. Barth, J. Weckesser, G. Trimarchi, M. Vladimirova, A. De Vita, C. Cai, H. Brune, P. Günter, and K. Kern, J. Am. Chem.Soc. 124, 7991 (2002).

    CAS  Article  Google Scholar 

  5. [5]

    S. De Feyter, A. Gesquière, M. Klapper, K. Mullen, and F. C. De Schryver, Nano. letter. 3, 1485 (2003).

    Article  Google Scholar 

  6. [6]

    S. Berner, M. de Wild, L. Ramoino, S. Ivan, A. Baratoff, H.-J. Güntherodt, H. Suzuki, D. Schlettwein, and T. A. Jung, Phys. Rev. B. 68, 115410 (2003).

    Article  Google Scholar 

  7. [7]

    J. A. Theobald, N. S. Oxtoby, M. A. Phillips, N. R. Champness, and P. H. Beton, Nature 424, 1029 (2003).

    CAS  Article  Google Scholar 

  8. [8]

    H. Brune, M. Giovannini, K. Bromann, and K. Kern, Nature 394, 451 (1998).

    CAS  Article  Google Scholar 

  9. [9]

    M. Corso, W. Auwärter, M. Muntwiler, A. Tamai, T. Greber, and J. Osterwalder, Science 303, 217 (2004).

    CAS  Article  Google Scholar 

  10. [10]

    K. H. Wu, Y. Fujikawa, T. Nagao, Y. Hasegawa, K. S. Nakayama, Q. K. Xue, E. G. Wang, T. Briere, V. Kumar, Y. Kawazoe, S. B. Zhang, and T. Sakurai, Phys. Rev. Lett. 91, 126101 (2003).

    Article  Google Scholar 

  11. [11]

    J. L. Li, J. F. Jia, X. J. Liang, X. Liu, J. Z. Wang, Q. K. Xue, Z. Q. Li, J. S. Tse, Z. Y. Zhang, and S. B. Zhang, Phys. Rev. Lett. 88, 066101 (2002).

    Article  Google Scholar 

  12. [12]

    M. Y. Lai, and Y. L. Wang, Phys. Rev. B. 64, 241404 (2001).

    Article  Google Scholar 

  13. [13]

    V. G. Kotlyar, A. V. Zotov, A. A. Saranin, T. V. Kasyanova, M. A. Cherevik, I. V. Pisarenko, and V. G. Lifshits, Phys. Rev. B. 66, 165401 (2002).

    Article  Google Scholar 

  14. [14]

    W. Chen, K. P. Loh, H. Xu, and A. T. S. Wee, Appl. Phys. Lett. 84, 281 (2004).

    CAS  Article  Google Scholar 

  15. [15]

    W. Chen, X. Xie, H. Xu, A. T. S. Wee, and K. P. Loh, J. Phys. Chem. B. 107, 11597 (2003).

    CAS  Article  Google Scholar 

  16. [16]

    L.I. Johansson, Fredrik Owman, and Per Martensson Phys. Rev. B 53, 13793 (1996).

    CAS  Article  Google Scholar 

  17. [17]

    F. Owman, P. Mårtensson, Surf. Sci. 369, 126 (1996).

    CAS  Article  Google Scholar 

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to Wei Chen.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Chen, W., Loh, K.P., Xu, H. et al. Growth of Co Nanoclusters on SiC Honeycomb Templates. MRS Online Proceedings Library 818, 305–311 (2004). https://doi.org/10.1557/PROC-818-M5.5.1

Download citation