Bi-2212 precursor films were deposited on both sides of polycrystalline Ag tapes by electrodeposition. After a melt-solidification process in flowing oxygen atmosphere, c-axis textured Bi-2212 films with Jc( 0T, 4.2K) up to 820,000 A/ cm2 were obtained. A post annealing in flowing nitrogen at 475°C for 25 minutes increased Tc from 72 K to 92 K, and Jc(H=0T) > 17, 000A/ cm2 was observed at 60 K. No scaling behavior of the pinning force was observed, indicating more than one pinning mechanism in thus obtained Bi-2212/Ag tapes.
Similar content being viewed by others
References
K. Heine et al., Appl. Phys. Lett. 55 (1989) 2441.
J. Kase et al., Jpn. J. Appl. 29 (1990) L1096.
K. Togano et al., Adv. Cryo. Eng. Mat. 38 (1992)1081.
G. Villard et al., IEEE Transaction on Applied Superconductivity 11(2001) 3039.
H. Miao et al., Physica C 303 (1998)81.
D.J. Zuraski, et al, J. Electrochem. Soc. 135 (1988) 1607.
M. Maxfield et al., Appl. Phys. Lett. 54 (1989) 1932.
R.N. Bhattacharya et al., Science and Technology of Thin Film Superconductors, 2 (1991) 243.
R.N. Bhattacharya et al., Physica C 211 (1993) 475.
R.N. Bhattacharya et al., Physica C 333 (2000) 59.
E.E. Hellstrom et al., Physica B 216 (1996) 252.
M.R. Koblischika, Physica C 282-287 (1997) 2193.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Chen, J., Bhattachary, R., Padmanabhanl, R. et al. Preparation of Bi-2212/Ag Tapes by Electrodeposition. MRS Online Proceedings Library 689, 45 (2001). https://doi.org/10.1557/PROC-689-E4.5
Published:
DOI: https://doi.org/10.1557/PROC-689-E4.5