Abstract
The purpose of this research was to characterize the oxidation behavior of several model (TiAl, TiAl-Nb, TiAl-Cr, TiAl-Cr-Nb) and engineering alloys (XD, K5, Alloy 7, WMS) after long-term isothermal exposure (∼7000 h) at 704°C, and after shorter time exposure (∼1000 h) at 800°C in air. High-resolution field emission and microprobe scanning electron microscopy were used to characterize the scales formed on these alloys. Similarities and differences observed in the scales are correlated with the various ternary and quaternary microalloying additions.
Similar content being viewed by others
References
P.A. Bartolotta and D. L. Krause, NASA/TM-1999–209071, 1999.
H. Clemens, H. Kestler, Adv. Eng. Mater. 2 (9), 551 (2000).
D. Eylon, M. M. Keller and P. E. Jones, Intermetallics 6 (7–8), 703 (1998).
T. Noda, Intermetallics 6 (7–8), 709 (1998).
I.E. Locci, M.P. Brady, R.A. Mackay and J.W. Smith, Scripta Mat. 37 (6), 761 (1997).
M.P. Brady, W.J. Brindley, J.L. Smialek, I.E. Locci, JOM 48 (11), 46 (1996).
N.S. Jacobson, M. P. Brady, and G. M. Mehrotra, Oxidation of Metals 52, 537 (1999).
V.A.C. Haanappel et al., Oxidation of Metals 48, 263 (1997).
M. Nombela, V. Kolarik, M. Gross, H. Fietzek, and N. Eisenreich, Matl. High Temp. 17, 49 (2000).
A. Rahmel, W.J. Quadakkers, and M. Schutze, Materials and Corrosion 46, 271 (1995).
J.C. Schaeffer et al., in Gamma Titanium Aluminides, edited by Y-W Kim et al. (TMS, 1995) p. 71.
J.M. Rakowski et al., Scr. Metall. Mater. 33, 997 (1995).
M. Yoshihara, K. Miura and Y-W Kim, et al., Scr. Metall. Mater. 11, p. 93.
F. Dettenwanger et al., Matls & Corrosion 48 (1), 23 (1996).
R.W. Beye and R. Gronsky, Acta Metall. Mater. 42 (4) 1373 (1994).
C. Lang and M. Schutze, Mater. Corros. 48, 13 (1997).
W.J. Quadakkers, N. Zheng, A. Gil, E. Wallura, H. Hoven, High Temp. Corr. Prot. Mat. 4, 187 (1997).
E.H. Copland, B. Gleeson, D.J. Young, Acta Mater. 47 (10), 2937 (1999).
W.B. Retallick, M.P. Brady, D.L. Humphrey, Intermetallics 6, 335 (1998).
P. Perez, J.A. Jimenez, G. Frommeyer, and P. Adv. Matl. Sc. Eng. A 284, 138 (2000).
J. Magnan et al., Met. and Mat. Trans. A 30, 19 (1999).
V.A.C. Haanappel et al., Mat. High Temp. 14 (1), 19 (1997).
J. Doychak, S. V. Raj, I.E. Locci, M. Hebsur, NASA CP-10082, 18 (1991).
M.P. Brady, E.D. Verink Jr., J.W. Smith, Oxidation of Metals 51 (5–6), 539 (1999).
Y. Shida, and H. Anada, Oxidation of Metals 45 (1–2), 197 (1996).
J.D. Sunderkotter et al., Intermetallics 5, 525 (1997).
V. Shemet et al., Oxidation of Metals 54 (3–4), 211 (2000).
Acknowledgment
Appreciation is expressed to J. W. Smith and T. R. McCue for dedicated and excellent microscopy work. The long-term oxidation study efforts of the engineering γ-alloys at NASA Glenn was initiated by Bill Brindley, with whom many useful discussions on the oxidation and embrittlement mechanisms in Ti-base alloys are gratefully acknowledged.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Locci, I.E., Brady, M.P. & Smialek, J.L. Long Term Oxidation of Model and Engineering TiAl Alloys. MRS Online Proceedings Library 646, 444–449 (2000). https://doi.org/10.1557/PROC-646-N5.50.1
Published:
Issue Date:
DOI: https://doi.org/10.1557/PROC-646-N5.50.1