The Influence of some Microstructural and Test Parameters on the Tensile Stress and Ductility Behaviour of a MA FeAl Intermetallic


This study examines the influence of microstructural parameters (grain and dispersoid size, vacancy content) and some test parameters (strain rate, protective oxide coatings, air and water vapour excluding films, and surface geometrical quality) on the tensile behaviour (yield stress, work hardening rate, tensile stress, ductility) of a mechanically-alloyed, fine-grained Fe-40Al intermetallic. Major changes of strength and ductility are obtained by changing grain size (1% and 10% for grain sizes of 100µm and 1µm) and by avoiding premature stress/strain concentrators (ductility increased from 5% to 10% for imperfectly machined to prepolished samples). Ductility variations are interpreted using a slow-crack-propagation-to-instability model, where the roles of environment, surface state, deformation processes, and fracture mechanisms can be distinguished.

This is a preview of subscription content, access via your institution.


  1. 1

    C.G. McKamey, J.H. CeVan, P.F. Tortorelli and V.K. Sikka, J. Mater. Res. 6, 1779 (1991).

    CAS  Article  Google Scholar 

  2. 2

    C.T. Liu, E.H. Lee and C.G. McKamey, Scripta Metall. 23, 875 (1989).

    CAS  Article  Google Scholar 

  3. 3

    C.T. Liu and E.P. George, Scripta Metall. 24, 1285 (1990).

    CAS  Article  Google Scholar 

  4. 4

    M.A. Crimp, K.M. Vedula and D.J. Gaydosh, in High Temperature Ordered Intermetallic Alloys II, Vol. 81, eds. N.S. Stoloff, C.C. Koch, C.T. Liu and O. Izumi, p. 499, MRS Symposium Proceedings, Pittsburgh, PA, 1987.

  5. 5

    P. Nagpal and I. Baker, Mater. Char. 27, 167 (1991).

    CAS  Article  Google Scholar 

  6. 6

    D.J. Gaydosh, S.L. Draper, R.D. Noebe and M.V. Nathal, Mater. Sci. Eng. A150, 7 (1992).

    CAS  Article  Google Scholar 

  7. 7

    P. Nagpal and I. Baker, Scripta Metall. Mater. 25, 2577 (1991).

    CAS  Article  Google Scholar 

  8. 8

    I. Baker, O. Klein, C. Nelson and E.P. George, Scripta Metall. Mater. 30, 863 (1994).

    CAS  Article  Google Scholar 

  9. 9

    L.M. Pike and C.T. Liu, Scripta Mater. 38, 1475 (1998).

    CAS  Article  Google Scholar 

  10. 10

    M.A. Crimp and K.M. Vedula, Mater. Sci. Eng. 78, 193 (1986).

    CAS  Article  Google Scholar 

  11. 11

    D.V. Gaydosh, S.L. Draper and M.V. Nathal, Metall. Trans. 20A, 1701 (1989).

    CAS  Article  Google Scholar 

  12. 12

    I. Baker and P. Munroe, Int. Mater. Rev. 42, 181 (1997).

    CAS  Article  Google Scholar 

  13. 13

    R. Baccino, D. San Filippo, F. Moret, A. Lefort and G. Webb, Proc. PM'94, Powder Metallurgy World Congress, Paris, June 1994, Vol. II, Editions de Physique, Les Ulis, 1994, p. 1239.

  14. 14

    D.G. Morris and S. Gunther, Mater. Sci. and Eng. A208, 7 (1996).

    CAS  Article  Google Scholar 

  15. 15

    D.G. Morris, S. Gunther and C. Briguet, Scripta Mater. 37, 71 (1997).

    CAS  Article  Google Scholar 

  16. 16

    M.A. Montealegre, J.L. Gonzalez-Carrasco, M.A. Morris-Muñoz, J. Chao and D.G. Morris, Intermetallics 8, 439 (2000).

    CAS  Article  Google Scholar 

  17. 17

    J. Chao, M.A. Muñoz-Morris, J.L. Gonzalez-Carrasco and D.G. Morris, submitted to Intermetallics.

  18. 18

    D.B. Kasul and L.A. Heldt, Metall. and Mater. Trans. 25A, 1285 (1994).

    CAS  Article  Google Scholar 

  19. 19

    J.H. Schneibel and M.G. Jenkins, Scripta Metall. Mater. 28, 389 (1993).

    CAS  Article  Google Scholar 

  20. 20

    A. Tonneau, Ph. D. Thesis, University of Poitiers, 20th Oct. 1999.

Download references

Author information



Corresponding author

Correspondence to J. Chao.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Chao, J., Muñoz-Morris, M., Gonzalez-Carrasco, J. et al. The Influence of some Microstructural and Test Parameters on the Tensile Stress and Ductility Behaviour of a MA FeAl Intermetallic. MRS Online Proceedings Library 646, 1–6 (2000).

Download citation