TEM Characterization of Corrosion Products Formed on a Stainless Steel-Zirconium Alloy

Abstract

The corrosion products formed on a stainless steel-15Zr (SS-15Zr) alloy have been characterized by transmission electron microscopy (TEM) and energy dispersive x-ray spectroscopy (EDS). Examination of alloy particles that were immersed in 90’C deionized water for two years revealed that different corrosion products were formed on the stainless steel and intermetallic phases. Two corrosion products were identified on an austenite particle: trevorite (NiFe2O4) in the layer close to the metal and maghemite (Fe2O3) in the outer layer. The corrosion layer formed on the intermetallic was uniform, adherent, and amorphous. The EDS analysis indicated that the layer was enriched in zirconium when compared with the intermetallic composition. High-resolution TEM images of the intermetallic-corrosion layer interface show an interlocking metal-oxide interface which may explain the relatively strong adherence of the corrosion layer to the intermetallic surface. These results will be used to evaluate corrosion mechanisms and predict long-term corrosion behavior of the alloy waste form.

This is a preview of subscription content, access via your institution.

References

  1. 1.

    S.M. McDeavitt, D.P. Abraham, and J.Y. Park, J. Nucl. Mat. 257, 21–34 (1998).

    CAS  Article  Google Scholar 

  2. 2.

    D.P. Abraham, D.D. Keiser Jr, and S.M. McDeavitt, Proc. Intl. Conf. on Decommissioning and Decontamination and on Nuclear and Hazardous Waste Management, Vol. 2, American Nuclear Society, LaGrange Park, IL p. 783 (1998).

    CAS  Google Scholar 

  3. 3.

    D.P. Abraham, J.W. Richardson Jr, and S.M. McDeavitt, Mat. Sci. Eng. A239-240, 658 (1997).

    CAS  Article  Google Scholar 

  4. 4.

    A. T. Nakayama and Y. Oshida, Corrosion 24, 336 (1968).

    CAS  Article  Google Scholar 

  5. 5.

    J. E. Castle and C. R. Clayton, Passivity of Metals, R. P. Frankenthal and J. Kruger, eds., The Electrochemical Society Inc, Princeton, NJ p. 714 (1978).

  6. 5.

    G. Aronwitz and N. Hackerman, J. Electrochem. Soc. 110, 633 (1963).

    Article  Google Scholar 

  7. 6.

    C. L. McBee and J. Krueger, Electrochim. Acta 17, 1337 (1972).

    CAS  Article  Google Scholar 

  8. 9.

    T. P. Hoar, Palladium Medal Address, J. Electrochem. Soc. 117, 17c (1970).

    CAS  Google Scholar 

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to J. S. Luo.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Luo, J.S., Abraham, D.P. TEM Characterization of Corrosion Products Formed on a Stainless Steel-Zirconium Alloy. MRS Online Proceedings Library 608, 583 (1999). https://doi.org/10.1557/PROC-608-583

Download citation