Relationship Between Structure and Luminescent Properties of Epitaxial Grown Y2O3:Eu Thin Films on LaAlO3 Substrates

Abstract

Cathodoluminescence images of individual pores have been obtained at nanometer resolution in europium-activated yttrium oxide (Y2O3:Eu) (001) thin films, epitaxially grown on LaAlO3 (001) substrates. Comparison with Z-contrast images, obtained simultaneously, directly show the “dead layer” to be about 5 nm thick. This “dead layer” is the origin of the reduced emission efficiency with increasing pore size. Pore sizes were varied by using different substrate temperatures and laser pulse repetition rates during film growth. These films are epitaxially aligned with the substrate, which is always Al terminated.

This is a preview of subscription content, access via your institution.

References

  1. 1.

    L. Manchanda and M. Gurvitch, IEEE Electronic Devices Lett. 9, 180(1988).

    CAS  Article  Google Scholar 

  2. 2.

    T.S. Kalkur, Y.R. Kwor, and C.A. Paz de Araujo, Thin Solid Films 170, 185(1989).

    CAS  Article  Google Scholar 

  3. 3.

    S.J. Duclos, C.D. Greskovich, and C.R. O‘Clair, MRS Symp. Proc. 348, 503(1994).

  4. 4.

    G. Blasse and B.C. Grabmaier, Lum. Mater. Springer, Berlin (1994)

    Google Scholar 

  5. 5.

    S.C. Choi, M.H. Cho, S.W. Whangbo, C.N. Whang, S.B. Kang, S.I. Lee, and M.Y. Lee, Appl. Phys. Lett. 71, 903(1997).

    CAS  Article  Google Scholar 

  6. 6.

    R.P. Rao, Solid State Communications 99, 439(1996)

    CAS  Article  Google Scholar 

  7. 7.

    K.-I. Onisawa, M. Fuyama, K. Tamura, K. Taguchi, T. Nakayama, and Y.A. Ono, J. Appl. Phys. 68, 719(1990).

    CAS  Article  Google Scholar 

  8. 8.

    A.F. Jankowski, L.R. Schrawyer, and J.P. Hayes, J. Vac. Sci. Technol. A11, 1548(1993)

    Article  Google Scholar 

  9. 9.

    W.M. Cranton, D.M. Spink, R. Stevens, and C.B. Thomas, Thin Solid Films 226, 156(1993).

    CAS  Article  Google Scholar 

  10. 10.

    S.L. Jones, D. Kumar, R.K. Singh, and P.H. Holloway, Appl. Phys. Lett. 71, 404(1997).

    CAS  Article  Google Scholar 

  11. 11.

    K.G. Cho, D. Kumar, D.J. Lee, S.L. Jones, P.H. Holloway, and R.K. Singh, Appl. Phys. Lett. 71, 3335(1997).

    CAS  Article  Google Scholar 

  12. 12.

    K.G. Cho, D. Kumar, S.L. Jones, D.J. Lee, P.H. Holloway, and R.K. Singh, J. Electrochem. Soc. 145, 3456(1998).

    CAS  Article  Google Scholar 

  13. 13.

    H-J. Gao, D. Kumar, K.G. Cho, P.H. Holloway, R.K. Singh, X.D. Fan, Y. Yan, and S.J. Pennycook, Appl. Phys. Lett. 75, 2223(1999).

    CAS  Article  Google Scholar 

  14. 14.

    S. J. Pennycook, ‘STEM: Z-contrast’, in Handbook of Microscopy, ed. By S. Amelinckx, D. van Dyck, J. van Landuyt, and G. van Tendeloo, VCH Publishers, Weinheim, Germany, pp. 595 (1997)

  15. 15.

    J. Fitz-Gerald, S.J. Pennycook, H. Gao, V. Krishnamoorthy, J. Marcinka, W. Glenn, R. Singh, Mat. Res. Soc. Proc. Spring} 1998, 502, (1998)

    Google Scholar 

  16. 16.

    J. Fitz-Gerald, T. Trottier, R.K. Singh, P.H. Holloway, Appl. Phys. Lett. 72, 1838(1998).

    CAS  Article  Google Scholar 

  17. 17.

    D. Kumar, J. Fitz-Gerald, R.K. Singh, Appl. Phys. Lett. 72, 1451(1998).

    CAS  Article  Google Scholar 

  18. 18.

    H-J. Gao, {etet al.}, Appl Phys. Lett. (to be published).

  19. 19.

    N.D. Browning, M. F. Chisholm, S.J. Pennycook, Nature 366, 143(1993).

    CAS  Article  Google Scholar 

  20. 20.

    J.L. Daams, P. Villars, and J.H.N. Vanvucht, Atlas of Crystal Structure types for Intermetallic Phases, P.6706. ASM International, Materials Park. OH(1994)

    Google Scholar 

  21. 21.

    M.G. Paten and E.N. Maslen, Acta. Crystallogr. 19, 307(1965).

    Article  Google Scholar 

  22. 22.

    B.H. O'Conner, T.M. Valentine, Acta Crystallogr. B 25, 2140(1969).

    Article  Google Scholar 

  23. 23.

    M. Faucher, J. Pannetier, Acta Crystallogr.B 36, 3209(1980).

    Article  Google Scholar 

  24. 24.

    W.v. Schaik and G. Blasse, Chem. Mater. 4, 410(1992).

    Article  Google Scholar 

  25. 25.

    F. Jollet, C. Noguera, N. Thromat, M. Gautier, and J.P. Duraud, Phys. Rev. B 42, 7587(1990).

    CAS  Article  Google Scholar 

  26. 26.

    E.S. Machlin, Materials Science in Microelectronics, Giro Press, Croton-on-Hudson (1995)

    Google Scholar 

Download references

Acknowledgments

The authors are grateful to A. Kadavanich for assistance with the CL detection system. The work at ORNL was sponsored by the Division of Materials Sciences, U.S. Department of Energy, under Contract No. DE-AC05-96OR22464 with Lockheed Martin Energy Research Corporation, and by appointment to the ORNL Postdoctoral Research Program administrated jointly by ORISE and ORNL. The work at University of Florida was supported by the Phosphor Technology Center of Excellence by DARPA Grant No. MDA972-93-1-0030.

Author information

Affiliations

Authors

Corresponding author

Correspondence to H-J. Gao.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Gao, HJ., Duscher, G., Fan, X.D. et al. Relationship Between Structure and Luminescent Properties of Epitaxial Grown Y2O3:Eu Thin Films on LaAlO3 Substrates. MRS Online Proceedings Library 589, 203 (1999). https://doi.org/10.1557/PROC-589-203

Download citation