Optical Probes and Electrical Resistivity Measurements of Conductive Die Attach Adhesives

Abstract

An important phenomenon in silver (Ag) particle-filled adhesives is the development of electrical conductivity as the polymer composite is cured. We report the results of optical and electrical measurements performed on a commercially available Ag particle/polymer composite as a function of sample temperature. Surface enhanced Raman scattering (SERS) was used to probe the chemical nature of the Ag interface while a four-point contact probe monitored the onset of DC electrical conductivity. Complementary to the die attach adhesives studies, SERS experiments were also performed on commercially available neat Ag flake with controlled adsorbate coverages. For both the neat flake and filled adhesive, a carboxylate layer was attached to an oxygen-covered Ag flake surface via the carboxylic acid end of the molecule. The SERS results observed a partial decomposition of the carboxylate species into an amorphous carbon layer upon an increase in the temperature of both the flake and filled adhesive samples. However, the temperature threshold for the chemical conversion was lower for the Ag-filled adhesive relative to the neat flake. In the composite samples, the formation of the amorphous carbon layer occurred well below the curing temperature and coincided with a corresponding decrease in the electrical resistivity of the adhesive. Thus, an initial step in developing electrical conductivity appears to be the partial conversion of the lubricant adsorbate to an amorphous carbon layer.

This is a preview of subscription content, access via your institution.

References

  1. 1.

    Surface Enhanced Raman Scattering, edited by R. K Chang and T. E. Furtak,(Plenum, New York, 1982).

    Google Scholar 

  2. 2.

    A. G. Brolo, D. E. Irish, and B.D. Smith, J. Mol. Struct. 405, 29 (1997).

    CAS  Article  Google Scholar 

  3. 3.

    I. I. Suni, J. Appl. Electrochem. 27, 1219 (1997).

    CAS  Article  Google Scholar 

  4. 4.

    J. I. Gersten and A. Nitzan, in Surface Enhanced Raman Scattering, edited by R. K Chang and T. E. Furtak (Plenum, New York, 1982), p. 89.

  5. 5.

    J. Miragliotta, R. C. Benson, and T. E. Phillips, MRS Symposium Proceeding vol. 445, edited by S. K. Groothuis, P. S. Ho, K. Ishida, and T. Wu, (Materials Research Society, Pittsburgh, PA, 1997), pg. 217.

    CAS  Article  Google Scholar 

  6. 6.

    J. H. Schachtschneider and R. G. Synder, Spectrochim. Acta 19 (1963) 117.

    CAS  Article  Google Scholar 

  7. 7.

    Infrared and Raman Characteristic Frequencies of Organic Molecules, edited by D. Lin-Vien, N. B. Colthup, W. G. Fateley, and J. G. Grasselli (Academic Press, New York, 1991), pg. 356.

    Google Scholar 

  8. 8.

    J. L. Delarbre, E. Fabreque, L. Maury, and L. Bardet, J. Raman Spectro. 20 (1989) 41.

    CAS  Article  Google Scholar 

  9. 9.

    B. Sexton and R. J. Madix, Surf. Sci. 105 (1981) 177.

    CAS  Article  Google Scholar 

  10. 10.

    M. Moskovits and J. S. Suh, J. Am. Chem. Soc. 107 (1985) 6826.

    CAS  Article  Google Scholar 

  11. 11.

    E. H. Lee, D. M. Hembree, Jr., G. R. Rao, and L. K. Mansur, Phys. Rev. B48 (1993) 15540.

    CAS  Article  Google Scholar 

  12. 12.

    R. L. Opila and J. M. Worlock, J. Electrochem. Soc. 133 (1986) 974.

    CAS  Article  Google Scholar 

Download references

Author information

Affiliations

Authors

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Miragliotta, J., Benson, R.C., Phillips, T.E. et al. Optical Probes and Electrical Resistivity Measurements of Conductive Die Attach Adhesives. MRS Online Proceedings Library 515, 245–250 (1998). https://doi.org/10.1557/PROC-515-245

Download citation