Comparison of the Morphological and Optical Characteristics of InP Islands on GalnP/GaAs (311)A and (100)

Abstract

We have studied the effect of surface orientation on the optical and morphological characteristics of coherently-strained InP islands grown on GaInP/GaAs. The differences between islands grown on the (100) orientation and the (311)A orientation are studied. Islands grown on the (311)A orientation are more dense than the islands grown on the (100) orientation. For the (100) orientation, the island height distribution is bimodal peaked at 20 Å and 220 Å. For the (311)A orientation, the island height distribution is also bimodal peaked at 15 Å and 60 Å. Photoluminescence measurements for the (311)A orientation show a peak at 1.9 eV attributed to small islands. This peak is shifted to higher energies in comparison to the corresponding peak for the (100) orientation which is at 1.77 eV. This peak shift is due to the fact that the small islands on the (311)A orientation are smaller than the corresponding islands on the (100) orientation.

This is a preview of subscription content, access via your institution.

References

  1. 1.

    C. Weisbuch, and B. Vinter, Quantum Semiconductor Structures. Academic Press, Inc., San Diego, CA, 1991, pp. 191–1943 and references therein.

    Google Scholar 

  2. 2.

    D. Eaglesham, and M. Cerullo, Phys. Rev. Lett. 64, p. 1943 (1990).

    CAS  Article  Google Scholar 

  3. 3.

    R. Nötzel, Semiconductor Sci. and Technol. 11, p. 1365 (1996) and references therein.

    Article  Google Scholar 

  4. 4.

    G.S. Solomon, J.A. Trezza, and J.S. Harris Jr., Appl. Phys. Lett. 66, p. 991 (1995).

    CAS  Article  Google Scholar 

  5. 5.

    D. Leonard, M. Krishnamurthy, S. Fafard, J.L. Merz, and P.M. Petroff, J. Vac. Sci. and Technol. B 12, p. 1063 (1994).

    CAS  Article  Google Scholar 

  6. 6.

    M. Sopanen, H. Lipsanen, and J. Ahopelto, Appl. Phys. Lett. 67, p. 3768 (1995).

    CAS  Article  Google Scholar 

  7. 7.

    V. Bressler-Hill, C.M. Reaves, S. Varma, S.P. DenBaars, and W.H. Weinberg, Surf. Sci. 341 p. 29 (1995).

    CAS  Article  Google Scholar 

  8. 8.

    C.M. Reaves, V. Bressler-Hill, W.H. Weinberg, and S.P. DenBaars, J. Electron. Mater. 24, p. 1605 (1995).

    CAS  Article  Google Scholar 

  9. 9.

    J. Temmyo, A. Kozen, T. Tamamura, R. Nötzel, T. Fukui, and H. Haasegawa, J. Electron. Mater. 25, p. 431 (1996).

    CAS  Article  Google Scholar 

  10. 10.

    R. Nötzel, J. Temmyo, and T. Tamamura, Nature 369, p. 131 (1994).

    Article  Google Scholar 

  11. 11.

    C.M. Reaves, V. Bressler-Hill, S. Varma, W.H. Weinberg, and S.P. DenBaars, Surf. Sci. 326, p. 209 (1995).

    CAS  Article  Google Scholar 

  12. 12.

    C.M. Reaves, N.A. Cevallos, G.C. Hsueh, Y.M. Cheng, W.H. Weinberg, P.M. Petroff, and S.P. DenBaars, Seventh International Conference on Indium Phosphide and Related Materials (New York, IEEE, 1995) pp. 307-10.

    Google Scholar 

  13. 13.

    N. Carlsson, W. Seifert, A. Petersson, P. Castrillo, M.E. Pistol, and L. Samuelson, Appl. Phys. Lett. 65, p. 3093 (1994).

    CAS  Article  Google Scholar 

  14. 14.

    CM. Reaves, R.I. Pelzel, G.C. Hsueh, W.H. Weinberg, and S.P. DenBaars, Appl. Phys. Lett., in press.

  15. 15.

    D.I. Libyshev, P.P. Gonzalez-Borrero, E. Marega Jr., E. Petitprez, and P. Basmaji, J. Vac. Sci. Tech. B 14, p. 2212 (1996).

    Article  Google Scholar 

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to W. H. Weinberg.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Pelzel, R.I., Reaves, C.M., DenBaars, S.P. et al. Comparison of the Morphological and Optical Characteristics of InP Islands on GalnP/GaAs (311)A and (100). MRS Online Proceedings Library 448, 187–192 (1996). https://doi.org/10.1557/PROC-448-187

Download citation