Abstract
The ionic conductivity of LiI thin films grown on sapphire(0001) substrates has been studied in-situ during deposition as a function of film thickness and deposition conditions. LiI films were produced at room temperature by sublimation in an ultra-high-vacuum system. The conductivity of the LiI parallel to the film/substrate interface was determined from frequency-dependent impedance measurements as a function of film thickness using Au interdigital electrodes deposited on the sapphire surface. The measurements show a conduction of ~5 times the bulk value at the interface which gradually decreases as the film thickness is increased beyond 100 nm. This interfacial enhancement is not stable but anneals out with a characteristic log of time dependence. Fully annealed films have an activation energy for conduction (σT) of ~0.47 ±.03 eV, consistent with bulk measurements. The observed annealing behavior can be fit with a model based on dislocation motion which implies that the increase in conduction near the interface is not due to the formation of a space-charge layer as previously reported but to defects generated during the growth process. This explanation is consistent with the behavior exhibited by CaF2 films grown under similar conditions.
Similar content being viewed by others
References
N. J. Dudney, Ann. Rev. Mater. Sci.19, 103 (1989).
C. C. Liang, J. Electrochem. Soc.120, 1289 (1973).
T. Jow and J. B. Wagner, Jr., J. Electrocem. Soc.126, 1963 (1979).
K. Shahi and J. B. Wagner, Jr., J. Electrochem. Soc.128, 6 (1981).
O. Nakamura and J. B. Goodenough, Sol. State Ionics7, 119 (1982).
F.W. Poulsen, N.H. Andersen, B. Kindl, and J. Schoonman, Sol. State Ionics9&10, 119 (1983).
M. R.-W. Chang, K. Shah, and J. B. Wagner, Jr., J. Electrochem. Soc.131, 1213 (1984).
S. Fujitsu, M. Miyayama, K. Koumoto, H. Yanagida, and T. Kanazawa, J.Mater. Sci.20, 2103 (1985).
N. J. Dudney, J. Am. Cer. Soc.70, 65 (1987).
F. A. Modine and D. Lubben, J. Appl. Phys.74, 2658 (1993).
K. L. Kliewer and J. S. Kohler, Phys. Rev.140, A1226 (1965).
J. Maier, Sol. State Ionics23, 59 (1987).
N. J. Dudney, J. Am. Cer. Soc.68, 65 (1985).
E. Schreck, K. Läuger, and K. Dransfield, Z. Phys.B62, 331 (1986).
J. R. Macdonald, in Impedance Spectroscopy, John Wiley and Sons, New York (1987).
B. J. H. Jackson and D. A. Young, J. Phys. Chem. Solids30, 1973 (1969).
C. Schlaiker and C. C. Liang, J. Electrochem. Soc.118, 1447 (1971).
F. W. Poulsen, Sol. State Ionics2, 53 (1981).
J. Maier, Phys. Stat. Sol.A112, 115 (1989).
estimated value
W. G. Johnston, Phys. Rev.98, 1777 (1955).
B. Wassermann, T. P. Martin and J. Maier, Sol. State Ionics28–30, 1514 (1988).
B. Wassermann, W. Hönle, and T. P. Martin, Sol. State Comm.65, 561 (1988).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lubben, D., Modine, F.A. Enhanced Ionic Conduction at the Film/Substrate Interface in LiI Thin Films Grown on Sapphire(0001). MRS Online Proceedings Library 318, 445–450 (1993). https://doi.org/10.1557/PROC-318-445
Published:
Issue Date:
DOI: https://doi.org/10.1557/PROC-318-445