Comparative Creep Properties of Single-Phase Intermetallics of the Ti-Al System

Abstract

Creep characteristics of polycrystalline single-phase intermetallics, α2-Ti3Al and γ-TiAl, at 1100 K have been summarized to evaluate their relative strength at elevated temperature at three strain-rate levels, 10−1 10−4 and 10−8s−1, and are compared with those of α Ti-AI terminal solid solution alloys. The strength of these intermetallics is obviously higher than that of α, random solid solutions, especially at low strain-rates. However, the difference in high-temperature long-term strength among inter-metallic alloys is not significant at any strain-rate level.

This is a preview of subscription content, access via your institution.

References

  1. 1.

    H. Oikawa, Mater. Sci. Eng. A152/153, 427–432 (1992).

    Article  Google Scholar 

  2. 2.

    Y. Ishikawa, K. Maruyama and H. Oikawa, Mater. Trans. JIM 33, (1992) (in press).

  3. 3.

    M. Koo, K. Mashino, T. Matsuo and M. Kikuchi, Tainetsu Kinzoku Zairyo 33, 59–67 (1992).

    Google Scholar 

  4. 4.

    Y. Ishikawa, K. Maruyama and H. Oikawa, unpublished work (1992).

  5. 5.

    M. Nobuki, K. Hashimoto, T. Tsujimoto and Y. Asai, Nippon Kinzoku Gakkai-shi 50, 840–844 (1986).

    CAS  Google Scholar 

  6. 6.

    S. Mitao, Y. Kohsaka and C. Ouchi, in THERMEC-88, edited by I. Tamura (ISIJ, Tokyo, 1988), pp.620–627.

  7. 7.

    M. Ohtsuka and H. Oikawa, in Proc, 7th World Conf, on Titanium, edited by I.L. Caplan and F.H. Froes (TMS, Warrendale, 1992), (in press).

  8. 8.

    T. Fukuda, M. Ohtsuka and H. Oikawa: unpublished work (1992).

  9. 9.

    H. Oikawa and T. Oomori, Mater. Sci. Eng. A104, 125–130 (1988).

    CAS  Article  Google Scholar 

  10. 10.

    T. Oomori, T. Yoneyama and H. Oikawa, Trans. Jpn. Inst. Met. 29, 399–405 (1988).

    Article  Google Scholar 

  11. 11.

    H. Oikawa, K. Sasaki, A. Sagara and K. Maruyama, J. Mater. Sci. Lett. 7, 987–988 (1988).

    CAS  Article  Google Scholar 

  12. 12.

    H. Sato and H. Oikawa, Scr. Metall. 22, 87–92 (1988).

    CAS  Article  Google Scholar 

  13. 13.

    S. Nanba and H. Oikawa, Mater. Sci. Eng. A101, 31–37 (1988).

    Article  Google Scholar 

  14. 14.

    M. Doner and H. Conrad, Metall. Trans. 4, 2809–2817 (1973).

    CAS  Article  Google Scholar 

  15. 15.

    M.X. Cui and H. Oikawa, Nippon Kinzoku Gakkai-shi 49, 195–202 (1985).

    CAS  Google Scholar 

  16. 16.

    J.C. Mishurda and J.H. Perepezko, in Microstructure/Property Relationships in Titanium Aluminides and Alloys, edited by Y.W. Kim and R.R. Boyer (TMS, Warrendale, 1991), pp.3–30.

  17. 17.

    M. Seki and H. Oikawa. Mater. Trans. JIM 30, 1027–32 (1989).

    CAS  Article  Google Scholar 

  18. 18.

    H. Oikawa, Y. Ishikawa and K. Masada, unpublished work (1989).

Download references

Acknowledgments

The work was supported in part by a Grant-in-Aid of the Ministry of Education (Grant No.04239105) and by Light Metals Educational Foundation, Incorp.

Author information

Affiliations

Authors

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Maruyama, K., Oikawa, H. Comparative Creep Properties of Single-Phase Intermetallics of the Ti-Al System. MRS Online Proceedings Library 288, 653–658 (1992). https://doi.org/10.1557/PROC-288-653

Download citation