The Surface Interaction of Oxygen with a Gamma TiAl

Abstract

The composition and bonding of incipient and atmospheric oxides grown on a Ti - 47.0 Al - 2.2 Nb alloy were examined using Auger, x-ray, and low-energy ion scattering spectroscopies. The depth distribution of various components was determined with secondary-ion mass spectroscopy (SIMS). An oxide grown on the material in air at room temperature showed advanced Al and Ti oxide bonding states, which had very different stabilities during heating in vacuum up to 600°C. The Ti-oxygen bonding state was markedly reduced while the Al oxide was somewhat enhanced during this process. Further controlled studies at 600°C, involving oxygen adsorption at pressures below ~ 10−6 Torr, showed an initial Al cation surface enrichment until the detectable Al 2p peak was 90% oxidized. Further oxygen exposure gradually produced a fully oxidized Ti valence state with a pronounced enrichment of the Ti cation at the vacuum-solid interface. The results are discussed in terms of the kinetic and thermodynamic factors of the rate-limiting steps in the oxidation process.

This is a preview of subscription content, access via your institution.

References

  1. 1.

    H. G. Nelson, Proc. 2nd Int. SAMPE Metals and Metals Processing Conf., Dayton, OH, August 1988, p. 310.

    Google Scholar 

  2. 2.

    G. Welsch and A. I. Kahveci, Oxidation of High-Temperature Intermetallics, T. Grobstein and J. Doychak (eds.); The Minerals, Metals, and Materials Society, Warrendale, PA, 1989, p. 207.

  3. 3.

    G. H. Meier, D. Appalonia, R. A. Perkins, and K. T. Chiang, Oxidation of High-Temperature Intermetallics, T. Grobstein and J. Doychak (eds.); The Minerals, Metals, and Materials Society, Warrendale, PA, 1989, p. 157.

  4. 4.

    M. Khobaib and F. W. Vahldiek, Proc. 2nd Int. SAMPE Metals and Metals Processing Conf., Dayton, OH, August 1988, p. 262.

    Google Scholar 

  5. 5.

    C. D. Wagner, W. M. Riggs, L. E. Davis, J. F. Molder, and G. E. Muilenberg, Handbook of X-Ray Photoelectron Spectroscopy. Physical Electronics Division, Perkin-Elmer Corp., Eden Prairie, MN, 1979.

    Google Scholar 

  6. 6.

    A. F. Carley. P. R. Chalker, J. C. Riviere, and M. W. Roberts, J. Chem. Soc., Faraday Trans. 1, 83, 351 (1987).

    Article  Google Scholar 

Download references

Acknowledgments

Thanks are given to M. R. Shanabarger (UCSB) for supplying the titanium aluminide sample used in this study. Appreciation is also extended to R. D. Reiswig (Los Alamos) for sample polishing and preparation. This research was supported by NASA-Ames under contract # W-7405-ENG-36.

Author information

Affiliations

Authors

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Taylor, T.N., Paffett, M.T. The Surface Interaction of Oxygen with a Gamma TiAl. MRS Online Proceedings Library 288, 1019–1024 (1992). https://doi.org/10.1557/PROC-288-1019

Download citation