Preparation of Bipbsrcacuo Superconductors by Laser Pedestal Growth Method

Abstract

Bi-Pb-Sr-Ca-Cu-0 superconductors were prepared by the laser pedestal growth method. The high Tc phase was created only by post annealing. As the growing speed increased, the annealing time necessary to obtain a Tc above 100K decreased. When the low Tc phase was aligned with the growing direction, Tc was under 100K, but a Jc of 15B0A/cm2(77.3K, OT) was obtained. In this case, magnetic field dependence below 300 gauss was superior to that of Pb-free materials.

This is a preview of subscription content, access via your institution.

References

  1. 1

    S.Jin, T.H.Tiefel, R.C.Sherwood, M.E.Davis, R.B.van Dover, G. W.Kammlott, R.A.Fastnacht and H.D.Keith, Appl. Phys. Lett.,51 (24), 2074 (1988)

    CAS  Article  Google Scholar 

  2. 2

    M.Nagata, 6th US-Japan Workshop on High Field Superconductors Boulder, Colorado, (1989)

  3. 3

    M.Maeda, Y.Tanaka, M.Fukutomi and T.Asano, Jan.J.Appl. Phys., 21, L209 (1988)

    Article  Google Scholar 

  4. 4

    R.S.Feigelson, D.Gazit, D.K.Fork and T.H.Geball, SCIENCE, 240 1642 (1988)

  5. 5

    W.C.Cabrera, W.Gopel, G.F.de la Fuente and H.R.Verdun, Appl. Phys. Lett., 55.(10), 1032 (1989)

    Article  Google Scholar 

  6. 6

    U.Endo, S.Koyama and T.Kawai, Jpn. J. Appl. Phys. 27, L1476 (1988) ; 27, L1861 (1988)

    CAS  Article  Google Scholar 

  7. 7

    K.Hayashi, H.Nonoyama, N.Nagata, H .Hitotsuyanagi and M.Kawashima, 2nd International Symposium on Superconductivity Tsukuba, Japan, (1989) (to be published)

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to K. Hayashi.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Hayashi, K., Nonoyama, H., Ueyama, M. et al. Preparation of Bipbsrcacuo Superconductors by Laser Pedestal Growth Method. MRS Online Proceedings Library 169, 309–312 (1989). https://doi.org/10.1557/PROC-169-309

Download citation