Rf Surface Resistance Measurements in the Pb-Bi-Sr-Ca-Cu-O System

Abstract

Wires were fabricated from the high-Tc superconductor Bi0.7Pb0.3SrCaCu1.8Ox (Pb-BSCCO) by an extrusion process. The specimens were sintered for periods up to 14 days, and density was found to decrease with longer sintering times. Rf surface resistance data revealed that the onset of superconductivity occurred at 105 K and that the transition was very broad.

This is a preview of subscription content, access via your institution.

References

  1. 1

    J. R. Delayen and C. L. Bohn, Phys. Rev. B 40, 5151 (1989).

    Article  Google Scholar 

  2. 2

    D. H. Wu, W. L. Kennedy, C. Zahopoulos, and S. Sridar, Appl. Phys. Lett. 55, 696 (1989).

    CAS  Article  Google Scholar 

  3. 3

    C. L. Bohn, J. R. Delayen, U. Balachandran, and M. T. Lanagan, Appl. Phys. Lett. 55,304 (1989).

    CAS  Article  Google Scholar 

  4. 4

    K. C. Goretta, M. T. Lanagan, J. P. Singh, J. T. Dusek, U. Balachandran, S. E. Dorris, and R. B. Poeppel, Mater. & Manufact. Process. 4, 163 (1989).

    Article  Google Scholar 

  5. 5

    D. W. Johnson, Paper (17-SVI-89), presented at 91st Ceram. Soc. Meet., April 23-27, 1989, Indianapolis.

  6. 6

    S. X. Dou, H. K. Liu, A. J. Bourdillon, M. Kviz, N. X. Tan, and C. C. Sorrell, Phys. Rev. B. 40, 5266 (1989).

    Article  Google Scholar 

  7. 7

    D. Shi, M. S. Boley, J. G. Chen, M. Xu, K. Vandervoort, Y. X. Liao, A. Zangvil, J. Akujieze, and C. Segre, Appl. Phys. Lett. 55, 699 (1989).

    CAS  Article  Google Scholar 

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to M. T. Lanagan.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Lanagan, M.T., Bohn, C.L., Delayen, J.R. et al. Rf Surface Resistance Measurements in the Pb-Bi-Sr-Ca-Cu-O System. MRS Online Proceedings Library 169, 1133–1136 (1989). https://doi.org/10.1557/PROC-169-1133

Download citation