Low Pressure Growth of GaAs/AlGaAs Layers on 2N and 3N Substrates in a Multiwafer Reactor

Abstract

The epitaxial growth of GaAs/AIGaAs layers and multilayer structures has been investigated in different low pressure horizontal multiwafer reactors for high throughput capable to handle several 2“ and 3“ wafers in one run. The growth behavior in these reactors will be described with respect to gas flow dynamics. The background carrier concentration is in the 1014 cm−3range. The uptake of dopants (SiH4) is strongly reduced upon pressure reduction.

The uniformity of GaAs and AIGaAs layer thickness is better than ±3 % over 3“ diameter substrates. The uniformity of composition (measurer on HEMT structures) is better than ± 1 % across 98 % of the wafer areas (± 0.5 % across 75 %). Also the reproducibility is better than 1 %. Results on the uniformity of dopant distribution will also be presented.

HEMT structures grown at low pressure conditions show mobilities of 100,000 cm2/Vs at 77 K and over 210,000 cm2/Vs at 20 K (ns= 6×1011 cm−2, spacer thickness 9 nm). HEMT devices with transconductance of 330 mS/mm could be achieved.

This is a preview of subscription content, access via your institution.

References

  1. /1/

    P.J.A. Thijs, T.v. Dongen, P.l. Kuindersma, J.J.M. Binsma, I.F. Tiemeyer, J.M. Lagemaat, D. Moroni and W. Nijman “High quality InGaAsP – lnP for multiple quantum well laser diodes grown by low-pressure OMVPE”, J. of Crystal Growth 93 (1988) p. 863.

    CAS  Article  Google Scholar 

  2. /2/

    D. Grützmacher, K. Wolter, M. Zachau, H. Jürgensen, H. Kurz and P. Balk “GaInAs/InP multi quantum well structures for lasers by LP-MOVPE”, Inst. Phys. Conf. Ser. No. 91, Chapter 7, 1988.

  3. /3/

    M. Heuken, University Duisburg, FRG Unpublished results

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to M. Heyen.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Heyen, M., Heuken, M., Strauch, G. et al. Low Pressure Growth of GaAs/AlGaAs Layers on 2N and 3N Substrates in a Multiwafer Reactor. MRS Online Proceedings Library 145, 245–251 (1989). https://doi.org/10.1557/PROC-145-245

Download citation