Oxidation of Aluminum Nitride for Defect Characterization

Abstract

The thermal oxidation of aluminum nitride was developed as a means to study defects in bulk aluminum nitride crystals. The oxidation kinetics was established for the dry oxidation of highly textured AlN polycrystals produced by sublimation-recombination crystal growth in a tungsten furnace. Despite seeding on polycrystalline tungsten, the grains were predominantly [0001] oriented as verified by electron backscattering diffraction (EBSD). The oxidation rate is dependent on the crystal’s orientation, polarity, stress, and surface condition, thus oxidation decorates grain boundaries, polishing scratches, and inversion domains by producing oxide layers of different thicknesses. The initial oxidation rate of nitrogen polar (0001) AlN is approximately 25% faster than on aluminum polar crystals. Low temperature (800 °C) dry oxidation produced an amorphous oxide layer and generated a high density of defects (vacancies, stacking faults, and dislocations) in the nitride near the oxide/nitride interface, as observed by cross-sectional transmission electron microscopy. In contrast, high temperature oxidation (1000 °C) produced a crystalline oxide layer, and left the nitride free of observable defects.

This is a preview of subscription content, access via your institution.

References

  1. 1.

    J.C. Rojo, L.J. Schowalter, G. Slack, K. Morgan, J. Barani, S. Schujman, S. Biswas, B. Raghothamachar, M. Dudley, M. Shur, R. Gaska, N.M. Johnson, and M. Kneissl, Progress in the preparation of aluminum nitride substrates from bulk crystals, Mater. Res. Soc. Symp. Proc. 722 K1.1 (2002).

    Article  Google Scholar 

  2. 2.

    V.F. Mymrin, K.A. Bulashevich, N.I. Podolskaya, and S. Yu. Karpov, Bandgap engineering of electronic and optoelectronic devices on native AlN and GaN substrates: a modelling insight, J. Cryst. Growth 281 115 (2005).

    CAS  Article  Google Scholar 

  3. 3.

    R. Schlesser, R. Dalmau, D. Zhuang, R. Collazo, and Z. Sitar, Crucible materials for growth of aluminum nitride crystals, J. Cryst. Growth 281 75 (2005).

    CAS  Article  Google Scholar 

  4. 4.

    G.A. Slack, J. Whitlock, K. Morgan, and L.J. Schowalter, Properties of crucible materials for bulk growth of AlN, Mater. Res. Soc. Symp. Proc. 798 293 (2004).

    CAS  Google Scholar 

  5. 5.

    M. Bickermann, B.M. Epelbaum, and A. Winnacker, Characterization of bulk AlN with low oxygen content, J. Cryst. Growth 269 432 (2004).

    CAS  Article  Google Scholar 

  6. 6.

    B. Wu, R.H. Ma, H. Zhang, and V. Prasad, Modeling and simulation of AlN bulk sublimation growth systems, J. Cryst. Growth 266 303 (2004).

    CAS  Article  Google Scholar 

  7. 7.

    B. Raghothamachar, M. Dudley, J.C. Rojo, K. Morgan, and L.J. Schowalter, X-ray characterization of bulk AlN single crystals grown by the sublimation technique, J. Cryst. Growth 250 244 (2003).

    CAS  Article  Google Scholar 

  8. 8.

    D. Zhuang and J.H. Edgar, Wet etching of GaN, AlN, and SiC: a review, Mater, Sci. Eng. R. 48 1 (2005).

    Article  Google Scholar 

  9. 9.

    Z. Gu, J.H. Edgar, S.A. Speakman, D. Blom, J. Perrin, and J.Chaudhuri, Thermal oxidation of polycrystalline and single crystalline aluminum nitride wafers, J. Electron. Mater. 34 1271 (2005).

    CAS  Article  Google Scholar 

  10. 10.

    D. Zhuang, J.H. Edgar, L. Liu, B. Liu, and L. Walker, Wet chemical etching of AlN single crystals, MRS Internet J. Nitride Semicond. Res. 7 4 (2002) {rs http://nsr.mij.mrs.org/7/4/ url}.

    Article  Google Scholar 

  11. 11.

    P.R. Tavernier, T. Margalith, L.A. Coldren, S.P. DenBaars, and D.R. Clarke, Chemical mechanical polishing of gallium nitride, Electrochem. Solid State Lett. 5 G61 (2002).

    CAS  Article  Google Scholar 

  12. 12.

    J.L. Weyher, S. Muller, I. Grzegory, and S. Porowski, Chemical polishing of bulk and epitaxial GaN, J. Cryst. Growth 182 17 (1997).

    CAS  Article  Google Scholar 

  13. 13.

    J. Chaudhuri, L. Nyakiti, R.G. Lee, Z. Gu, J.H. Edgar, and J.G. Wen, Thermal oxidation of single crystalline aluminum nitride, submitted to Mater. Charact.

Download references

Acknowledgment

This work was support from grants from the National Science Foundation (DMR-0408874) and the Office of Naval Research (N00014-02-1-0290). The TEM work was carried out in the Center for Microanalysis of Materials, University of Illinois, which is partially supported by the U.S. Department of Energy under grant DEFG02-91-ER45439.

Author information

Affiliations

Authors

Corresponding author

Correspondence to J.H. Edgar.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Edgar, J., Gu, Z., Taggart, K. et al. Oxidation of Aluminum Nitride for Defect Characterization. MRS Online Proceedings Library 892, 2102 (2005). https://doi.org/10.1557/PROC-0892-FF21-02

Download citation