Abstract
The thermal oxidation of aluminum nitride was developed as a means to study defects in bulk aluminum nitride crystals. The oxidation kinetics was established for the dry oxidation of highly textured AlN polycrystals produced by sublimation-recombination crystal growth in a tungsten furnace. Despite seeding on polycrystalline tungsten, the grains were predominantly [0001] oriented as verified by electron backscattering diffraction (EBSD). The oxidation rate is dependent on the crystal’s orientation, polarity, stress, and surface condition, thus oxidation decorates grain boundaries, polishing scratches, and inversion domains by producing oxide layers of different thicknesses. The initial oxidation rate of nitrogen polar (0001) AlN is approximately 25% faster than on aluminum polar crystals. Low temperature (800 °C) dry oxidation produced an amorphous oxide layer and generated a high density of defects (vacancies, stacking faults, and dislocations) in the nitride near the oxide/nitride interface, as observed by cross-sectional transmission electron microscopy. In contrast, high temperature oxidation (1000 °C) produced a crystalline oxide layer, and left the nitride free of observable defects.
Similar content being viewed by others
References
J.C. Rojo, L.J. Schowalter, G. Slack, K. Morgan, J. Barani, S. Schujman, S. Biswas, B. Raghothamachar, M. Dudley, M. Shur, R. Gaska, N.M. Johnson, and M. Kneissl, Progress in the preparation of aluminum nitride substrates from bulk crystals, Mater. Res. Soc. Symp. Proc. 722 K1.1 (2002).
V.F. Mymrin, K.A. Bulashevich, N.I. Podolskaya, and S. Yu. Karpov, Bandgap engineering of electronic and optoelectronic devices on native AlN and GaN substrates: a modelling insight, J. Cryst. Growth 281 115 (2005).
R. Schlesser, R. Dalmau, D. Zhuang, R. Collazo, and Z. Sitar, Crucible materials for growth of aluminum nitride crystals, J. Cryst. Growth 281 75 (2005).
G.A. Slack, J. Whitlock, K. Morgan, and L.J. Schowalter, Properties of crucible materials for bulk growth of AlN, Mater. Res. Soc. Symp. Proc. 798 293 (2004).
M. Bickermann, B.M. Epelbaum, and A. Winnacker, Characterization of bulk AlN with low oxygen content, J. Cryst. Growth 269 432 (2004).
B. Wu, R.H. Ma, H. Zhang, and V. Prasad, Modeling and simulation of AlN bulk sublimation growth systems, J. Cryst. Growth 266 303 (2004).
B. Raghothamachar, M. Dudley, J.C. Rojo, K. Morgan, and L.J. Schowalter, X-ray characterization of bulk AlN single crystals grown by the sublimation technique, J. Cryst. Growth 250 244 (2003).
D. Zhuang and J.H. Edgar, Wet etching of GaN, AlN, and SiC: a review, Mater, Sci. Eng. R. 48 1 (2005).
Z. Gu, J.H. Edgar, S.A. Speakman, D. Blom, J. Perrin, and J.Chaudhuri, Thermal oxidation of polycrystalline and single crystalline aluminum nitride wafers, J. Electron. Mater. 34 1271 (2005).
D. Zhuang, J.H. Edgar, L. Liu, B. Liu, and L. Walker, Wet chemical etching of AlN single crystals, MRS Internet J. Nitride Semicond. Res. 7 4 (2002) {rs http://nsr.mij.mrs.org/7/4/ url}.
P.R. Tavernier, T. Margalith, L.A. Coldren, S.P. DenBaars, and D.R. Clarke, Chemical mechanical polishing of gallium nitride, Electrochem. Solid State Lett. 5 G61 (2002).
J.L. Weyher, S. Muller, I. Grzegory, and S. Porowski, Chemical polishing of bulk and epitaxial GaN, J. Cryst. Growth 182 17 (1997).
J. Chaudhuri, L. Nyakiti, R.G. Lee, Z. Gu, J.H. Edgar, and J.G. Wen, Thermal oxidation of single crystalline aluminum nitride, submitted to Mater. Charact.
Acknowledgment
This work was support from grants from the National Science Foundation (DMR-0408874) and the Office of Naval Research (N00014-02-1-0290). The TEM work was carried out in the Center for Microanalysis of Materials, University of Illinois, which is partially supported by the U.S. Department of Energy under grant DEFG02-91-ER45439.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Edgar, J., Gu, Z., Taggart, K. et al. Oxidation of Aluminum Nitride for Defect Characterization. MRS Online Proceedings Library 892, 2102 (2005). https://doi.org/10.1557/PROC-0892-FF21-02
Published:
DOI: https://doi.org/10.1557/PROC-0892-FF21-02