Effects of α-silicon nitride powder processing on surface oxidation kinetics

Abstract

The oxidation of two α–Si3N4 powders has been studied using x-ray photoelectron spectroscopy (XPS) and Bremsstrahlung-excited Auger electron spectroscopy (AES). These two powders had comparable specific surface areas but were produced by different methods. The powders were oxidized by heating in air at temperatures between 850° and 1000 °C. The oxide thickness for each heating time and temperature was determined both from the relative O 1s and N 1s peak intensities and from the relative SiO2 and Si3N4 Si KLL peak intensities. In each case, the oxide thickness calculated from the XPS data was systematically higher than those determined from the AES data. This difference may be due to uncertainties in the data analysis procedures. The oxidation of each powder followed a linear rate law for these temperatures. On one of the powders, the XPS data showed evidence of oxynitride formation. Analysis with thermal decomposition mass spectroscopy also showed that much more hydrogen was evolved from this particular powder, particularly at temperatures >700 °C. These differences in bulk impurity levels are believed to be responsible for the differences in the activation energies for oxidation which were measured to be 104 ± 22 kJ/mol and 62 ± 4 kJ/mol for these two powders.

This is a preview of subscription content, access via your institution.

References

  1. 1

    G. Wotting and G. Ziegler, Interceram. 2, 32–35 (1986) and 3, 57–60 (1986).

    Google Scholar 

  2. 2

    F. F. Lange, J. Am. Ceram. Soc. 67 (2), 83 (1984).

    CAS  Article  Google Scholar 

  3. 3

    G. Schwier, Progress in Nitrogen Ceramics, edited by F. L. Riley (Martinus Nijhoff Publishers, Boston, MA, 1983), pp. 157–166.

    Google Scholar 

  4. 4

    Anon., Advanced Ceramics Materials Technical Report, Ube Industries, 3.6000 (1987).

  5. 5

    P.S. Wang, S.M. Hsu, and T.N. Wittberg, J. Mater. Sci. 26, 1655 (1991).

    CAS  Article  Google Scholar 

  6. 6

    P. S. Wang, S. G. Malghan, S. M. Hsu, and T. N. Wittberg, Surf. Interf. Anal. 18, 159 (1992).

    CAS  Article  Google Scholar 

  7. 7

    P.S. Wang, S.M. Hsu, S.G. Malghan, and T.N. Wittberg, J. Mater. Sci. 26, 3249 (1991).

    CAS  Article  Google Scholar 

  8. 8

    J. M. Horton, J. Am. Ceram. Soc. 52, 121 (1969).

    CAS  Article  Google Scholar 

  9. 9

    W.C. Tripp and H.C. Graham, J. Am. Ceram. Soc. 59, 399 (1976).

    CAS  Article  Google Scholar 

  10. 10

    Certain commercial equipment, instruments, or materials are identified in this paper in order to specify adequately the experimental procedure. Such identification does not imply recommendation or endorsement by the National Institute of Standards and Technology, nor does it imply that the materials or equipment identified are necessarily the best available for the purpose.

  11. 11

    W. H. Press, B. P. Flannery, S. A. Teukolsky, and W. T. Vetterling, Numerical Recipes (Cambridge University Press, New York, 1987), pp. 400, 407–420, 523–528.

    Google Scholar 

  12. 12

    C.D. Wagner, in Practical Surface Analysis, edited by D. Briggs and M.P. Seah (John Wiley, New York, 1983), Appendix 4.

    Google Scholar 

  13. 13

    T.A. Carlson and G.E. McGuire, J. Electron Spectrosc. 1, 161 (1972).

    CAS  Article  Google Scholar 

  14. 14

    S. Tanuma, C. J. Powell, and D. R. Penn, Surf. Interf. Anal. 17, 927 (1991).

    CAS  Article  Google Scholar 

  15. 15

    C.J. Powell, J. Vac. Sci. Technol. A 3, 1338 (1985).

    CAS  Article  Google Scholar 

  16. 16

    S.R. Scholes, Modern Glass Practice, 7th ed. (CSI Publishing Co., Boston, MA, 1975), p. 387.

    Google Scholar 

  17. 17

    Handbook of Chemistry and Physics, edited by R. C. Weast, 60th ed. (Chemical Rubber, Boca Raton, FL, 1988), p. B-121.

  18. 18

    J. H. Scofield, J. Electron. Spectrosc. 8, 129 (1976).

    CAS  Article  Google Scholar 

  19. 19

    A.D. Katnani and K.I. Papathomas, J. Vac. Sci. Technol. A 5, 1335 (1987).

    CAS  Article  Google Scholar 

  20. 20

    H. J. Stein and H. A. R. Wegener, J. Electrochem. Soc. 124, 908 (1977).

    CAS  Article  Google Scholar 

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to Pu Sen Wang.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Wang, P.S., Malghan, S.G., Hsu, S.M. et al. Effects of α-silicon nitride powder processing on surface oxidation kinetics. Journal of Materials Research 8, 3168–3175 (1993). https://doi.org/10.1557/JMR.1993.3168

Download citation