Preparation of ultrafine tungsten carbide powder by CVD method from WCl6–C2H2–H2 mixtures

Abstract

The synthesis of ultrafine tungsten carbide powder from WCl6–C2H2-H2 mixtures was investigated. Under most experimental conditions, a mixture of α–WC and β–W2C was produced. The specific surface area and morphology of the product prepared under various reaction conditions were determined. The product particle size increased with temperature up to 1373 K and then decreased, went through a minimum with increasing WCl6 partial pressure, and decreased with increasing H2 flow rate. The specific surface area of the product showed the opposite trend in all cases.

This is a preview of subscription content, access via your institution.

References

  1. 1

    S.W.H. Yih and C.T. Wang, Tungsten (Plenum Press, New York, 1981), pp. 385–391.

  2. 2

    E. Lardner, Powder Metall. 21, 65–68 (1978).

    CAS  Article  Google Scholar 

  3. 3

    H.E. Exner and J. Gerland, Powder Metall. 13, 13–16 (1970).

    CAS  Article  Google Scholar 

  4. 4

    F. K. Poehring and T. R. Wright, J. Am. Ceram. Soc. 55, 58–62 (1972).

    Article  Google Scholar 

  5. 5

    S. S. Kim and H. S. Kim, J. Korean Inst, of Metallurgy & Materials 29, 651–658 (1991).

    Google Scholar 

  6. 6

    J. Hojo, T. Oku, and A. Kato, J. Less-Comm. Met. 59, 85–89 (1978).

    CAS  Article  Google Scholar 

  7. 7

    B. D. Cullity, Elements of X-ray Diffraction (Addison-Wesley, Reading, MA, 1978), pp. 254, 367, 411.

  8. 8

    R. F. Strickland-Constable, Kinetics and Mechanisms of Crystallization (Academic Press, New York, 1968), p. 44.

  9. 9

    A. Kato, Ceramics (Korea) 19, 478–482 (1984).

    CAS  Google Scholar 

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to Chang-Whan Won.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Won, CW., Chun, BS. & Sohn, H.Y. Preparation of ultrafine tungsten carbide powder by CVD method from WCl6–C2H2–H2 mixtures. Journal of Materials Research 8, 2702–2708 (1993). https://doi.org/10.1557/JMR.1993.2702

Download citation