Abstract
Solid-state amorphization is reported to occur in aluminum-platinum thin films. A uniform amorphous alloy layer was observed at the interface between aluminum and platinum layers for electron beam evaporated samples in an as-deposited state. For a pure aluminum overlayer deposited on top of a coevaporated Al–Pt amorphous alloy, the aluminum dissolves into the amorphous phase leading to a fully amorphous sample. In this last case the amorphization is nonuniform upon low-temperature anneals (T < ≃2 200 °C) and gives rise to hole formation in the aluminum overlayer. Direct observations of this phenomenon during in situ annealing of the thin films in a transmission electron microscope were carried out.
Similar content being viewed by others
References
S. P. Murarka, I. A. Blech, and H. J. Levinstein, J. Appl. Phys. 47, 5175 (1976).
E. G. Colgan, J. Appl. Phys. 62, 1224 (1987).
M. Nastasi, L. S. Hung, and J. W. Mayer, Appl. Phys. Lett. 43, 831 (1983).
X. A. Zhao, E. Ma, H. Y. Yang, and M. A. Nicolet, Thin Solid Films 153, 379(1987).
E. G. Colgan, C. Y. Li, and J. W. Mayer, J. Mater. Res. 2, 557 (1987).
E. G. Colgan, C. Y. Li, and J. W. Mayer, Appl. Phys. Lett. 51, 424 (1987).
G Cliff and G W. Lorimer, J. Microsc. 103m, 203 (1975).
P. Hirsch, A. Howie, D. W. Pashley, and M. J. Whelan, Electron Microscopy of Thin Crystals (Krieger, New York, 1977).
J. M. Legresy (unpublished results).
W. K. Chu, J. W. Mayer, and M. A. Nicolet, Backscattering Spectrometry (Academic, New York, 1978).
J. C. Barbour, K. Sickafus, and M. Nastasi, J. Vac. Sci. Technol. A 3, 1895 (1985).
L. R. Doolittle, Nucl. Instrum. Methods B 9, 344 (1985).
L. E. Davis, N. C. MacDonald, P. W. Palmberg, G. E. Riach, and R. E. Weber, in Handbook of Auger Electron Spectroscopy (Physical Electronics Industries, Eden Prairie, MN, 1976), 2nd ed., pp. 13–15.
P. Villars and L. D. Calvert, Pearson’s Handbook of Crystallographic Data for Intermetallic Phases (American Society for Metals, Metals Park, OH, 1985).
R. B. Schwartz and W. L. Jonhson, Phys. Rev. Lett. 51, 415(1983).
A. R. Miedema, P. F. de Châtel, and F. R. de Boer, Physica B 100, 1 (1980).
E. G. Colgan, Ph.D. thesis, Cornell University (1987).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Legresy, J.M., Blanpain, B. & Mayer, J.W. Solid-state amorphization in Al–Pt thin films. Journal of Materials Research 3, 884–889 (1988). https://doi.org/10.1557/JMR.1988.0884
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1988.0884