Abstract
In this article, we describe a solid-state photoelectrochemical cell for light detection. Safranine-T dye mixed with polyvinyl alcohol (PVA) solution was deposited on a conducting and transparent indium-tin-oxide (ITO)-coated glass that was used as one electrode and another ITO-coated glass as the counterelectrode. A solid polymeric electrolyte consisting of polyethylene oxide-ammonium perchlorate-ethylene carbonate and propylene carbonate with suitable weight ratio was prepared and sandwiched between these two ITO-coated glass electrodes, which were separated by a Teflon spacer about 50 µm thick. The cell was biased with a direct current source to make the dye and PVA-coated ITO as the anode and the other ITO as the cathode. On illumination by a tungsten lamp, from the cathode side, the change of photocurrent was measured. The dark current-voltage characteristics and the growth and decay of the photocurrent for steady and pulsed illumination were studied.
Similar content being viewed by others
References
Tang, C. W. (1987), Appl. Phys. Lett. 51, 913.
Tang, C. W. (1989), J. Appl. Phys. 65, 3610.
Pei, Q., Yu, G., Zhang, C., and Heeger, A. J. (1995), Science 269, 1086.
Pei, Q., Yang, Y., Yu, G., Zhang, C., and Heeger, A. J. (1996), J. Am. Chem. Soc. 118, 3922.
Cao, Y., Pei, Q., Andersson, M. R., Yu, G., and Heeger, A. J. (1997), J. Electrochem. Soc. 114, L317.
Li, Y., Gao, J., Wang, D., Yu, G., Cao, Y., and Heeger, A. J. (1998), Syn. Metals 97, 191.
Cao, Y., Yu, G., Heeger, A. J., and Yang, C. Y. (1996), Appl. Phys. Lett. 68, 3218.
Kumar, A. and Lewis, N. S. (1990), Appl. Phys. Lett. 57, 2730.
Antoniadis, H., Hsieh, B. R., Abkowitzz, M. A., Jenekhe, S. A., and Stolka, M. (1994), Synth. Met. 62, 265.
Schauer, F. (1999), J. Appl. Phys. 86, 524.
Nigrey, P. J., Maclnnes, D., Nairns, D. P., MacDiarmid, A. G., and Heeger, A. J. (1981), J. Electrochem. Soc. 128, 1651.
Shacklette, L. W., Maxfield, M., Gould, S., Wolf, J. F., Jow, T. R., and Baughmann, R. H. (1987), Synth. Met. 18, 1651.
Garnier, F., Tourillon, G., Gazard, M., and Dubois, J. C. (1983), J. Electro. Chem. 148, 299.
Pei, Q. and Inganas, O. (1992), Adv. Mater. 4, 277.
Hu, B., Yang, Z., and Karasz, F. E. (1994), J. Appl. Phys. 76, 2491.
Burrows, P. E. and Bulovic, V. (1994), Appl. Phys. Lett. 65, 2922.
Campbell, I. H., Smith, D. L., Neef, C. J., and Ferraris, J. P. (1998), Appl. Phys. Lett. 72, 2565.
Gao, J., Heeger, A. J., Campbell, I. H., and Smith, D. L. (1999), Phys. Rev. B 59, R2482.
Mark, P. and Helfrich, W. (1962), J. Appl. Phys. 33, 205.
Yang, J. and Shen, J. (1999), J. Appl. Phys. 85, 2699.
Burrows, P. E., Shen, Z., Bulovic, V., McCarty, D. M., Forest, S. R., Cronin, J. A., and Thompson, M. E. (1996), J. Appl. Phys. 79, 7991.
Smith, D. L. (1997), J. Appl. Phys. 81, 2869.
Dey, S. K., Manik, N. B., Bhattacharya, S., and Basu, A. N., Synth. Met., submitted.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Dey, S.K., Manik, N.B. Study on photoconductivity of dye-polymer-based solid-state thin film. Appl Biochem Biotechnol 96, 55–62 (2001). https://doi.org/10.1385/ABAB:96:1-3:055
Issue Date:
DOI: https://doi.org/10.1385/ABAB:96:1-3:055