Fatigue of air supply manifold support rod in military jet engines

  • R. J. H. Wanhill
Peer Reviewed Articles

Abstract

Bending fatigue failure occurred in a support rod linking the bleed air supply manifold to the diffuser case in a military jet engine. Other rods were subsequently found cracked. The rods were wrought Inconel 718, operating at approximately 550 °C. The bending was caused by relative movements of two expansion sleeves held together by the rods. Accommodative swiveling of the spherically rounded ends of the rods in the mating seatings of the inner sleeves was prevented by contact pressure, fretting, and binding. The main reason for binding was decomposition of the antigalling compound applied to the contact surfaces. Fractographic analysis and oxidation interference colors enabled interpretation of the cracking history of the broken rod. Elementary stress and fracture mechanics calculations indicated that the maximum fatigue stress was below the stress needed to “unlock” the spherically rounded rod end from its seating.

Keywords

diffuser air supply fatigue Inconel 718 rods jet engine 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    P. Heuler and J.W. Bergmann: “IEPG TA 31, A Research Programme into Lifing Concepts for Military Aero-Engine Components,” Final Report B-TA-3602, Industrieanlagen-Betriebsgesellschaft mbH (IABG), Ottobrunn, Germany, August 1997.Google Scholar
  2. 2.
    J.C. Runkle and R.M. Pelloux: “Micromechanisms of Low-Cycle Fatigue in Nickel-Based Superalloys at Elevated Temperatures,” Fatigue Mechanisms, ASTM Special Technical Publication 675, J.T. Fong, ed., ASTM, W. Conshohocken, PA, 1979, pp. 501–24.Google Scholar
  3. 3.
    U.R. Evans: The Corrosion and Oxidation of Metals, Second Supplementary Volume, Edward Arnold, London, 1976, p. 379.Google Scholar
  4. 4.
    T.C. Radtke: Personal Communication from the Aeronautical and Maritime Research Laboratory (AMRL), Melbourne, Australia, 23 March 1993.Google Scholar
  5. 5.
    U.R. Evans: The Corrosion and Oxidation of Metals: Scientific Principles and Practical Applications, Edward Arnold, London, 1971, pp. 27–28.Google Scholar
  6. 6.
    E. Andrieu, H. Ghonem, and A. Pineau: “Two-Stage Crack Tip Oxidation Mechanism in Alloy 718,” Elevated Temperature Crack Growth, MD-vol. 18, S. Mall and T. Nicholas, ed., The American Society of Mechanical Engineers, New York, NY, 1990, pp. 25–29.Google Scholar
  7. 7.
    R.J.H. Wanhill, J.A.M. Boogers, H.N. Huisman, and H.H. Ottens: “Failure and Cracking of Inconel 718 Air Supply Manifold Support Rods,” NLR TP 96047 L, National Aerospace Laboratory NLR, Amsterdam, The Netherlands, January 1996.Google Scholar
  8. 8.
    Department of the Navy, NAVAIR Technical Order 02-1-517/T.O. 2-1-111/DMWR 55-2800-206, February 1990, p. 21–22.Google Scholar
  9. 9.
    H.E. Sliney: “Solid Lubricants,” Friction, Lubrication, and Wear Technology, vol. 18, ASM Handbook, P.J. Blau, ed., ASM International, Materials Park, OH, 1992, pp. 114–15.Google Scholar
  10. 10.
    R.J.H. Wanhill and C.E.W. Looije: “Fractographic and Microstructural Analysis of Fatigue Crack Growth in Ti6Al-4V Fan Disc Forgings,” AGARD Report 766 (Addendum), Advisory Group for Aerospace Research and Development, Neuilly-sur-Seine, France, April 1993, pp. 2.1–2.40.Google Scholar
  11. 11.
    J.C. Newman, Jr.: “A Crack-Closure Model for Predicting Fatigue Crack Growth Under Aircraft Spectrum Loading,” Methods and Models for Predicting Fatigue Crack Growth Under Random Loading, J.B. Chang and C.M. Hudson, ed., ASTM STP 748, ASTM, W. Conshohocken, PA, 1981, pp. 53–84.Google Scholar
  12. 12.
    Fatigue Crack Growth Computer Program NASA/FLAGRO Version 2.0, Annex 2 in ESACRACK User’s Manual, ESA PSS-03-209 Issue 2, European Space Agency, Paris, 1995.Google Scholar
  13. 13.
    R.E. Peterson: Stress Concentration Design Factors, John Wiley & Sons, Inc., New York, 1953, p. 74.Google Scholar

Copyright information

© ASM International 2004

Authors and Affiliations

  • R. J. H. Wanhill
    • 1
  1. 1.National Aerospace Laboratory NLRAmsterdamThe Netherlands

Personalised recommendations