Abstract
Alumina ceramics were brazed to Inconel 600 and UMCo-50 superalloys at 900 °C for 10 min using an Sn10Ag4Ti active filler metal. The brazing filler showed good wettability on alumina and superalloys. The flexural strengths were 69 and 57 MPa for alumina/Inconel 600 and alumina/UMCo-50 joints, respectively. In both cases, the brazed specimens fractured along the Sn10Ag4Ti/superalloy interfaces after four-point bending tests. Electron probe microanalysis (EPMA) elemental mapping revealed that the Ni of Inconel 600 and the Co of UMCo-50 dissolved into Sn10Ag4Ti filler metal, which serves to reinforce the weak Sn10Ag4Ti matrix.
Similar content being viewed by others
References
H.W. Wu and T.H. Chuang: “Joining Alumina to Superalloys With Ag-Cu-Ti Active Filler Metals” in Proc. 4th Int. Conf. Joining Ceramics, Glass and Metal, Konigswinter, Germany, May 17–19, 1993, pp. 92–98.
O.M. Akselsen: “Advances in Brazing of Ceramics,” J. Mater. Sci., 1992, 27, pp. 1989–2000.
P. Duhaj, P. Sebo, P. Svec, and D. Janickovic: “Development and Characterisation of Ag-Cu-Ti Brazes Prepared With Planar Flow Casting,” Mater. Sci. Eng. A, 1999, 271, pp. 181–87.
A.H. ElSawy and M.F. Fahmy: “Brazing of Si3N4 Ceramic to Copper,” J. Mater. Proc. Technol., 1998, 77, pp. 266–72.
W.B. Hanson, K.I. Ironside, and J.A. Ferine: “Active Metal Brazing of Zirconia,” Acta Mater., 2000, 48, pp. 4673–76.
T. Yano, H. Suematsu, and T. Iseki: “High-Resolution Electron Microscop of a SiC/SiC Joint Brazed by a Ag-Cu-Ti Alloy,” J. Mater. Sci., 1988, 23, pp. 3362–66.
J.K. Boadi, T. Yano, and T. Iseki: “Brazing of Pressureless-Sintered SiC Using Ag-Cu-Ti Alloy,” J. Mater. Sci., 1987, 22, pp. 2431–34.
W. Weise, W. Malikowski, and W. Bohm: “Verbinden von Keramik mit Keramik oder Metall durch Aktivlöten unter Argon oder Vakuum,” Firmenschrift Degussa Hanau AG, Hanau, Germany (in German).
Y.H. Chai, W.P. Weng, and T.H. Chuang: “Relationship Between Wettability and Interfacial Reaction for Sn10Ag4Ti on Al2O3 and SiC Substrates,” Ceram. Int., 1998, 24, pp. 273–79.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Chang, S.Y., Hung, Y.T. & Chuang, T.H. Joining alumina to inconel 600 and UMCo-50 superalloys using an Sn10Ag4Ti active filler metal. J. of Materi Eng and Perform 12, 123–127 (2003). https://doi.org/10.1361/105994903770343240
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1361/105994903770343240