Physico-chemical oxidative cleavage strategy facilitates the degradation of recalcitrant crystalline cellulose by cellulases hydrolysis
- 533 Downloads
Efficient enzymatic conversion of recalcitrant crystalline cellulose is critical for enabling cost-effective industrial conversion of cellulosic biomass to biofuels and chemicals. Fully understanding enzyme digestion mechanism is paving a new way to design efficient process for biomass conversion. Accordingly, a continuing drive is inspiring to discover new routes to promote crystalline cellulose disruption.
Herein, a physico-chemical oxidative cleavage strategy of irradiation oxidation/post-reduction (IOPR) was employed to treat crystalline cellulose I to cleave glycosidic bonds association with some new oxidized and reduced chain ends, thus boosting downstream degradation by cellulases from Trichoderma reesei. The hydrolysis performance of treated crystalline cellulose was conducted with either T. reesei Cel7A (TrCel7A) alone, or a cellulase enzyme mixture (90% Celluclast 1.5 L, 10% β-glucosidase). 81.6 and/or 97% of conversion efficiency have been reached for 24-h and 48-h cellulase hydrolysis, respectively. The high efficient conversion of crystalline cellulose after IOPR is mainly attributed to generating some new chain ends, which are identified by MAIDI-TOF–MS and HPLC. Furthermore, the nanoscale architectures of crystalline cellulose before and after IOPR are systematically investigated by XRD, EPR, ATR- FTIR, GPC, and XPS techniques. Together with TEM images, the results reveal a fascinating digestion mechanism of “peel-off” and “cavity-formation” paradigms toward degrading crystalline cellulose by cellulase mixtures after IOPR treatment.
This encouraging results show that the proposed IOPR approach will become a potential competitive alternative to current biomass pretreatment. It opens a new avenue toward the implementation of pretreatment and the design of enzyme cocktails in lignocellulosic biorefinery.
KeywordsCrystalline cellulose Irradiation oxidation Post-reduction Enzymatic hydrolysis Degradation mechanism
attenuated total reflectance Fourier transform infrared spectroscopy
electron paramagnetic resonance
gel permeation chromatography
high-performance liquid chromatograph
lytic polysaccharide monooxygenases
matrix-assisted laser desorption/ionization-time of flight–mass spectrometry
reactive oxygen species
transmission electron microscopy
X-ray photoelectron spectroscopy
Cellulose, the most abundant polysaccharides with a linear chain polymer of β-1,4-linked d-glucose units in nature, is playing a pivotal role in the enzyme-based “biorefinery” from lignocellulose . As an ideal alternative of petroleum-based source, cellulose can be hydrolyzed into monomeric sugars for downstream conversion to a wide range of fuels, chemicals, and materials; thus it will eliminate the associated economic, environmental, and energy security issues of fossil-based fuels production . However, the remarkable recalcitrance of crystalline cellulose has hitherto held one limiting step in this enzyme-based “biorefinery” process .
Numerous approaches have been developed to accelerate enzymatic hydrolysis of crystalline cellulose into glucose, including dilute acid/alkali, ammonia fiber expansion (AFEX), ionic liquids, organosolv methods [4, 5, 6, 7]. These above techniques have demonstrated two major effects, one is to increase the enzymes accessibility to binding cellulose surface; the other is to decrease the free energy of enzymes for processive decrystallization through reducing cellulose crystallinity [8, 9]. However, complexities associated with both the cost-effective industrialization and large amount of chemicals consumption are still the major challenges for practical utilization of these approaches.
In nature, biomass-degrading microorganisms have evolved a series of enzymes to help digest crystalline cellulose. For example, the well-characterized brown rot fungi have a more efficient cellulolytic system depending on an oxidative–hydrolytic two-step mechanism , it was found that lignocellulose was firstly oxidized by reactive oxygen species (ROS) from enzymes prior to hydrolysis by glycoside hydrolases . Recently, lytic polysaccharide monooxygenases (LPMOs) have shown the synergistical interaction with hydrolytic cellulases to break down crystalline cellulose by an oxidative cleavage mechanism [12, 13, 14]. It was demonstrated that LPMOs not only introduce oxidized chain breaks in the polysaccharide chains, but also decrease the free energy for decrystallization [15, 16]. These unexpected findings provide new perspectives to design more efficient biorefinery process in future.
In our previous works, γ-ray irradiation pretreatment could facilitate enzymatic hydrolysis of crystalline cellulose without significant changing cellulose allomorph and crystallinity [17, 18]. Similar phenomena were described by many researchers, who demonstrated that irradiation pretreatment (e.g., γ-ray, plasma, electron beam, microwave) would become a universal approach to accelerate biomass degradation [19, 20, 21]. The mechanism was revealed that irradiation caused oxidative cleavage of glucan chain involved ROS. It is deduced that a synergistic effect may be existed between irradiation oxidative cleavage and enzyme hydrolysis for crystalline cellulose degradation. However, the oxidized microstructure of irradiated cellulose is unclear due to the low selectivity and complexity of physical oxidation. To the best of our knowledge, the synergistic effect on cellulose degradation between non-enzyme oxidative cleavage and hydrolytic cellulases has not been available so far.
To meet this challenge, first of all, it briefly describes the that high hydrolysis efficiency of crystalline cellulose is obtained after it is treated by IOPR process. To test the feasibility of IOPR in real biorefinery, several types of cellulose substrates, including “model” cellulose (e.g., Avicel PH-101) and real biomass cellulose (e.g., Eucalyptus hardwood and pine softwood), are investigated in this work. Then, using XRD, EPR, FTIR, XPS, GPC, MALDI-TOF, and HPLC techniques, it is comprehensively elucidated the fact that crystalline celluloses treated with IOPR show remarkable high degradation efficiency by cellulases, changes in nanoscale structural features of crystalline cellulose are systematically verified, including cellulose crystallinity index (CCI), accessibility, surface area, degree of polymerization (DP), number of reducing ends, functional group features during degradation, and oligosaccharide products. Furthermore, through TEM images, a digestion mechanism of crystalline cellulose by free hydrolytic cellulases is illustrated through IOPR process. Finally, the potential feasibility of IOPR process in an industrial setting is preliminarily discussed.
Avicel microcrystalline cellulose (PH-101, cellulose I), cellobiose (≥ 98%), ethylenediamine (≥ 99%), sodium azide, direct orange 15, direct blue 1, TrCel7A (0.13 U/mg powder, expressed in corn plant from Hypocrea jecorina), and Celluclast 1.5 L (145 FPU/mL, 369.4 mg protein/mL, Novozyme Corp.) were all purchased from Sigma Aldrich (St. Louis, MO, USA). TrCel7A and Celluclast 1.5 L were directly used from company without any purification. Additional file 1: Figure S1 shows the SDS-Page analyses of these enzymes. β-glucosidase (20.5 CBU/mg powder, 6.8 mg protein/g powder) was purchased from Jiangsu Ruiyang Biotechnology Co. Ltd. (Wuxi City, Jiangsu, China). Prior to experiments, the protein content in enzymes were verified by Bradford assay and BSA was used as standard.
Methanol and acetonitrile (HPLC grade) were purchased from Fisher Chemical Co. (Beijing, China). Ethanol, sodium hydroxide, glacial acetic acid, phosphoric acid, and sulfuric acid were of analytic grade and purchased from Beijing Chemical Factory (Beijing, China). Other reagents were purchased from local chemical company, Beijing, China.
Cellulose substrates preparation
Cellulose substrate IC-I
Avicel PH-101 (~ 15 g) in a 20-mL glass tube was exposed to a gamma resource (60Co) with the level of 600 kGy at room temperature according to the procedures detailed in our previous work . The irradiated Avicel (5 g) was suspended with 50 mL deionized water and stirred at room temperature for 1 h, and the mixture was filtered with 0.45-μm membrane. Then, the solid residue was washed with 50 mL deionized water for 3 times and lyophilized to obtain the irradiated cellulose I (defined as IC-I). The soluble fraction in the liquor was lyophilized and subjected to MALDI-TOF–MS and HPLC for sugars analyses. The untreated Avicel PH-101 substrate was defined as C-I in this work.
Cellulose substrate IpRC-I
The irradiated Avicel PH-101 without washing was used for post-reduction treatment with sodium borohydride (NaBH4) in alkali solution to prepare the substrate IpRC-I. The detailed procedures of post-reduction treatment were modified according to the method reported by Beeson et al. . In brief, 0.6-g irradiated Avicel was mixed with 5 mL fresh preparation of 20 mg/mL NaBH4 in 1.0 M ammonium hydroxide. The reaction was preceded at room temperature for 2 h with occasional stirring. Then, 1 mL of glacial acetic acid was added to remove excessive NaBH4. 10 mL of methanol:acetic acid (9:1, vol.%) mixtures was added to neutralize the alkali and it stopped the reduction reaction. Finally, the mixture was centrifuged at 8000 rpm for 5 min; the solid residue was washed with 50 mL methanol in triplicate up to pH neutral, and air-dried over 12 h to achieve cellulose powder, which was defined as cellulose substrate IpRC-I. The methanol in the supernatant was removed with N2 at 40 °C, and then lyophilized for sugars analyses by HPLC.
Cellulose substrate C-II
Avicel PH-101 (10 g) was dipped into 100 mL 25% NaOH (w/v) solution at 4 °C for 1 h. The slurry was then centrifuged at 5000 rpm for 30 min, and washed with 150 mL of cool deionized water for 6 times up to neutral pH . The washed solid residue was lyophilized and defined as cellulose substrate C-II for subsequent experiments.
Cellulose substrate C-III
Avicel PH-101 (5 g) was soaked in 100 mL of ethylenediamine at room temperature for 24 h. The slurry was then centrifuged at 5000 rpm for 30 min, and washed with anhydrous methanol (6 × 150 mL) until neutral pH . The washed solid residue was air-dried and defined as cellulose substrate C-III for subsequent experiments.
Cellulose substrates C-E and C-P
Two crystalline cellulosic substrates from real biomass, Eucalyptus hardwood and pine softwood, were prepared and defined as C-E (85% glucan content) and C-P (78% glucan content), respectively. The detail procedures of cellulose substrates C-E and C-P preparation were described in our previous work . In brief, the irradiated wood biomass (88 g, 800 kGy) was added into 350 mL of aqueous γ-valerolactone solution (40:60 GVL/H2O, vol%); the mixture was heated to 170 °C and kept for 1 h. After cooling, the slurry was filtered to obtain the solid residue, which was successively washed with aqueous γ-valerolactone (3 × 300 mL) and deionized water (3 × 500 mL). The crystalline allomorph of cellulose substrates C-E and C-P was confirmed by XRD, and the glucan contents of C-E and C-P were analyzed by HPLC.
Enzymatic hydrolysis of cellulose substrates
Enzymatic hydrolysis of cellulose substrates by sole TrCel7A was performed with 0.5% (w/v) glucan in 50 mM acetate buffer (pH 5.0, 25 mg/L of sodium azide) at enzyme loading of 12 mg protein/g glucan. The enzyme hydrolysis time was fixed at 0.5, 1, 2, 3, 5, 7, and 9 h. The hydrolysis of cellulose by free hydrolytic cellulases (90% Celluclast 1.5 L and 10% β-glucosidase) was carried out at 1% (w/v) glucan loading with different enzyme loadings (2, 5, 10, 20, and 50 mg protein/g glucan) for 6, 12, 24, 36, and 48 h. The content of cellulose substrate loading for enzymatic hydrolysis was monitored on the basis of the glucan content in substrate. Other enzyme hydrolysis conditions were as follows: reaction volume 1 mL, temperature 50 °C, and agitation 60 rpm in an end-over-end rotary incubator. The enzyme hydrolysis reaction was immediately stopped by putting reactor in the boiling water bath for 5 min. The hydrolysates were subjected to HPLC analysis. All experiments were repeated in triplicate and the final experimental data were expressed as mean ± StDev in this work.
Enzyme adsorption assays of cellulose substrates
Accessibility of cellulose substrates by Simons’ stain
The accessibility of cellulases to cellulose substrates (C-I, IC-I, IpRC-I) was evaluated by Simons’ stain . Since the molecular size of orange dye’s (5–36 nm) is almost the same as that of typical cellulase, the adsorption of orange dye during Simons’ stain is normally used to determine the accessible surface area of cellulose substrate .
Electron paramagnetic resonance (EPR) monitoring activation oxygen radicals
EPR experiments were performed on a JES FA-200cw-EPR spectrometer (JEOL, Japan) at room temperature to monitor the free radicals generating from irradiation oxidation towards cellulose. The detailed procedures were described by Liu et al. . The EPR conditions were as follows: microwave frequency (x-band) 9.06 GHz, microwave power 10 mW, center field 324 mT, sweep width 50 mT, modulation amplitude 0.35 mT, modulation frequency 100 kHz, sweep time 60 s, and temperature 37 °C. The EPR spectra were normalized based on the mass of the sample.
Attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR)
The variances of functional groups towards cellulose substrates C-I, IC-I, and IpRC-I were analyzed by FT-IR (TENSOR 27, Bruker, USA) equipped with a temperature-controlled attenuated total reflectance (ATR) device with a ZnSe crystal (Pike Technology) . The spectra were recorded from 600 to 4000/cm at a resolution of 2/cm.
X-ray diffraction (XRD)
The crystallinity of cellulose substrates was performed on a D8 ADVANCE XRD (Bruker, Germany) using Cu Kα radiation at a voltage of 40 kV and a current of 40 mA. Scans were obtained from 2è = 5 to 45, 30 min per sample. The cellulose crystallinity index (CCl) was commonly estimated using two methods: XRD peak height and XRD peak deconvolution [24, 30].
Peak deconvolutions were performed using PeakFit (Version 4.12, Systat Software Inc, San Jose, CA). XRD experimental data were fitted using Gaussian–Lorentzian analysis to sure F value > 30,000 and R2 > 0.998. For crystalline cellulose I, five crystalline peaks (at 2θ = 14.8°, 16.5°, 20.5°, 22.5°, and 34.5°) and one amorphous peak (2θ = 21.5°) were deconvoluted and fitted to obtain the XRD original spectra.
Gel permeation chromatography (GPC)
Cellulose substrates C-I, IC-I, and IpRC-I were derivatized with anhydrous pyridine and phenyl isocyanate prior to GPC analyses for the molecular weight distribution . A weighted cellulose substrate was dissolved in tetrahydrofuran (abbrev. THF) with the final concentration of 5 g/L. GPC analyses were performed on 1515GPC instrument (Waters, USA) equipped with refractive index (abbrev. RI) detector. The conditions were as follows: THF was used as eluent at the rate of 1.0 mL/min; injection volume was 50.0 ìL. Column temperature was 35 °C. The detected molecular weight ranges were from 500 to 4 × 106 Da. The average molecular weight was calculated by the universal polystyrene calibration curve . Degree of polymerization (DP) was calculated using these molecular weights divided by 519, the molecular weight of cellulose tricarbanilate monomer .
Transmission electron microscopy (TEM)
To elucidate the effect of IPOR process on the enzyme hydrolysis mechanism, the morphologies of cellulose substrates C-I, IC-I, and IpRC-I after enzymatic digestion were imaged by 120 kV TEM (HT7700, Hitachi, Japan) with a 4 mega-pixel Gatan UltraScan 1000 camera (Gatan, Pleasanton, CA). For TEM images, the samples were dropwise cast directly on carbon-coated copper grids, and negatively stained with 2 wt% aqueous phosphotungstic acid (pH 6.2) .
X-ray photoelectron spectroscopy (XPS)
Elemental distribution and chemical state on the surface (5–10 nm) of cellulose substrates C-I, IC-I, and IpRC-I were analyzed by ESCALAB 250 XPS (Thermo Fisher Scientific, USA). The data were acquired using twin anode Al Kalph (300 W), a pass energy of 100 eV for survey; 30 eV for high-resolution scans. The analyzed area was 500 ìm × 500 ìm. The carbon element signals were deconvoluted (within 0.2 eV) into C1 (284.8 eV), C2 (286.5 eV), C3 (287.9 eV), and C4 (288.8 eV) signals using XPS PEAK (Version 4.1) .
Matrix-assisted laser desorption/ionization-time of flight–mass spectrometry (MALDI-TOF–MS)
MALDI-TOF–MS was performed to detect the oligosaccharides concentration on an ABI 4700 Voyager DE PRO (USA), using 2,5-dihydroxybenzoic acid (DHB) as matrix. 8 μL of DHB solution (10 mg/mL) was mixed with 2 μL of oligosaccharides solution (10 mg/mL). 0.5 μL of mixture solution was deposed on a MTP 384 target plate ground. The spotted samples were then dried in a vacuum desiccator. The spectra were obtained using the reflection mode with an acceleration voltage of 25 kV, a reflector voltage of 26, and pulsed ion extraction of 40 ns in the positive ion mode. The acquisition range was from m/z 500 to 4000 .
Trifluoroacetic acid hydrolysis for oligosaccharides determination
To quantification of soluble oligosaccharides derived from IOPR, the samples were completely hydrolyzed by trifluoroacetic acid (TFA) prior to HPLC analysis . Specifically, the lyophilized oligosaccharides (10 mg) were dissolved in 2 mL aqueous TFA (2.0 M) and hydrolyzed in a preheated oil bath at 121 °C for 1 h. After reaction, the samples were immediately cooled with ice water, and centrifuged at 8000×g for 5 min. The supernatant was dried under a stream of nitrogen at 40 °C. The dried sample was duplicate washed with 5 mL isopropanol and centrifuged at 10,000×g for 5 min, then the precipitate was dried under a stream of nitrogen. The final samples were dissolved in water for monomeric sugars detection by HPLC.
High-performance liquid chromatograph (HPLC)
The quantification of cellobiose and glucose was performed on a Series 1500 HPLC (Alltech,USA) with a prevail carbohydrate ES 5 μ column (GRACE) and an evaporative light-scattering detector (ELSD). The mixture solution of acetonitrile:H2O = 75:25 (v/v) was used as the mobile phase at the flow rate of 1 mL/min. The column temperature was 30 °C.
The xylose, glucose, and sorbitol were also analyzed by HPLC with refractive index detector (RI, Schambeck SFD GmbH,Germany). The separation was performed in an Aminex HPX-87H column (BIO-RAD) at 60 °C. The mobile phase was 5 mM H2SO4 at a flow rate of 0.6 mL/min . All samples were filtered with 0.22-μm membrane prior to HPLC analysis.
Results and discussions
Irradiation and IOPR process boost the enzymatic degradation of recalcitrant crystalline cellulose
In comparison of the control (C-I), cellulose substrates IC-I and IpRC-I are easily more prone to degradation by cellulases, which are dramatically releasing higher concentration of cellobiose (Fig. 1a) and ratio of cellobiose/glucose (Fig. 1b). The ratio of cellobiose/glucose for IC-I and IpRC-I increases with the rate of cellulobiose during the hydrolysis. It indicates that IC-I and IpRC-I are more prone to degradation by CBH I to release cellobiose. In other words, cellobiohydrolase shows the higher hydrolytic velocity on IC-I and IpRC-I .
Furthermore, the apparent turnover frequency (TOF) of free hydrolytic cellulases (Celluclast 1.5 L and β-glucosidase) was also investigated in our work. An interesting observation in Fig. 1c shows that TOF for IC-I hydrolysis is higher than these for IpRC-I and C-I at low enzyme loadings (2–5 mg protein/g glucan). It is perhaps the hypothesis that irradiation oxidative cleavage of glycosidic bonds in crystalline cellulose opens up the inaccessible oligosaccharides for cellulases . It is easily deduced that high glucose concentration from the irradiated biomass and/or “model” cellulose can be probably obtained at relatively low enzyme dosage. This phenomenon was confirmed in our previous work, wherein 76% of cellulose conversion to glucose was achieved for high crystalline cellulose derived from irradiated lignocellulose at relatively low enzyme loadings of ~ 7 mg protein/g cellulose for 52-h hydrolysis .
Alternatively, we analyzed the effects of cellulase loadings ranging from 2 to 50 mg protein/g cellulose on glucose release of C-I, IC-I, and IpRC-I biodegradation (Fig. 1d). The effect of enzyme loadings on the initial rate of glucose release from C-I, IC-I, and IpRC-I was evaluated during enzymatic hydrolysis, and the results are depicted in Additional file 1: Figure S2. As expected, the observed results of Fig. 1d reveal that the highest glucose yields released from IpRC-I cellulose are achieved, following with IC-I. However, C-I releases the lowest glucose yields under the same conditions. Here is a specific example, a total enzyme loading of 20 mg per g cellulose is used to ensure that about 97% of IpRC-I and 86% of IC-I substrates can be converted into glucose for 48-h and 72-h cellulase hydrolysis, respectively, while only 43% of C-I is converted into glucose.
In addition, the kinetics curves of cellulase hydrolysis on different cellulose substrates were investigated, including crystalline cellulose II, III, cellulose derived from hardwood Eucalyptus treated with irradiation (defined as C-E), and softwood pine treated with irradiation (defined as C-P) under the same conditions. As shown in Fig. 1e, irradiation and/or IOPR treatments are able to enhance enzyme hydrolysis efficiency regardless of real lignocellulose biomass and/or “model” cellulose. It was reported that cellulose III was hydrolyzed by fungal cellulases from T. reesei at rates up to 5-fold higher than native cellulose I . It is the common conception that crystalline cellulose I was considered as much harder recalcitrance to enzymatic hydrolysis than other allomorph forms (II, III, and PASC) due to highly ordered glucan chains and each chain stabilized by intra-/inter-molecular hydrogen bonds in the crystal . Excitedly, all tested cellulose substrates after IOPR treatment in our work are completely digested for 48-h enzyme hydrolysis. It has been demonstrated that IOPR process facilitates enzymatic degradation of recalcitrant crystalline cellulose, which is a potential competitive alternative to current biomass pretreatment for the real biorefinery [17, 18, 22].
Structural characteristics of crystalline cellulose treated by irradiation and IOPR process
The observed data in Fig. 2b show that IOPR treatment does not alter its allomorph form of crystalline cellulose I. However, after stepwise irradiation oxidation and NaBH4 reduction treatment, crystalline cellulose I results in a 4.98 and 6.0% decrease of CCl, respectively (Fig. 2b). It was pointed out that irradiation and IOPR had slight influence on allomorph and crystallinity of cellulose . This phenomenon is confirmed by X-ray diffraction (XRD) analyses (Additional file 1: Figure S3) and is good consistent with these reported in the literatures [21, 36]. The characteristic peaks of XRD patterns for C-I, IC-I, and IpRC-I were observed at 14.8°, 16.5°, 20.5°, 22.5°, and 34.5°, which are corresponding to crystalline peak 101, 10ī, 021, 002, and 040 of cellulose allomorph I, respectively (Additional file 1: Figure S3).
The enzyme accessibility of cellulosic substrates, C-I, IC-I, and IpRC-I, was evaluated by Simon’s stain method . The observed data in Fig. 2c show that IC-I and IpRC-I achieve a 26.7 and 29.6% of enhancement in accessibility, respectively, in comparison with C-I. It may be attributed to the fact that irradiation induces partial degradation of cellulose to soluble oligosaccharides (Additional file 1: Figure S4) according to HPLC analyses. It is speculated that irradiation can cleave the backbone-chain structure of crystalline cellulose, which was confirmed by GPC analyses. The observed data in Fig. 2d show that irradiation causes dramatic decrease in the cellulose DPw from 343 to 35 ~ 42. It suggests that IC-I and IpRC-I have 9.5- and 8-fold times of total number of chain ends over C-I substrate (Additional file 1: Figure S5). The reasonable explanation may be the fact that irradiation generates activation oxygen radicals resulting in 1,4-glucan chain cleavage of cellulose . The derived radical oxygen species (ROS) was further confirmed from EPR analyses (Additional file 1: Figure S6).
Adsorption ability of TrCel7A and Celluclast 1.5 L for three cellulosic substrates
Adsorption parameters for TrCel 7A
Bmax for Celluclast 1.5 L (mg/g)
To further explain “substrate-affinity” factors, XPS and FT-IR experiments were conducted. The data in Additional file 1: Figures S7 and S8 show that weak acid groups (e.g., aldehydes, ketones, lactones) of cellulose are formed after irradiation treatment. After post-reduction, these acid groups are reduced by sodium borohydride and transferred into hydrogen group. These new reduced end existing in cellulose structure may be easily accessible to cellulases. Recently, a similar phenomenon was reported by Hu et al.  that the addition of LPMO (AA9) to a commercial cellulase mixture would decrease Cel7A (a processive exoglucanase) adsorption during hydrolysis of crystalline cellulose I. Nakamura and co-workers  pointed out that the hydrolytic velocity of CBH I on the crystalline cellulose surface was related to a high dissociation rate constant from the substrate.
Based on the structure characteristics of cellulose substrates, C-I, IC-I, and IpRC-I, it was observed that β-1,4 glycosidic bonds of cellulose backbone chain were scissored by ROS derived from irradiation oxidation. XPS analysis showed that a range of new oxidized end products is formed with ketone group (–C=O–) when cellulose was treated by irradiation oxidation (e.g., IC-I cellulose), while FT-IR data reveal that a range of new chain reductive end products is generated and ketone functional group is disappeared after post-reduction treatment (e.g., IpRC-I cellulose). These new reductive end products may be acting as “substrate-affinity” factors much easier accessible to cellulases. Therefore, a positive effect on hydrolytic efficiency (seen in Fig. 1) is achieved by the oxidized and reduced new chain ends, which damage the normal chair conformation of the sugar ring .
Analysis of the new chain end products of crystalline cellulose treated with irradiation and IOPR process
From these above observations, two important features stand out. First, a cleavage of glycosidic bond in crystalline cellulose after IOPR treatment is achieved by conjugating with an ROS oxidation step. Second, new chain end products of sorbitol structure released from IOPR are dominated by even-numbered oligosaccharides with the DP ≤ 7. The schematic overview of irradiation and IOPR related to cleavage of glycosidic bonds of crystalline cellulose association with oxidized and reduced new chain ends are shown in Fig. 3c. These nanoscale architecture modifications of cellulose reveal a synergy linkage of IOPR and cellulase hydrolysis, wherein the degradation mechanism of cellulose shows noticeable difference from the traditional glycoside hydrolysis .
Fascinating digestion mechanism of crystalline cellulose by free hydrolytic cellulases after irradiation and IOPR process
TEM images in Fig. 4 confirm that there exists a fascinating digestion mechanism of “peel-off” and “cavity-form” combination for cellulases acting on crystalline cellulose after cellulose substrates are treated with IOPR process. In case of irradiated cellulose (IC-I), the reducing end of the particle is finely tapered to a narrow point, and the opposite end displays a blunt edge, exhibiting a slight angle from the long axis (Fig. 4B, B’’), and the middle surface shows ablation (Fig. 4B’). As for the native cellulose substrate (C-I), the similar phenomenon is observed for both ends of cellulose hydrolyzed by cellulases (Fig. 4A, A’’), but the middle keeps almost undamaged (Fig. 4A’; Additional file 1: Figure S9). This results in reducing end-oriented digestion mechanism on the surface as Ce17A from T. reesei ; it is the typical “peel off” mechanism that CBH I (e.g., TrCel7A) degrades the cellulose from the reducing end, narrowing of the crystal end, whereas CBH II (e.g., TrCel6A) hydrolyzes the cellulose chain from the nonreducing end less processively than CBH I, sharpening the crystal tip [39, 41].
Regarding NaBH4 post-reduction cellulose (IpRC-I), TEM images show that the reducing end of the particle displays narrowed, irregular, but not finely tapered morphology (Fig. 4c), and cavities-formation is observed in the middle and the opposite end (Fig. 4c’, c’’). It can be attributed to the fact that the new end products in glucan chain generated from IOPR are much accessible to CBHs, which excavate extensive cavities into the surface of the cellulose bundles. This fascinating digestion paradigm is similar to the cavity-forming mechanism caused by cellulosomes (e.g., Ce17A from Caldicellulosiruptor bescii) .
In combination with MALDI-TOF–MS and TEM, a reasonable conclusion can be drawn that there is an unexpected connection between cellulose chain structural modification, especially chain end products, and enzymatic degradation of crystalline cellulose, rather than only focusing on the traditional concerns about DP, accessibility, crystallinity and allomorphs forms of cellulose. This encouraging result opens a new avenue toward the implementation of pretreatment and the design of enzyme cocktails in lignocellulosic biorefinery.
A novel non-enzymatic oxidative cleavage strategy of IOPR process is proposed to act on crystalline cellulose I to boost downstream degradation by cellulases from Trichoderma reesei. Regardless of the “model” cellulose substrates (e.g., Avicel PH-101) or real biomass cellulose (e.g., Eucalyptus and Pine), the treated crystalline celluloses are easily bio-converted into fermentable sugars. 81.6% of conversion efficiency was achieved for 24-h cellulase hydrolysis of crystalline cellulose. Assuming elongation of saccharification time to 48 h, 97% of conversion efficiency has been reached. Combining consideration of the low milling energy consumption to the crackdown of feedstock after irradiation pretreatment on biomass [18, 22, 42], a practical cost-efficient pretreatment protocol will be suggested for lignocellulosic biorefinery. Although the comprehensive assessment of IOPR process still needs to experimentally evaluate the potential feasibility in an industrial setting, the results suggest that the proposed approach is motivating Scientists inspiration and will become an economically competitive alternative to current biomass pretreatment.
HZ performed the experiments and analyzed the data. LW determined the concentration of enzyme. YL supervised the project, conceived the experiments, and wrote the manuscript. All authors read and approved the final manuscript.
This work was financially funded by the National Natural Science Foundation of China (NSFC, 21476016; 21776009). The authors thank Dr. Jian Sun (Beijing University of Chemical Technology, China) for kindly providing ATR-FTIR instrument and helped to finish the SDS-PAGE analysis. The authors also acknowledge prof. Keqin Wang (Hunan Institute of Nuclear Agricultural Science and Space Breeding, Hunan, China) for kindly completing experiments about biomass and crystalline cellulose irradiation treatment.
The authors declare that they have no competing interests.
Ethics approval and consent to participate
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
- 4.Chen X, Shekiro J, Pschorn T, Sabourin M, Tao L, Elander R, Park S, Jennings E, Nelson R, Trass O, et al. A highly efficient dilute alkali deacetylation and mechanical (disc) refining process for the conversion of renewable biomass to lower cost sugars. Biotechnol Biofuels. 2014;7:98.CrossRefGoogle Scholar
- 34.Sluiter A, Hames B, Ruiz R, Scarlata C, Sluiter J, Templeton D. Determination of sugars, byproducts, and degradation products in liquid fraction process samples. Nat Renew Energy Lab. 2006. http://www.nrel.gov/docs/gen/fy08/42623.pdf.
- 39.Igarashi K, Uchihashi T, Koivula A, Wada M, Kimura S, Okamoto T, Penttilä M, Ando T, Samejima M. Traffic jams reduce hydrolytic efficiency of cellulase on cellulose surface. Science. 2011;334:453.Google Scholar
Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated.