Amorphous molybdenum sulfide (MoSx) is a highly active noble-metal-free electrocatalysts for the hydrogen evolution reaction (HER). The MoSx was prepared by electrochemical deposition at room temperature. Low-cost precursors of Mo and S were adopted to synthesize thiomolybdates solution as the electrolyte. It replaces the expensive (NH)2MoS4 and avoid the poison gas (H2S) to generate or employ. The (MoO2S2)2−, (MoOS3)2− and (MoS4)2− ions were determined by UV–VIS spectroscopy. The electrodeposition of MoSx was confirmed with XRD, XPS and SEM. The electrocatalyst activity was measured by polarization curve. The electrolyte contained (MoO2S2)2− ion and (MoOS3)2− ion electrodeposit the MoSx thin film displays a relatively high activity for HER with low overpotential of 211 mV at a current density of 10 mA cm−2, a relatively high current density of 21.03 mA cm−2 at η = 250 mV, a small Tafel slope of 55 mV dec−1. The added sodium dodecyl sulfate (SDS) can efficient improve the stability of the MoSx film catalyst.
Hydrogen is a cleaner and sustainable energy, and it is one of the promising alternative energy carriers [1, 2]. Electrochemical water splitting is attractive methods for hydrogen evolution [3,4,5]. An important problem for this method is seeking highly catalytic active electrocatalysts for hydrogen evolution reaction. In this regard, various efficient electrocatalysts materials, including Pt and other noble metals were investigated. However, high cost of Pt or other noble metals impede their widespread application [6, 7].
The employment of catalysts should have greatly highly catalytic active, low-cost, and earth-abundant non-noble metal. Recently, molybdenum sulfide is found to be an active HER catalyst, and it is useful for acidic HER condition [8,9,10,11,12,13,14,15,16,17,18,19,20]. While amorphous molybdenum shows highly catalytic activity at the unsaturated sulfur atoms present over the entire surface [11, 13, 21,22,23,24,25]. In the previous research, the most promising method of preparing the amorphous materials is cathodic reduction of an aqueous solution of ammonium tetrathiomolybdate ((NH)2MoS4). Some researchers used the commodity ((NH)2MoS4) [13, 21, 25,26,27], however, the commodity ((NH)2MoS4) is highly expensive, therefore, some researchers synthesize the ((NH)2MoS4) solution [28,29,30]. The methods for preparing of ammonium tetrathiomolybdate ((NH4)2(MoS4)) species are almost identical to Krüss , and the methods was improved by John W. McDonald’s group  for the preparation of (NH4)2(MoO2S2), (NH4)2(MoOS3) and (NH4)2(MoS4). The synthesis involves the exhaustive treatment by H2S gas of molybdate solution in concentrated NH4OH. This method can easy to obtain the (NH4)2(MoS4), however, a steady stream of H2S was employed. Ponomarev et al.  prepared the tetrathiomolybdate solution utilized a chemical reaction route. To a mixture solution of 5 mmol L−1 Na2MoO4 and excess Na2S was added hydrochloric acid with stirring until a pH of 8.0 was attained. During this process, large amount of H2S gas was generated.
In this work, we further improved the approaches of synthesis of thiomolybdates solution. (NH4)6Mo7O24·4H2O and Na2S·9H2O were employed as the precursors of Mo and S, respectively. The ammonium chloride buffer solution (pH = 8) replaced the hydrochloric acid to make the pH of the solution to 8. This method does not produce a large amount of H2S gas due to excessive local acid concentration. And it is very simple, the process is easy to control and is mild. Additionally, the precursor materials are economic, especially, the prepared thiomolybdates solution has great stability. The synthesized thiomolybdates solution as the electrolyte, employ the electrochemical deposition of amorphous molybdenum sulfide thin film for electrochemical hydrogen evolution. The HER performance measurement result suggests the catalyst displayed high catalytic activity for hydrogen evolution reaction. Add a bit of surfactant into the electrolyte, the stability of the MoSx film has effectively improved.
Materials and methods
Hexaammonium heptamolybdate tetrahydrate ((NH4)6Mo7O24·4H2O, ≥ 99.0%) was used as the Mo precursor. Sodium sulfide nonahydrate (Na2S·9H2O, ≥ 98.0%) was used as the S precursor. Ammonium chloride (NH4Cl, ≥ 99.5%), ammonia solution (NH3, 25–28%), sulfuric acid (H2SO4, 95–98%), hydrochloric acid (HCl, 36.0–38.0%), acetone (CH3COCH3, ≥ 99.5%), sodium dodecyl sulfate (C12H25NaO4S, ≥ 85.0%). All reagents were purchased and used as received.
UV–VIS spectrophotometer (TU-1810,Beijing). Scanning electron microscopy (SEM) combined with energy dispersive X-ray spectroscopic (EDS) images were taken with a TESCAN VEGA II LMU instrument. The phase compositions of the samples were identified using an X-ray diffractometer (XRD, X’pert PRO, PANalytical B.V., Holland) using Cu Kα radiation (0.15418 nm). The electrodeposition and electrochemical measurements were carried out at room temperature in a three-electrode glass cell connected to an electrochemical workstation (CHI440A, chenghua, Shanghai). The surface chemical composition was analyzed by X-ray photoelectron spectroscopy (XPS, Thermoelectron ESCALAB 250, USA).
Syntheses of thiomolybdates solution
(NH4)6Mo7O24·4H2O (3.58 g) was dissolved in 200 mL ammonium chloride buffer solution (pH = 8). In a second container, 21.65 g of Na2S·9H2O was added to 300 mL of ammonium chloride buffer solution (pH = 8). These two solutions were mixed and transferred to a 500 mL beaker. Put the mixed solution beaker to the ~ 90 °C water bath for 2 h. After that, the black and red solution was transferred to a 500 mL flask. Once the solution is cooling down to the room temperature, then the deionized water is used to add the solution to the scale.
The substrate used titanium ingot (11.28 mm diameter, 3.5 mm thick, purity 99.99%). Prior to the electrodeposition, the Ti substrate was carefully cleaned with mechanical polishing, acetone and HCl solution (9 wt%) in an ultrasound bath each for 5 min, successively. And then it was washed with deionized water after each step. Polytetrafluoroethylene (PTFE) electrode sets with working area of 1 cm2. MoSx was deposited on Ti substrate by electrodeposition in a three-electrode setup. The PTFE electrode sets with treated Ti substrate as the working electrode, saturated calomel electrode (SCE) as the reference electrode, and a graphite board as the counter electrode. The synthesized thiomolybdates solution as the electrolyte. The electrodeposition adopted the method of chronopotentiometry (CP).
The thiomolybdates determination were conducted using the UV–VIS spectrophotometer of ref. 30. Take 0.1 mL thiomolybdates solution and dilute to 100 mL for spectral detecting. The range of wavelength is from 190 to 600 nm. The scan rate is 0.5 nm s−1.
Electrochemical measurements were carried out with a three-electrode configuration in which saturated calomel electrode as the reference electrode, a graphite board as the counter electrode. Linear sweep voltammetry (LSV) with a 5 mV s−1 scan rate was performed in 0.5 M H2SO4 electrolyte, which was purged with N2 gas for at least 30 min prior to the LSV measurements in order to remove any dissolved O2. LSV curves were measured fifth for each sample to verification of the system’s chemical stability. The scan range from 0.00 to − 0.55 V vs. SCE (not iR corrected). After the LSV measurements, the solution was stirred. The reference electrode was calibrated for the reversible hydrogen potential using platinum wire was working and counter electrodes in the electrolyte solution saturated with H2. In 0.5 M H2SO4, the potential was converted to the reversible hydrogen potential (RHE) reference electrode by E (vs. RHE) = E (vs. SCE) + 0.26 V. The resistance (R) was tested by EIS. EIS measurements were carried out in the frequency range of 0.1 Hz to 105 Hz under a hydrogen evolution voltage, which corresponds to the potential at 10 mA cm−2.
Electrochemical stability is an important parameter for viability of a HER catalyst. To investigate HER stability under electrocatalytic operation in the acidic environment, long-term potential cycling stability of the MoSx film was assessed by taking continuous cyclic voltammograms (CV) between 0.0 and − 0.55 V vs. saturated calomel electrode (not iR corrected) at 100 mV s−1.
Results and discussion
Thiomolybdates solutions were synthesized in the buffer solutions containing different concentrations of ammonium chloride. The ammonium chloride concentration is from 0.1 to 0.5 M. Different ammonium chloride concentration results in the different color of the thiomolybdates solutions. The thiomolybdates solutions color was changed from light yellow to dark red, along with the increasing of the ammonium chloride concentration. The different color of the thiomolybdates solutions attribute to the different thiomolybdates species. The various thiomolybdates can be determined by UV–VIS Spectroscopy . The actual UV–VIS Spectra of the thiomolybdates solutions are shown in Fig. 1. Peak position and molar absorptivities are provided in Table 1.
By comparing the results from the previously reports , it can be concluded that to adjust the ammonium chloride concentration of the ammonium chloride buffer solution can syntheses the various thiomolybdates solutions. With the concentration of ammonium chloride increases, the thio-degree rises up. In the 0.2 M NH4Cl buffer solution, the molar absorptivities for the peaks at 292.0 and 395.5 nm, the result clear support for the (MoO2S2)2− ion was synthesized. In the 0.3 M NH4Cl buffer solution, the peak at 466 nm started to appear, this result supports for the (MoOS3)2− ion initial synthesis. In the solutions with ammonium chloride concentration of 0.4 M and 0.5 M, the intensity of the peak at 467.0 nm is becoming stronger, and the intensity of the peaks at 396.0 and 467.0 nm was very close. From the previously reports , the purity (MoS4)2− ion exhibits a very strong absorption at 467 nm but non at 395 nm. In Fig. 1, according to the spectra of the 0.4 M NH4Cl and the 0.5 M NH4Cl buffer solution, the peaks at 396.0 and 467.0 nm are simultaneous occurrence. From these results it is clear that the solution contains both of the (MoOS3)2− ion and (MoS4)2− ion, and the content of (MoS4)2− in the 0.5 M NH4Cl buffer solution is more than in the 0.4 M NH4Cl buffer solution. The ammonium chloride concentration determines the buffer capacity of buffer solution. The results suggest both of the 0.4 M and 0.5 M NH4Cl buffer solution could synthesize the solution with the (MoOS3)2− ion and (MoS4)2− ion. And the two ions could to produce the molybdenum sulfide thin film under electrochemical deposition. We required the synthesized thiomolybdates solution as the electrolyte to electrodeposit of molybdenum sulfide thin film, and the molybdenum sulfide thin film could with relatively high HER performance.
Characterization of MoSx
In the previous studies [13, 21, 25,26,27], they always employed the purity tetrathiomolybdate to prepare the MoS2 or MoS3. In this work, we applied the synthesized thiomolybdates solution as the electrolyte to electrodeposit of molybdenum sulfide thin film for electrochemical hydrogen evolution, and XRD (Additional file 1: Figure S1) analysis identified as amorphous molybdenum sulfides.
Figure 2 displays the detailed XPS scans for the Mo and S binding energies for the molybdenum sulfide thin film. The XPS spectra of molybdenum sulfide thin film are similar to those of known MoSx samples [13, 22]. The molybdenum sulfide thin film exhibits two characteristic peaks at 229.4 and 232.5 eV, attributed to the Mo 3d5/2 and 3d3/2 binding energies for Mo4+ [11, 13, 22]. The observation of Mo 3d5/2 and 3d3/2 binding energies at 230.5 and 234.1 eV suggests the presence of Mo5+ ions [11, 13, 22]. The peaks, corresponding to the Mo 3d5/2 and 3d3/2 orbital of Mo6+ are observed at 233.1 and 235.7 eV. Meanwhile, the S 2p1/2 and 2p3/2 energies at 162.0 and 162.4 eV demonstrate the existence of bridging S2−. And the S 2p1/2 and 2p3/2 energies at 163.3 and 164.7 eV indicate the existence of bridging S22− or S2−. The binding energies of Mo and S, proving that the structure is amorphous molybdenum sulfides, labeled as MoSx [22, 31].
The electrodeposition method for amorphous molybdenum sulfide thin film was CP. The deposition current density was 2 mA cm−2, the deposition temperature was 20.0 °C, the deposition time was 900 s, and accompanied with stirring during the deposition process. The electrolyte used the synthesized thiomolybdates solutions with 0.2 M, 0.4 M and 0.5 M ammonium chloride, respectively. The samples named as S-0.2, S-0.4 and S-0.5 corresponding to the ammonium chloride concentration. The deposition curves (potential–time) are shown in Fig. 3a, and color film formed on the electrode (Inset in Fig. 3a).
The HER catalytic activity of these molybdenum sulfide films as the catalyst was measured employing the standard three-electrode electrochemical configuration in 0.5 M H2SO4 electrolyte-aerated with Ar, as described in “Materials and methods”. The polarization curves (not iR corrected) showing the normalized current density versus voltage (j versus V) for the S-0.2, S-0.4 and S-0.5 films along with Pt wire and Ti ingot samples, for comparison, are illustrated in Fig. 3b. As expected, Pt wire catalyst exhibits excellent HER performance, and their HER performances are summarized in Table 2. In contrast, S-0.2, S-0.4 and S-0.5 films produces j of 10 mA cm−2 at η of 319 mV, 211 mV and 270 mV, respectively. Further insight into the catalytic activity of MoSx samples were obtained by extracting the slopes from the Tafel plots shown in Fig. 3c. The corresponding Tafel slopes of the MoSx films are in the range of 55 to 87 mV dec−1. The lowest Tafel slope of ~ 55 mV per decade was attained for the sample of S-0.4. This indicates the Volmer reaction is taking place, a process to convert protons into sorbed hydrogen atoms on the MoSx film surface, and this process becomes the rate-determining step in the HER mechanism [5, 32, 33]. Figure 3d exhibits the ammonium chloride concentration dependent current densities at η = 150, 200 and 250 mV. The current densities at the optimal ammonium chloride concentration are 1.12, 7.50 and 21.03 mA cm−2 at η = 150, 200 and 250 mV, respectively. The optimal ammonium chloride concentration is 0.4 M. The sample of S-0.4 film displayed relative high catalytic activity for hydrogen evolution reaction, the overpotential is lower than many other reported acid-stable and earth-abundant HER electrocatalysts, including amorphous MoS3 (~ 270 mV at 10 mA cm−2) , amorphous MoSx film (~ 150 mV at 0.4 mA cm−2) , amorphous molybdenum sulfide (~ 200 mV at 10 mA cm−2) , electrodeposited MoS2 (~ 440 mV at 10 mA cm−2)  and double-gyroid mesoporous MoS2 films (~ 235 mV at 10 mA cm−2)  (More details of HER parameters of MoSx and other literature values is listed in Table 3).
Another important aspect utilized to evaluate the performance of an electrocatalyst is the long-term operating stability. Continuous cyclic voltammetry (CV) in the cathodic potential window at a scan rate of 100 mV s−1 was performed on the films over 1000 cycles to investigate their long-term stability. Cathodic polarization curves were collected after 1000 cycles testing (Fig. 4) to investigation the current–density degradation compared with the initial polarization curve. In Fig. 4a, the cathodic polarization curves were corresponding to the sample of S-0.4. It is observed that the current density (without iR correction at overpotential of 250 mV) degradation from 20.72 mA cm−2 to 5.34 mA cm−2 (ca. 26% retention) after 1000 cycles. This suggests that the sample of S-0.4 was not stable enough. To improve the stable of the sample, a little surfactant was added into the thiomolybdates solution electrolyte. The purpose is to reduce the surface tension of the electrode, and allows the deposited sample to have better adhesion. Among a wide variety of surfactants, sodium dodecyl sulfate (SDS) was accepted. The concentration of SDS in the thiomolybdates solution was 5 mM. With the same condition of S-0.4, the sample added SDS labeled as S-0.4-SDS. And the cathodic polarization curves were collected of the sample S-0.4-SDS shown in Fig. 4b. From the curves, the current density (without iR correction at overpotential of 250 mV) degradation from 8.31 to 7.87 mA cm−2 (ca. 95% retention) after 1000 cycles. This demonstrates that the S-0.4-SDS films are stable throughout long-term repeated cycling in acidic electrolyte. The HER catalytic activity of the sample of S-0.4-SDS was studied by polarization measurements. The current densities are 0.86, 3.37 and 8.31 mA cm−2 at η = 150, 200 and 250 mV, respectively. The Tafel slop is about 80 mV dec−1. Although the Tafel slop was higher, the stable of the catalytic was much more improved. Furthermore, SEM images performed on the two samples (Fig. 5) both of their before and after cycles. The SEM images confirms that the surface morphology of S-0.4-SDS (Fig. 5c) and was not changed after 1000 cycles (Fig. 5d). In addition, the energy-dispersion X-ray spectroscopy (EDS) images (Additional file 1: Figure S3h, i, k, l) showed homogeneous distribution of Mo and S elements. But the surface morphology of S-0.4 (Fig. 5a) was appeared many deep cracks after 1000 cycles (Fig. 5b) with corresponding EDS mapping (Additional file 1: Figure S3b, c, e, f) uniform distribution for Mo and S elements. The SDS is one of the surface active agent. Adding appropriate surfactant can decrease the surface tension of the MoSx film, increase the dispersion and minish effectively particle size of MoSx film, thereby improve effectively the stability of the MoSx film.
Meanwhile, electrochemical impedance spectroscopy (EIS) was employed to evaluate the conductivity of the catalysts (Additional file 1: Figure S2). The Nyquist plots were fitted using an equivalent circuit containing a resistor (Rs) in series with two parallel units, a charge-transfer resistance (Rct) and a constant phase element (CPE1), where Rs represents the solution resistance. The Rs values of S-0.4, S-0.4-SDS, and Ti ingot are 1.546, 1.477 and 1.146 Ω, respectively. The observed semicircle is mainly ascribed to the Rct of H+ reduction at the electrode–electrolyte interface. The Rct values of S-0.4, S-0.4-SDS, and Ti ingot are estimated as 1.762, 1.941 and 47.600 Ω from the diameter of the semicircles, respectively. A smaller Rct value represents a faster reaction rate in the catalytic process. The EIS results could further explain the S-0.4 and S-0.4-SDS presented a charge-transfer resistance (Rct) obviously lower than those of Ti ingot. The result is consistent with the polarization curve.
In conclusion, we have developed a low-cost, environmentally friendly and a simple synthetic strategy to synthesis of thiomolybdates solution as the electrolyte to electrodeposit of amorphous molybdenum sulfide thin film for the HER. Our results provide evidence for electrodeposit of amorphous molybdenum sulfide thin film not only can used the electrolyte consists purity (MoS4)2− ion but also the (MoO2S2)2− ion and the (MoOS3)2− ion consists in the electrolyte can electrodeposit the amorphous molybdenum sulfide thin film. The electrolyte contained (MoO2S2)2− ion and (MoOS3)2− ion electrodeposit the MoSx thin film displays a relatively high activity for HER with low overpotential of 211 mV at a current density of 10 mA cm−2, a relatively high current density of 21.03 mA cm−2 at η = 250 mV, a small Tafel slope of 55 mV dec−1. When the SDS is added into the electrolyte, the stability of the MoSx film has effectively improved, even though the catalytic activity for hydrogen evolution reaction has reduced. Therefore, this work essentially offers an economy, mild condition, viable and scalable strategy for preparing highly efficient HER electrocatalysts for the development of effective electrochemical water-splitting technology.
Availability of data and materials
We have presented all our main data in the form of tables and figures.
- MoSx :
amorphous molybdenum sulfide
hydrogen evolution reaction
linear sweep voltammetry
saturated calomel electrode
reversible hydrogen potential
electrochemical impedance spectroscopy
scanning electron microscopy
energy dispersive X-ray spectroscopic
X-ray photoelectron spectroscopy
sodium dodecyl sulfate
Dresselhaus MS, Thomas IL (2001) Alternative energy technologies. Natute 414:332–337
Turner JA (2004) Sustainable hydrogen production. Science 305(5686):972–974
Bloor LG, Molina PI, Symes MD, Cronin L (2014) Low pH electrolytic water splitting using earth-abundant metastable catalysts that self-assemble in situ. J Am Chem Soc 136(8):3304–3311
Rausch B, Symes MD, Chisholm G, Cronin L (2014) Decoupled catalytic hydrogen evolution from a molecular metal oxide redox mediator in water splitting. Science 345(6202):1326–1330
Wang J, Xu F, Jin H, Chen Y, Wang Y (2017) Non-noble metal-based carbon composites in hydrogen evolution reaction: fundamentals to applications. Adv Mater 29(14):1605838
Subbaraman R, Tripkovic D, Strmcnik D, Chang KC, Uchimura M, Paulikas AP, Stamenkovic V, Markovic NM (2011) Enhancing hydrogen evolution activity in water splitting by tailoring Li+-Ni(OH)2-Pt interfaces. Science 334(6060):1256–1260
Jiang B, Yang L, Liao F, Sheng M, Zhao H, Lin H, Shao M (2017) A stepwise-designed Rh-Au-Si nanocomposite that surpasses Pt/C hydrogen evolution activity at high overpotentials. Nano Res 10(5):1749–1755
Hu J, Huang B, Zhang C, Wang Z, An Y, Zhou D, Lin H, Leung MKH et al (2017) Engineering stepped edge surface structures of MoS2 sheet stacks to accelerate the hydrogen evolution reaction. Energy Environ Sci 10(2):593–603
Jaramillo TF, Jørgensen KP, Bonde J, Nielsen JH, Horch S, Chorkendorff I (2007) Identification of active edge sites for electrochemical H2 evolution from MoS2 nanocatalysts. Science 317:100–102
Voiry D, Salehi M, Silva R, Fujita T, Chen M, Asefa T, Shenoy VB, Eda G et al (2013) Conducting MoS2 nanosheets as catalysts for hydrogen evolution reaction. Nano Lett 13(12):6222–6227
Vrubel H, Merki D, Hu X (2012) Hydrogen evolution catalyzed by MoS3 and MoS2 particles. Energy Environ Sci 5(3):6136–6144
Maijenburg AW, Regis M, Hattori AN, Tanaka H, Choi KS, ten Elshof JE (2014) MoS2 nanocube structures as catalysts for electrochemical H2 evolution from acidic aqueous solutions. ACS Appl Mater Interfaces 6(3):2003–2010
Morales-Guio CG, Hu X (2014) Amorphous molybdenum sulfides as hydrogen evolution catalysts. Acc Chem Res 47(8):2671–2681
Li H, Tsai C, Koh AL, Cai L, Contryman AW, Fragapane AH, Zhao J, Han HS et al (2016) Activating and optimizing MoS2 basal planes for hydrogen evolution through the formation of strained sulphur vacancies. Nat Mater 15(1):48–53
Li G, Zhang D, Qiao Q, Yu Y, Peterson D, Zafar A, Kumar R, Curtarolo S et al (2016) All the catalytic active sites of MoS2 for hydrogen evolution. J Am Chem Soc 138(51):16632–16638
Kong Q, Wang X, Tang A, Duan W, Liu B (2016) Three-dimensional hierarchical MoS2 nanosheet arrays/carbon cloth as flexible electrodes for high-performance hydrogen evolution reaction. Mater Lett 177:139–142
Zhao Y, Xie X, Zhang J, Liu H, Ahn HJ, Sun K, Wang G (2015) MoS2 nanosheets supported on 3D graphene aerogel as a highly efficient catalyst for hydrogen evolution. Chemistry 21(45):15908–15913
Hinnemann B, Moses PG, Bonde J, Jørgensen KP, Nielsen JH, Horch S, Chorkendorff I, Nørskov JK (2005) Biomimetic hydrogen evolution: MoS2 nanoparticles as catalyst for hydrogen evolution. J Am Chem Soc 127:5308–5309
Xie J, Zhang J, Li S, Grote F, Zhang X, Zhang H, Wang R, Lei Y et al (2013) Controllable disorder engineering in oxygen-incorporated MoS2 ultrathin nanosheets for efficient hydrogen evolution. J Am Chem Soc 135(47):17881–17888
Li Y, Wang H, Xie L, Liang Y, Hong G, Dai H (2011) MoS2 nanoparticles grown on graphene: an advanced catalyst for the hydrogen evolution reaction. J Am Chem Soc 133(19):7296–7299
Merki D, Fierro S, Vrubel H, Hu X (2011) Amorphous molybdenum sulfide films as catalysts for electrochemical hydrogen production in water. Chem Sci 2(7):1262–1267
Chang YH, Lin CT, Chen TY, Hsu CL, Lee YH, Zhang W, Wei KH, Li LJ (2013) Highly efficient electrocatalytic hydrogen production by MoSx grown on graphene-protected 3D Ni foams. Adv Mater 25(5):756–760
Benck JD, Chen Z, Kuritzky LY, Forman AJ, Jaramillo TF (2012) Amorphous molybdenum sulfide catalysts for electrochemical hydrogen production: insights into the origin of their catalytic activity. ACS Catal 2(9):1916–1923
Murugesan S, Akkineni A, Chou BP, Glaz MS, Bout DAV, Stevenson KJ (2013) Room temperature electrodeposition of molybdenum sulfide for catalytic and photoluminescence applications. ACS Nano 7(9):8199–8205
Vrubel H, Hu X (2013) Growth and activation of an amorphous molybdenum sulfide hydrogen evolving catalyst. ACS Catal 3(9):2002–2011
Albu-Yaron A, Levy-Clement C, Katty A, Bastide S, Tenne R (2000) Infulence of the electrochemical deposition parameters on the microstructure of MoS2 thin films. Thin Solid Films 361–362:223–228
Lamouchi A, Ben Assaker I, Chtourou R (2017) Effect of annealing temperature on the structural, optical, and electrical properties of MoS2 electrodeposited onto stainless steel mesh. J Mater Sci 52:4635–4646
Ponomarev EA, Neumann-Spallart M, Hodes G, Lévy-Clément C (1996) Electrochemical deposition of MoS2 thin films by reduction of tetrathiomolybdate. Thin Solid Films 280:86–89
Kriiss G (1884) Ueber die Schwefelverbidungen des Molybdäns. Ann Chem 225:1–57
McDonald JW, Friesen GD, Rosenhein LD, Newton WE (1983) Syntheses and characterization of ammonium and tetraalkylammonium thiomolybdates and thiotungstates. Inorg Chim Acta 72:205–210
Tran PD, Tran TV, Orio M, Torelli S, Truong QD, Nayuki K, Sasaki Y, Chiam SY et al (2016) Coordination polymer structure and revisited hydrogen evolution catalytic mechanism for amorphous molybdenum sulfide. Nat Mater 15(6):640–646
Pentland N, Bockris JOM, Sheldon E (1957) Hydrogen evolution reaction on copper, gold, molybdenum, palladium, rhodium, and iron: mechanism and measurement technique under high purity conditions. J Electrochem Soc 104(3):182–194
Chialvo MRGD, Chialvo AC (1994) Hydrogen evolution reaction: analysis of the Volmer-Heyrovsky-Tafel mechanism with a generalized adsorption model. J Electroanal Chem 372:209–223
Kibsgaard J, Chen Z, Reinecke BN, Jaramillo TF (2012) Engineering the surface structure of MoS2 to preferentially expose active edge sites for electrocatalysis. Nat Mater 11(11):963–969
Chen Z, Cummins D, Reinecke BN, Clark E, Sunkara MK, Jaramillo TF (2011) Core-shell MoO3-MoS2 nanowires for hydrogen evolution: a functional design for electrocatalytic materials. Nano Lett 11(10):4168–4175
Ge X, Chen L, Zhang L, Wen Y, Hirata A, Chen M (2014) Nanoporous metal enhanced catalytic activities of amorphous molybdenum sulfide for high-efficiency hydrogen production. Adv Mater 26(19):3100–3104
This work was supported by the Project No. CDJXS11221171 Supported by the Fundamental Research Funds for the Central Universities, and the sharing fund of Chongqing University’s Large-scale Equipment.
The authors declare that they have no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
XRD spectra for MoSx film grown on the Ti ingot by chronopotentiometry negative electrodeposition at 2 mA cm−2. Figure S2. Nyquist plot representations of electrochemical impedance spectra of S-0.4, S-0.4-SDS, and Ti ingot. Figure S3. SEM images and EDS elemental mapping for Mo and S of amorphous MoSx films. Panels a and d are the SEM images for S-0.4 (a) before and (b) after CV for 1000 cycles with corresponding (b, c, e, f) EDS elemental mapping images, respectively. Panels g and j are the SEM images for S-0.4-SDS (c) before and (d) after CV for 1000 cycles with corresponding (h, i, k, l) EDS elemental mapping images, respectively.
About this article
Cite this article
Zhang, L., Wu, L., Li, J. et al. Electrodeposition of amorphous molybdenum sulfide thin film for electrochemical hydrogen evolution reaction. BMC Chemistry 13, 88 (2019). https://doi.org/10.1186/s13065-019-0600-0
- Thiomolybdates solution
- Amorphous molybdenum sulfide
- Buffer solution