In vitro analysis of the cytotoxicity and the antimicrobial effect of four endodontic sealers
- 7.1k Downloads
The aim of this study was to investigate in vitro the cytotoxicity and antibacterial properties of four different endodontic sealers using human periodontal ligament fibroblast cell proliferation and visual analysis of growth inhibition.
A silicone (GuttaFlow), silicate (EndoSequence BC), zinc oxide eugenol (Pulp Canal Sealer EWT) and epoxy resin (AH Plus Jet) based sealer were incubated with PDL fibroblasts (104 cells/ml, n = 6) up to 96 h. Cell proliferation (RFU) was determined by means of the Alamar Blue assay. Cell growth and morphology was visualized by means of fluorescent dyes. Possible antibacterial properties of the different sealers were visualized by means of SEM (Enterococcus faecalis; Parvimonas micra).
Fibroblast proliferation depended on sealer and cultivation time. After 72 and 96 h GuttaFlow and EndoSequence BC showed relatively non-cytotoxic reactions, while Pulp Canal Sealer EWT and AH Plus Jet caused a significant decrease of cell proliferation (p < 0.001). Visualization of cell growth and morphology with various fluorescent dyes supplemented the results. No antibacterial effect of EndoSequence BC to P. micra was found, whereas GuttaFlow showed a weak, Pulp Canal Sealer EWT and AH Plus Jet extensive growth inhibition. Also, no antibacterial effect of GuttaFlow, EndoSequence BC or AH Plus Jet to E. faecalis could be detected.
These in vitro findings reveal that GuttaFlow and EndoSequence BC can be considered as biocompatible sealing materials. However, prior to their clinical employment, studies regarding their sealing properties also need to be considered.
Keywordsin vitro study root canal sealer E. faecalis P. micra cytotoxicity
In recent decades, a considerable Improvement in endodontic methods, devices, and also in root canal filling materials, has occurred. Thus, patients as well as dental professionals are more inclined to favour tooth preservation over extraction of disputable teeth [1, 2]. In consequence, since increased technical knowledge and scientific improvements have lead to higher treatment success rates, endodontic treatment and the subsequent restoration of the tooth should be considered as a therapy superior to implantation [3, 4].
The choice of a biocompatible sealing material is crucial to the clinical success of endodontic therapy . Although sealers were developed to be confined within the root canal system, their extrusion over the apical constriction is frequently observed [6, 7]. Therefore, these materials should have good biocompatibility and be well tolerated by the peri-apical tissues . The induction of a mild tissue reaction, together with cellular resorption of the sealing material in the case of extrusion over the apical foramen, needs to be evaluated. Several in vitro, in vivo and clinical studies [9, 10, 11, 12, 13] indicate that AH Plus, an epoxy resin-based root canal sealer, is suitable for successful endodontic therapy. This sealer remains popular despite its well-documented mutagenicity , cytotoxicity and the induction of a severe inflammatory response [15, 16, 17]. Besides cell dysfunctionality as a reaction to the epoxy resin-based sealing material , an intense inflammation characterized by the presence of lymphocytes, macrophages, giant foreign body cells as well as necrotic bone fragments in maxilla of guinea pigs after AH Plus implantation was observed. Due to its severe initial inflammatory reaction that diminished over time but persisted throughout the entire observation period, the authors  claim that this material does not possess enough biocompatible properties to be considered as an acceptable sealer for clinical use. Based on these contradictory results concerning an endodontic sealing material with a "gold standard" status , the tissue reaction induced by alternative sealers needs to be investigated in similar study designs to decide upon their potential clinical usage. GuttaFlow is a relatively new sealing material, which combines gutta-percha and sealer into an injectable system. According to the manufacturer, this system is based on polydimethylsiloxane with added gutta-percha and nano-silver particles (< 30 μm). Due to its viscosity, it is more likely to be extruded into the peri-apical tissue when placed under pressure . However, it remains unclear which tissue reaction is caused by this material. In the study of AlAnezi et al. , the possible cytotoxicity of Endosequence BC Root Repair Material and grey and white MTA was evaluated. When exposed to these materials, the cells showed no significant difference in viability, while the cells in contact with AH 26 were significantly reduce in their viability.
Cleaning and shaping procedures are used to eliminate microorganisms from the root canal system during endodontic treatment. However, quite often a complete removal of bacteria is not possible . In such cases it would be desirable that sealing materials have antimicrobial properties. Using either the agar diffusion test or the direct contact test or both, different endodontic sealers have already been assessed for a possible antibacterial effect, most often measured against strains of E. faecalis [21, 22, 23, 24, 25, 26, 27, 28].
Baer and Maki  demonstrated that AH Plus and Pulp Canal Sealer EWT were not able to inhibit the growth of E. faecalis.
Therefore, the present in vitro study aimed at comparing the biocompatibility and the possible antibacterial effect on E. faecalis and P. micra of the four different root filling materials GuttaFlow, Endosequence BC, Pulp Canal Sealer EWT and AH Plus Jet.
Materials and methods
For this in vitro study four different root canal sealers were chosen: GuttaFlow (Roeko, Coltène Langenau Germany, Batch No. 240412) consists of a polydimethylsiloxane matrix, is a cold flowable and self-curing sealer, which combines sealer and gutta-percha in one product; Endosequence BC Sealer (Brasseler, Savannah, GA, USA, Batch No. 0900458) is a premixed ready-to-use injectable material, based on a calcium silicate composition; Pulp Canal Sealer EWT (Pulp Canal Sealer EWT; SybronEndo, Orange, CA, USA, Batch No. 9-1222) is a zinc oxide eugenol based sealer; AH Plus Jet (Dentsply/Detrey, Konstanz, Germany, Batch No. 1004002041) is an epoxy resin based root canal sealer and consists of a paste-paste system, with paste A containing epoxy resin and iron oxide, and paste B containing amines and silicone oil.
To determine the bacterial colonization of root canal sealers, discs of equal size (Ø 12.5 ± 0.5 mm; thickness 2 ± 0.5 mm) were prepared under sterile conditions from the materials and allowed to set for 24 h.
Human Periodontal Ligament Fibroblasts (Clonetics® HPdLF Lonza, Switzerland) were cultured in Dulbecco's Modified Eagle Medium, supplemented with 10% foetal bovine serum, 2 mM L-Glutamine and 100U/100 μg/ml Penicillin/Streptomycin (Invitrogen, Paisley, UK), incubated at 37°C, in a humidified atmosphere containing 5% CO2, and a bidaily medium change. To assess the interaction of the sealing agents with the fibroblasts, different in vitro assays were carried out.
To demonstrate the interactions between cells and sealing materials, cells (20,000 cells/well) were stained with various fluorescent dyes and viewed with an inverted fluorescence microscope (Axiovert 40C/Carl Zeiss, Göttingen, Germany) at magnifications of × 25-400 (Figure 1, middle).
Phallacidin (BODIPY® FL phallacidin; Invitrogen, Paisley, UK) selectively labels F-actin and was used to visualize the cytoskeleton. The blue-fluorescent DAPI nucleic acid stain (4',6-Diamidine-2'-phenylindole dihydrochloride; Roche Diagnostics, Mannheim, Germany) preferentially stains double stranded DNA. It yields highly fluorescent nuclei and no detectable cytoplasmic fluorescence. Blue fluorescence contrasts vividly with the green phallacidin staining.
Calcein-AM/Ethidium homodimer II staining (LIVE/DEAD® Viability/Cytotoxicity Kit; Invitrogen, Paisley, UK), a two-colour fluorescence-based method, was used to measure the viability of the cultured cells, and to detect a possible cytotoxic effect of the sealers. Calcein AM is a fluorogenic esterase substrate that is hydrolysed intracellularly to a green fluorescent product, which is an indicator of live cells. Ethidium homodimer II enters cells through damaged membranes and intercalates with the DNA in the nucleus, emitting a red fluorescent signal.
Cell viability assays
The four sealers were tested for possible effects on cell proliferation and metabolic activity of the PDL fibroblasts. Cell proliferation was quantitatively measured by means of the Alamar Blue assay (Alamar Blue Cell Viability Reagent; Biozol, Eching, Germany), which is based on detection of metabolic cell activity. The Alamar Blue reagent contains an indicator dye, which fluoresces in response to cell growth. The cells were incubated in a 96-well plate (10,000 cells/well) under standard conditions, and with 10% Alamar Blue for 96 h. At 0, 1, 6, 24, 48, 72, 96 h the fluorescence was measured at a wavelength of 560/20 and 620/40 nm with a fluorescence reader (Synergy HT-Reader, Biotek, Winooski, VT, USA). Cells without sealing material served as control. Logarithmic signals were converted to a linear scale and expressed as relative fluorescence units (RFU).
The cytotoxic potential of the four sealing materials was also investigated by means of the ToxiLight® BioAssay Kit (Lonza Rockland, Rockland, ME, USA). This assay is a non-destructive, bioluminescent cytotoxicity assay, which quantitatively measures the release of Adenylate Kinase (AK) from damaged cells. The PDL fibroblasts were incubated under standard conditions in a 96-well plate (30,000 cells/well). After incubating the cells with the sealing agent for 24 h, the supernatants were mixed with AK detection agent. After 5 min incubation, the emitted light intensity is measured in a luminometer (Synergy HT-Reader, Biotek, Winooski, VT, USA, Figure 1, right). Logarithmic signals were converted to a linear scale and expressed as relative luminescence units (RLU).
Bacterial colonization of root canal sealers
Enterococcus faecalis DSM 20478 was grown anaerobically for 24 h at 37°C in Schaedler broth (Becton Dickinson, Sparks, MD, USA). Parvimonas micra ATCC 33270 was grown anaerobically for 48 h at 37°C in Anaerobe Basal Broth (Oxoid, Basingstoke, Hampshire, England). Discs of equal size, prepared from the cements and set, were placed into Petri dishes, containing 25 ml of nutrient broth, inoculated with E. faecalis or P. micra, and incubated anaerobically at 37°C. After 24 h (E. faecalis) or 48 h (P. micra) of incubation, the discs were removed. To make the bacteria visible in a scanning electron microscope (SEM), the samples were fixed for 30 min in 3% formaldehyde at room temperature, and dehydrated by sequential washes through a series of 50 to 96% graded ethanol baths. After sputtering in a cold sputter unit, the samples were viewed in a DSM 962 SEM (Zeiss, Oberkochen, Germany) at an accelerating voltage of 10 kV.
Six replicates per sealing material were used in the cell proliferation and cytotoxicity assays, and the results are presented as means ± standard deviation. The statistical analysis was performed using SPSS 15.0 (SPSS Inc., Chicago, IL) and SAS 9.2 (SAS Institute Inc., Cary, NC). The data were analysed by the Mann-Whitney-Test; p < 0.05 was chosen to define statistical significance, p < 0.01 was termed as highly significant.
The need for endodontic treatment is often associated with an inflammation caused by bacterial infection. For the successful root canal treatment, minimizing the possible inflammatory reaction caused by sealing materials, and suppressing bacterial growth are fundamental conditions. The goal of the endodontic treatment is to treat the teeth before a bacterial infection develops, and to use a biocompatible sealing agent. In case of an infection leading to pulp necrosis or of a bacterial contamination of the apical tissue, it is crucial for the outcome of the endodontic treatment to have a successful microbial elimination from the infected root canal system or to achieve a small enough number of microorganisms, which is clinically manageable . It has also to be considered that in case of an inflammation caused by bacteria there will be a decrease of the pH in the peri-apical tissues, and thus there are special demands for the sealing agents . The major task in reducing the bacterial load, concentrated in the apical region of the root canal, is achieved by the mechanical effects of instrumentation and the use of antimicrobial solutions for irrigation. Different studies have shown the essential role of chemo-mechanical procedures in eliminating the bacteria from the root canal system [32, 33]. An antibacterial effect of root canal filling materials would be helpful, because if bacteria remain in dentinal tubules, this can serve as a reservoir for reinfection [34, 35]. The bacteria chosen for this study were E. faecalis and P. micra (formerly P. micros). The former has been especially associated with endodontic failure, but has also been isolated from necrotic pulps. The latter organism, P. micra, has been isolated from asymptomatic and symptomatic primary endodontic infections, including abscesses as well as from endodontically treated teeth in need of re-treatment.
Calcium hydroxide is a well-described intra-canal material with an antibacterial effect, based on an alkaline pH, which has been demonstrated in several studies [36, 37]. This substance was shown to inactivate bacterial lipopolysaccharides in vivo , but it is not effective in destroying all bacterial species associated with root canal infections.
Therefore, in this study the biocompatibility as well a possible antibacterial effects of four different types of root canal filling materials was tested; GuttaFlow, a gutta percha based material, the well described epoxy resin based AH Plus Jet, the Pulp Canal Sealer EWT as a zinc oxide eugenol based sealer, and the newly developed EndoSequence BC with a calcium silicate composition. An inflammatory reaction to various root canal filling materials is a frequent complication, and the knowledge of these characteristics is essential for the clinical success. Profound knowledge about the properties and responses to the used sealers is necessary to be better prepared for dealing with serious complications associated with over-extrusion of the material into the peri-apical area. The results of the cell proliferation assay showed that Pulp Canal Sealer EWT and AH Plus Jet significantly inhibited cell growth, and showed a lower biocompatibility in comparison to GuttaFlow and Endosequence BC. In the study of Brackett et al. , a severe and consistent cytotoxic response for Pulp Canal Sealer and AH Plus Jet was also observed, even over a time of up to 8 weeks, when tested in three different cell lines.
AH Plus also had a cytotoxic effect on human pulp cells in vitro, and showed other previously reported pro-inflammatory characteristics , The demands made on sealing materials have been modified in recent years. The primary requirement for sealing agents is to obturate the root canal system and to establish a hermetic seal of the apical area of the root. To achieve this is desirable to inhibit the growth of the microorganisms i.e. mainly bacteria remaining within the cleaned root canal system . On the other hand, root canal sealers are required to demonstrate a good biocompatibility and are not supposed to irritate the peri-radicular tissue. The sealing ability of the root canal filling material should allow an adequate peri-apical healing after placement.
This is relevant, because the extrusion of sealing materials into the apical region with the direct contact to the peri-apical tissue is a well-described complication in endodontic treatment. The over-extrusion of non-resorbable materials or materials with slow breakdown is regarded as a critical factor in the apical healing process.
It is known that when certain non-resorbable materials, especially in the maxilla, are extruded into the human sinus, or are in contact with connective tissue, these materials are capable of triggering chronic inflammations [42, 43]. The present findings with established root canal filling materials showed the challenging requirements for sealers. In addition, the paradoxical postulation of Grossmann is emphasized that root canal filling materials is supposed to inhibit the growth of all microorganisms, but at the same time show a good biocompatibility and not irritate the peri-radicular tissue.
The present study shows that the materials Endosequence BC and GuttaFlow demonstrated a high biocompatibility, but had no antibacterial effect against E. faecalis. For P. micra a weak antimicrobial effect was observed with GuttaFlow. The sealers AH Plus Jet and Pulp Canal Sealer EWT showed a lower biocompatibility compared to Endosequence BC and GuttaFlow, but exerted a strong antimicrobial effect on P. micra.
The authors whish to thank Claudia Darmstadt and Irmgard Schneiders for excellent technical assistance; Aslihan Gerhold-Ay from the Institute of Medical Biostatistics, Epidemiology and Informatics of the University Medical Centre, Johannes Gutenberg University Mainz, for advice concerning the statistical advice; Dr. Elmar Stender, Institute for Dental Material Sciences and Technology of the University Medical Centre, Johannes Gutenberg University Mainz, for the scanning electron micrographs.
- 1.Friedman S, Mor C: The success of endodontic therapy-healing and functionality. J Calif Dent Assoc. 2004, 6: 493-503.Google Scholar
- 9.Al-Khatar N, Kunzelmann KH, Hickel R: Apical leakage of new root canal sealers. J Dent Res. 1995, 74: 945.Google Scholar
- 40.Camargo CH, Camargo SE, Valera MC, Hiller KA, Schmalz G, Schweikel H: The induction of cytotoxicity, oxidative stress and genotoxicity by root canal sealers in mammalian cells. Oral Surg Oral Med Oral Pathol Oral Radiol Endod. 2009, 108: 952-960. 10.1016/j.tripleo.2009.07.015.CrossRefPubMedGoogle Scholar
- 41.Grossman LI: Root canal therapy. 1940, Kimpton, LondonGoogle Scholar
This article is published under license to BioMed Central Ltd. This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.