Green synthesis of silver nanoparticles from Tectona grandis seeds extract: characterization and mechanism of antimicrobial action on different microorganisms
- 228 Downloads
Green synthesis of silver nanoparticles makes use of plant constituents, like carbohydrates, fats, enzymes, flavonoids, terpenoids, polyphenols, and alkaloids, as reducing agents to synthesize silver nanoparticles. The present study for the first time utilized seed extract of Tectona grandis (teak) for reduction of 1 mM silver nitrate solution to silver nanoparticles. The method proved to be very simple, cost-efficient, and convenient. Synthesis of nanoparticles was confirmed by visual detection in which the colorless solution gets changed to a brown-colored solution. Further characterization was done by UV-visible spectroscopy, XRD, FTIR analysis, SEM/EDS, FESEM, and TEM. Size of silver nanoparticles was found to be 10–30 nm approximately as determined by transmission electron microscopy (TEM). Energy-dispersive spectra (EDS) revealed that nanoparticles contain silver in its pure form. Well diffusion method showed the antimicrobial effect of AgNPs on different microorganisms with the zone of inhibition of 16 mm for Staphylococcus aureus, 12 mm for Bacillus cereus, and 17 mm for E. coli when 50 μg of AgNPs was used. Minimum inhibitory concentration was found to be 5.2, 2.6, and 2.0 μg/ml for Bacillus cereus, Staphylococcus aureus, and E. coli respectively. Mode of action of antimicrobial activity of nanoparticles was investigated by determining leakage of reducing sugars and proteins, suggesting that AgNPs were able to destroy membrane permeability.
KeywordsSilver nanoparticles Green synthesis Characterization Antimicrobial activity
Field emission scanning electron microscopy
Fourier transformation infrared
Minimum inhibitory concentration
Scanning electron microscopy
Transmission electron microscopy
Nanotechnology is the process of synthesizing particles which are in the nano range, ranging from approximately 1 to 100 nm. They have large surface area to volume ratio due to which they possess optical properties as they are small enough to confine their electrons and produce quantum effects by which their detection becomes easy. Intensive research is being done on silver nanoparticles (AgNPs) owing to their wide range of applications in medical devices (He et al. 2013), pharmaceuticals (Kumar et al. 2011), clothing (Vigneshwaran et al. 2007a), and water purification (Lin et al. 2013) due to their antimicrobial properties and also in adsorption of metals and pesticides (Asthana et al. 2016; Das et al. 2012), sensing of food adulterants (Ping et al. 2012), detection of DNA (Thompson et al. 2008), etc.
Chemical reduction which is the most commonly used method for synthesis of nanoparticles uses an organic solvent, like ethylene glycol (Wiley et al. 2004), and reducing agents, like hydrazine (Guzmán et al. 2009), sodium borohydride (Song et al. 2009), trisodium citrate (Rashid et al. 2013), and ascorbate (Qin et al. 2010). There was an earnest need for the development of cleaner and safer methods as chemical reduction gives low yield, requires complicated purification and high energy. This gave rise to green synthesis which utilizes microorganisms (bacteria (Natarajan et al. 2010), fungi (Vigneshwaran et al. 2007b), yeast (Kowshik et al. 2002), actinomycetes (Sastry et al. 2003)) and plant extracts for the reduction of silver to silver nanoparticles. Synthesis of nanoparticles from microbes can be extracellular (Kowshik et al. 2002) or intracellular (Mukherjee et al. 2001). The major disadvantage of the use of microbial source is the maintenance of aseptic conditions, high cost of isolation, and their maintenance in culture media due to which plants promise to be excellent sources for reducing agents for the synthesis of nanoparticles. Parts of plants used for synthesis of AgNPs are leaf (Prakash et al. 2013), bark (Sathishkumar et al. 2009), seeds (Bar et al. 2009), roots (Suman et al. 2013), etc. There are numerous examples of AgNPs synthesis from diverse plant sources, like Chrysanthemum morifolium (He et al. 2013), Cassia auriculata (Kumar et al. 2011), Mimusops elengi (Prakash et al. 2013), Cinnamon zeylanicum (Sathishkumar et al. 2009), Jatropha curcas (Bar et al. 2009), and Morinda citrifolia (Suman et al. 2013). Constituents of plants, like carbohydrates, fats, enzymes, flavonoids, terpenoids, polyphenols, and alkaloids, are capable of reducing silver to nanoparticles.
Antimicrobial activity of silver nanoparticles has been reported in many research papers. The mechanism of antibacterial action of silver nanoparticles is a topic of debate and is not well understood. But many assumptions and theories are there. In one of the study on E. coli and Staphylococcus aureus, it was seen that silver ions get released by nanoparticles and accumulate around the cell wall or inside the cell and affect DNA replication and interact with thiol groups of protein, inducing protein inactivation (Feng et al. 2000). This also leads to the formation of reactive oxygen species (Matsumura et al. 2003).
Tectona grandis, commonly called as timber, teak, Sagun, has potential medicinal value. It is widely used for making furniture, cabinets, and musical instruments (Indira and Mohanadas 2002). Its bark has an antibacterial compound 5-hydroxy-1,4-naphthalenedione (Juglone) which shows antibacterial activity against Listeria monocytogenes and methicillin-resistant Staphylococcus aureus (MRSA) (Neamatallah et al. 2005). It is also used for the treatment of anemia and shows anti-hemolytic anemia activity (Diallo et al. 2008). Its seeds are acclaimed to be hair tonic, which is reported to increase the number of hair follicles in the anagenic phase (Jaybhaye et al. 2010). Its leaves, bark, and wood show antioxidant properties, with wood showing the highest (98.6%) inhibition against DPPH (Krishna and Jayakumaran 2010).
In the present study, Tectona grandis seed extract was utilized for the reduction of silver nitrate to silver nanoparticles, and characterization of the synthesized nanoparticles was carried out by UV-visible spectroscopy, scanning electron microscope (SEM), energy-dispersive X-ray spectroscopy (EDX), field emission scanning electron microscope (FESEM), transmission electron microscope (TEM), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FT-IR) analysis. Antimicrobial activity of the synthesized nanoparticles was investigated against representative human pathogenic microorganisms (Bacillus cereus, Staphylococcus aureus, and Escherichia coli). Minimum inhibitory concentration of silver nanoparticles against these microorganisms was determined. Besides, the mechanism of action of antimicrobial activity was understood by detecting leakage of reducing sugars and proteins through DNS and Bradford’s method, which indicated that killing of microorganisms was through the destruction of membranous structure and permeability.
Materials and methods
Tectona grandis seeds were collected from BHU campus. Before washing, the outer covering of the harvested seeds was removed. Seeds were dried at room temperature for 3–4 days so that moisture gets removed completely. Dried seeds were crushed to fine powder and stored in dry and airtight container for further use. Silver nitrate (AgNO3) was purchased from SRL, India. All other reagents were of analytical grade and used as received. All the solutions were freshly prepared with double distilled water for the experimental procedure and were kept in the dark to avoid any photochemical reaction.
Antimicrobial activity of silver nanoparticles was investigated against Gram-positive bacteria (Bacillus cereus; MTCC 9817 and Staphylococcus aureus; MTCC 7443) and Gram-negative bacteria (Escherichia coli; MTCC 443). Nutrient agar containing peptone, beef extract, and NaCl was used to maintain bacterial strains. Prior to the experiment, bacterial strains were inoculated in nutrient broth to encourage the growth of microorganisms in the exponential phase.
Tectona grandis seed extract preparation
Five grams of seed powder was carefully weighed and added in an Erlenmeyer flask of 250 ml containing 50 ml of double distilled water. The mixture in the flask was heated in a water bath for 15–20 min at 80 °C. After boiling, the extract was filtered using a muslin cloth to remove any coarse material. Volume was made up to 100 ml using double distilled water. The prepared extract was stored at 4 °C and used within 1 week.
Synthesis of silver nanoparticles using seed extract
1 mM silver nitrate solution in double distilled water was the source of silver. Silver nitrate and seed extract were mixed together in a ratio of 1:9. The reaction mixture was heated below the boiling point and continuously stirred at 800 rpm using magnetic stirrer. The mixture turned reddish brown in color within 1 h. The whole reaction was carried out in the dark. The obtained suspension of Ag/T. grandis was centrifuged at 15,000 rpm for 45 min. The pellet containing silver nanoparticles was washed 3–4 times with deionized water to remove silver ions and seed extract residue. The precipitated nanoparticles were lyophilized. Lyophilized nanoparticles were stored in a cool, dry, and dark place and further their characterization was carried out.
Characterization of synthesized nanoparticles
UV-1800 Shimadzu spectrophotometer was used to obtain UV-visible spectra of AgNPs at different time intervals using seed extract diluted with water (1:9) as a blank. Further shape and size of formed nanoparticles were determined by SEM, FESEM equipped with EDS, and TEM. A lyophilized sample of AgNPs was subjected to Zeiss EVO-18 scanning electron microscope at 20 kV to study the morphological features of silver nanoparticles. Further, the shape, morphology, and elemental mapping of AgNPs were studied using field emission scanning electron microscopy (NOVA NanoSEM 450). For this purpose, the lyophilized sample was sonicated for a sufficient amount of time, the smear was made on a platinum grid, and allowed to dry overnight under vacuum. The grid was then coated with a thin film of palladium and finally subjected to FESEM. Transmission electron microscopy was done to exactly determine the size of nanoparticles. Sonicated sample was loaded on a carbon-coated copper grid and was allowed to dry overnight in a vacuum and subjected to transmission electron microscopy (FEI-TECNAI G220 TWIN). The crystalline nature of AgNPs was confirmed by XRD pattern obtained from Rigaku-MiniFlex 600 X-ray diffractometer at 2θ range from 0 to 100°. The sample for XRD measurement was prepared by casting the powder of silver nanoparticles on a glass slide and subsequently air-drying it under ambient conditions. The pattern was recorded by CuKα radiation with λ of 1.5406 Å at a voltage of 40 kV and current of 15 mA with a scan rate of 10°/min. Presence of functional groups present in AgNPs was determined by using FTIR (ALPHA BRUKER Eco-ATR). Four per centimeter resolution was taken in all spectra with 500–4000 cm−1 IR range.
Well diffusion method is commonly used to check the antimicrobial activity of the nanoparticles. The antimicrobial activity of synthesized AgNPs was checked using this method. Three microorganisms, namely E. coli, Bacillus cereus, and Staphylococcus aureus were used for this purpose. 1 mg/ml solution of AgNPs was made in Milli Q water and was sonicated properly. Overnight grown culture in Luria-Bertani broth of the mentioned microorganisms was taken and diluted to an optical density of 1. Diluted bacterial suspension (500 μl) was spread uniformly on three different Luria-Bertani agar plates for three different microorganisms. After spreading, two wells were cut on each plate using well borer of approximately 10 mm diameter. One well was filled with 50 μg and the other with 100 μg of AgNPs solution in all the three plates. The plates were incubated at 37 °C for 24 h, and the zone of inhibition was measured.
Determination of minimum inhibitory concentration (MIC)
Minimum inhibitory concentration is defined as the minimum concentration of the material that inhibits the growth of the particular microorganisms. The method is based on growing microorganisms at varying concentrations of AgNPs in suspension. Sterile test tubes, containing 5 ml of Luria-Bertani broth were taken. In the test tubes, varying concentrations of AgNPs were added and one test tube was taken as control. Then, the test tubes including the control were inoculated with an equal volume (200 μl) of freshly prepared bacterial suspension diluted to an optical density of 0.5. The inoculated test tubes were incubated in a shaker incubator at 250 rpm and 37 °C for 24 h. The next day, absorbance was taken using UV-visible spectrophotometer at 600 nm, and the graph was plotted against optical density and the concentration of AgNPs. The concentration giving the least optical density corresponds to MIC of silver nanoparticles for that particular microorganism. The above method is repeated with all the three microorganisms, namely E. coli, Bacillus cereus, and Staphylococcus aureus.
Determination of the effect of AgNPs on leakage of membrane
In this leakage of reducing sugars and proteins through the membrane was determined. For this, overnight grown cultures of E. coli, Bacillus cereus, and Staphylococcus aureus were taken, and 2 ml sample was withdrawn from each culture and was marked as 0 h sample. One milliliter of AgNPs solution (1 mg/ml) was added to each culture and was incubated at 200 rpm and 37 °C. Now, the sample was withdrawn after 2 h, 4 h, and 6 h from each culture. All the samples were centrifuged at 10,000 rpm for 5 min. Pellet was discarded and the supernatant was preserved at − 30 °C immediately, and the concentration of reducing sugar and proteins were determined by DNS and Bradford’s method, respectively, as soon as possible.
Results and discussion
Antimicrobial activity of AgNPs
Diameter of zone of inhibition (mm)
Concentration of AgNPs
MIC results are in relation to the fact that a larger zone of inhibition corresponds to smaller minimum inhibitory concentration (Mohanty et al. 2010).
The maximum amount of sugars and proteins is released by E. coli (112.86 and 12.9 μg/ml, respectively) when treated with AgNPs. Whereas, the least amount is released by B. cereus.
In conclusion, a simple, safe, and one-step process is utilized for the synthesis of silver nanoparticles by using the Tectona grandis seed extract. Seed extracts act as a reducing agent for nanoparticles synthesis. No chemical reagent or surfactant template is required in the process, which consequently established the bioprocess with the advantage of being environmentally friendly. TEM analysis revealed that nanoparticles were in the range of 10–30 nm and spherical. SAED and XRD pattern confirmed the crystalline nature of AgNPs. Synthesized nanoparticles showed antimicrobial activity which was investigated by agar well diffusion method against B. cereus, S. aureus, and E. coli. Minimum inhibitory concentration against these pathogens was determined by the broth dilution method which was found to be 5.2, 2.6, and 2.0 μg/ml for B. cereus, S. aureus, and E. coli, respectively. MIC results were in accordance with the zone of inhibition, i.e., more zone of inhibition less MIC value and vice-versa. Mechanism of action of antimicrobial activity was found to be the change in permeability of membrane by detecting the release of reducing sugars and proteins through leaky membrane, which was detected by DNS and Bradford’s method, respectively.
We thank Central Instrument Facility, IIT-BHU for providing us the necessary instrumentation facilities. We are grateful to the Ministry of Human Resource and Development (MHRD), India for financial aid.
Availability of data and materials
Data sharing is not applicable. It will be shared if needed.
This submitted work has not been published previously (except in the form of an abstract, and an academic thesis), and is not under consideration for publication elsewhere, it’s publication is approved by all authors and tacitly or explicitly by the responsible authorities where the work was carried out, and if accepted, it will not be published elsewhere in the same form, in English or in any other language, including electronically without the written consent of the copyright holder. The authors declare that they have no competing interests.
AR carried out all the experiments mentioned in the manuscript as this was his M.Tech dissertation work. JR helped to draft the manuscript. MD is the Senior Professor and was the supervisor of the dissertation work. All authors read and approved the final manuscript.
The authors declare that they have no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
- Asthana A, et al. Silver Nanoparticle Entrapped Calcium-Alginate Beads for Fe (II) Removal via Adsorption. in Macromolecular Symposia: Wiley Online Library; 2016.Google Scholar
- Guzmán MG, Dille J, Godet S. Synthesis of silver nanoparticles by chemical reduction method and their antibacterial activity. Int J Chem Biomol Eng. 2009;2(3):104–11.Google Scholar
- Indira E, Mohanadas K. Intrinsic and extrinsic factors affecting pollination and fruit productivity in teak (Tectona grandis Linn. f.). Indian J Genet Plant Breeding. 2002;62(3):208–14.Google Scholar
- Krishna MS, Jayakumaran N. Antibacterial, cytotoxic and antioxidant potential of different extracts from leaf, bark and wood of Tectona grandis. Int J Pharm Sci Res. 2010;2:155–8.Google Scholar
- Mohanty A, et al. Physico-chemical and antimicrobial study of polyherbal formulation. Int J Comprehensive Pharm. 2010;1(4):1–3.Google Scholar
- Natarajan K, Selvaraj S, Murty VR. Microbial production of silver nanoparticles. Dig J Nanomater Biostruct. 2010;5(1):135–40.Google Scholar
- Sastry M, et al. Biosynthesis of metal nanoparticles using fungi and actinomycete. Curr Sci. 2003;85(2):162–70.Google Scholar
Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.