A technical study of the materials and manufacturing process used in the Gallery wall paintings from the Jokhang temple, Tibet
- 197 Downloads
Wall paintings from the Jokhang temple, Lhasa, Tibet, China cover over 4000 m2. In order to protect these valuable paintings and to provide more conclusive information regarding the date of the painting scheme from the outer north Gallery, painting materials and techniques have been studied using optical and scanning electron microscopy, X-ray diffraction and raman spectroscopy. Organic materials were analysed with pyrolysis-gas chromatography–mass spectrometry. The wall painting technique is typical of Tibetan paintings and includes multiple layers of locally sourced materials. Analytical results demonstrate the presence of natural and synthetic pigments, including cinnabar (HgS), malachite (CuCO3·Cu(OH)2), azurite (2CuCO3·Cu(OH)2), orpiment (As2S3), red lead (Pb3O4), synthetic ultramarine blue (Na3CaAl3Si3O12S) and emerald green (Cu(C2H3O2)2·3Cu(AsO2)2) which allow us to date the paintings from the mid to late nineteenth century. The binding media is a kind of animal glue which is likely to be bovine or yak glue, the traditional medium used in Tibet. Gilding was applied as gold powder or gold foil. In the past a sealing material or varnish containing drying oil (maybe tung oil) and pine resin was applied to the surface to protect the paintings.
KeywordsTibet Jokhang temple Wall painting Pigment Binding media
The Jokhang temple, also known as “Zula Kang” is located in the old city center of Lhasa. It has been the most important Tibetan Buddhist monastery since it was built in 647 C.E. (Tang Dynasty) by Songzain Gambo (the first king of Tubo Dynasty). Today, with an area of 25.1 thousand square meters, it is dedicated to Buddha, Bodhisattva, deities, patriarchs, and Dharma gods of Bonpo, Nyingma, Sakya, Kagyu and Gelug sects of Tibetan Buddhism [1, 2]. In 1961 the Jokhang temple was listed as a State-level key heritage site of China and included in the UNESCO World Heritage List in 2000.
There are relatively few published studies on wall paintings from Tibet, and most research has focused on the history, iconography, techniques of painting, and religious and aesthetic value of depictions. Limited research has focused on the constituent of materials and techniques of Tibetan wall paintings. For example, Xiang studied the contents, characters and the iconography of the wall paintings from the Gallery of Jokhang temple ; others have studied the compositions of pigment, plaster layer and base layer of wall paintings samples from Jokhang temple [21, 22, 23]. The pigments present in the wall paintings from the Potala Palace, Norbulingka and Sakya Monastery have also been reported . Data from these studies suggest that Tibetan murals have unique national characteristics in terms of their build-up or stratigraphy and the methods employed for their execution.
However, there is little literature about the varnishes and surface finishes which were routinely applied to the paintings and the binding media employed in Tibetan wall paintings. This work aims to study the techniques, pigments, binding media and varnish materials from fragments collected as part of conservation work carried out by CACH on the outside Gallery.
According to the records in “History of the Jokhang Temple”’: in 1783, the Dalai Lama VIII (1758–1804) invited painters to draw the wall paintings on the outside Gallery and courtyard . Thus, wall paintings on the outside gallery were likely firstly executed in the late eighteenth or early nineteenth century. However the paintings have been extensively repaired and repainted, so the exact date of the scheme is unknown. A multi-analytical approach was chosen for the analysis of samples based on published methods used for the study of wall paintings [25, 26, 27, 28, 29, 30, 31, 32, 33]. Cross-sections were prepared and studied using optical microscopy, Raman spectroscopy, and scanning electron microscopy–energy dispersive x-ray spectroscopy. Fragments were also analysed by X-ray diffraction for a complete characterisation of the ground materials. Binding media and varnish analysis was carried out with pyrolysis gas chromatography–mass spectrometry.
Optical microscopy was carried out using a Leica DM4000 M (Germany) and samples were observed under various magnifications. The stereo microscopy was carried out using a Keyence VHX-900 (Japan) and samples were observed under various magnifications.
Scanning electron microscopy (SEM) was carried out using ZEISS EVO18, equipped with a SmartSEM system for data collection. Sample cross-sections were coated with gold prior to analysis. The range of magnification is 5–106×. Focused working distance is 2–145 mm. The excitation voltage is 20 kV, and scanning time is 60 s. Energy spectrum analysis was carried using Bruker Nano XFlash Detector 5010 Energy Spectrometer (EDS).
Raman spectroscopy was carried out on cross-sections with a HORIBA (JY Company, France) instrument equipped with Olympus BX-41 microscope at 50×. The grating is 1200T (line/mm). The spectrometer is calibrated by monocrystalline silicon. The laser wavelengths employed were 532 and 785 nm, with an acquisition time of 20–30 s, and 4–6 acquisitions per spectrum. Red, yellow and black pigments were analysed with the 785 nm laser. While blue, green and white pigments were tested with 532 nm. The power on samples was kept as low as possible with suitable data achievable with powers of 2–3 mW.
Small samples of the fragments and powder collected on site and local soil samples were subjected to X-ray diffraction (XRD). A TTRIII (Rigaku, Japan) X-ray diffractometer was used for analysis. The X-ray emitter maximum output power is 18 kw, tube voltage is 20–60 kV, tube current is 10–30 mA, target is Cu, and focus size is 0.5 mm × 10 mm. Measurement range is 10° ≤ 2θ ≤ 80°, with a scanning speed of 10°/min.
Microsamples were analysed by pyrolysis-gas chromatography–mass spectrometry (Py-GC/MS). For the analysis 0.2 mg sample was ground into powder and placed into a thermal cracking sample cup. 3 μL TMAH solution (four methyl ammonium hydroxide, 25%) was added in the cup and put it for an hour to make them fully dissolved. Samples were then dried prior to analysis using a Thermal cracking apparatus (PY-3030D, Frontier Lab, Japan), GC/MS (QP2010Ultra, Shimadzu, Japan), Chromatographic column UA+-5 (Frontier Lab, stationary phase is 5% 2-methyl-2-phenyl-polysiloxane). The parameters for analysis were set as follows: the pyrolysis was performed at 600 °C for 10 s; the pyrolysis interface: 300 °C; injector: 250 °C; the oven temperature was set 40 °C for 5 min, then up to 280 °C at rate 10 °C/min, hold for 20 min.
All samples were taken from damaged parts or fragments that had fallen off. The samples, including three larger fragments and some smaller fragments and powder samples, were all taken from the outside Gallery of Jokhang temple.
Some paint samples were observed directly under the optical microscope and examined by Raman spectroscopy. Local soil samples were ground into powder and analysed by XRD. The ground layer (including coarse clay layer and fine clay layer) were scraped from the samples and ground into powder which was analysed by XRD. Other samples were prepared as cross-sections using an epoxy resin and polished before examination.
Results and discussion
Stratigraphy of the wall paintings
The flagstone wall.
The wall in the Jokhang temple is made of flagstones and is the basic support of the wall painting. Because the buildings are old, some walls have deformed and have shrunk under the influence of external environment. Thus, structural problems in the walls are one of the main factors leading to the loss of wall paintings.
The ground layer.
The ground is divided into three layers. The bottom is the Ba-ga soil, with coarse particles and mostly sandy loam, with a sand content not more than 12%. The middle layer is made of thin loess, in which some flexible materials (such as straw and gaunt) are generally added to reinforce and increase the flexibility of the layer. The last layer is Ang-ba soil, which has a fine particle size. However, only the highest grade wall paintings have so many ground layers, and may do not contain the Ang-ba layer. Since the stones on the flagstone wall are uneven, the ground layer varies in thickness from about 5 to 1 cm.
The preparation layer.
According to the local monks, the preparation layer is made of a local Yang-ga soil and is a very thin gray/white layer. Analytical results identify the main component of the white powder layer of the samples as magnesite (magnesium carbonate).
The paint layers.The color of the Jokhang temple mural is very rich. Blue, red, yellow, green and gold are mostly used and constitute the main thematic colors. The paintings are executed with meticulous painting with exact delineation (see Fig. 3a). In addition to the main painting scheme, there are two specific styles in the wall paintings: paint on a black background with gold lines (Fig. 3b), and paint on the gold-silver powder background in black (Fig. 3c). Traditionally, when painting, mineral pigments are ground into powder and a glue solution is added to make a liquid paint. After the color has been adjusted, the painter will use the paint to draw. The process of Tibetan wall painting is very strict and is described in detail elsewhere [10, 34, 35].
Technical study of three fragments
The ground layer is thick and is usually divided into two parts: next to the white layer is a thin layer of loess with fine clay particles tightly connected and distribute uniformly; below the fine layer is a coarse mud layer with larger clay particles mixed with different sizes of sand and small stones. The main components of the coarse ground layer were identified by XRD to be quartz, albite and microcline, and the main components of the fine layer are quartz, albite, microcline and calcite. The major components of the coarse and fine layers are almost the same, thus it is likely that the same kind of clay was used. The local Ba-ga soil, Ang-ba soil and loess soil were sampled and tested by XRD which revealed the main components of these soils are all quartz, calcite and albite, and are basically the same as those of coarse layer, fine layer and Ang-ba layers of the wall painting samples.
In some samples the blue pigment is found mixed with the green pigment (Fig. 6e), and the orange pigment contains red and yellow particles (Fig. 6f). As noted by Dambar , traditional Tibetan wall paintings mainly use white, yellow, red, blue and green pigments either on their own or mixed to create different tones as observed in the samples studied as part of this work.
Binding media and varnish in the samples were determined by THM-Py-GC/MS. The results (see Additional file 3) showed that fatty acid (especially high content of azelaic acid), oxidation products of tung oil after heat treatment, pyrolysis products of rosin resin and maker compounds of protein, were all detected in the samples. Therefore, it is likely that the varnish contains a mixture of drying oil (maybe tung oil) and rosin resin, while the binding media is a kind of animal glue which is likely used as the binding medium for the paint and preparatory layers. According to the literature and field interviews with local painters, today Tibetan painters generally use bovine glue as binding medium, which is similar to the medium identified by THM-Py-GC/MS. Thus, the animal glue used in the wall paintings of Jokhang temple is very likely to be bovine (or yak) glue.
There is no surface protective material on the wall paintings of Tubo Period (sixth century C.E.). However, after the fifth Dalai Lama, materials were used to protect the surface of the wall paintings. The materials can increase the gloss of the surface and can prevent the loss of pigment caused by repeated touching from thousands of believers. The traditional Tibetan protective materials (such as egg white, oils, etc.) are occasionally mentioned in local treatises. However, the recipes have not been written in detail and have been lost. Since 13th Dalai Lama Period, Tibetan painters have begun to use natural protective varnishes with imported resins, which were replaced by alkyd resin varnishes during the 1970s according to accounts of local painters. Tung oil and rosin resin were detected in samples of the varnish, both of which can be dissolved in turpentine, but it is not possible to date the application of the varnish due to the use of the same materials by painters today.
Implications for dating
The pigments used on Jokhang temple wall paintings are mainly natural mineral pigments, such as ochre, red lead, cinnabar, malachite, azurite, orpiment and magnesite. These pigments are all traditional pigments which are often used by Tibetan artists [21, 22, 23, 24]. It is noted that the same mineral can show a variety of colors by different degree of grinding or different processing methods, and that malachite and azurite are often found together, as observed in cross-sections.
In addition to traditional mineral pigments, synthetic pigments, such as Paris green and artificial ultramarine are also detected. These two synthetic pigments were produced in Europe in early nineteenth century. Subsequently, they began to enter China and were identified on many paintings, architectural painting and temple murals of the late Qing Dynasty. For example, Paris green has been found in the pigments of a late Qing Dynasty Taoist portraits , the architectural painting of Zhendu gate in the Imperial Palace  and the Qing Dynasty wall painting in the Potala Palace and Drepung Monastery [41, 42]. The use of artificial ultramarine is more extensive than Paris green. In China, many paintings from the late Qing Dynasty were executed in artificial ultramarine. For example, most murals and painted sculptures of Qing Dynasty in Dun Huang grotto used artificial ultramarine . Because Paris green and artificial ultramarine were also found in the samples of Jokhang temple, it is concluded that the wall paintings in the outside galley of Jokhang temple have been repaired and repainted in late Qing Dynasty, thus during the mid-nineteenth century or later.
Combining site investigations with sampling analysis, the materials and production process of Jokhang temple wall paintings have been studied. The results show that most pigments used in the wall paintings are natural mineral pigments, such as cinnabar, azurite, malachite green, dark blue, red lead and orpiment. At the same time, some synthetic pigments, such as emerald green and artificial ultramarine are also found, indicating that the wall paintings have been repaired or repainted more recently (maybe in mid or late nineteenth century). In addition to natural mineral and artificial pigments, gold powder and gold foil were also used widely in the wall paintings. The wall paintings are made with Tibetan traditional craft and contain multiple ground layers, white preparation layer, paint layer and a thick surface varnish which contained drying oil (maybe tung oil) and pine resin. The binding media used in the paint is a kind of animal glue which is likely to be bovine/yak glue according to the tradition of Tibet. While the conservation of the wall paintings requires careful monitoring of the condition of the polychromy surface, the main causes of damage are human beings who touch the surfaces, and the failure of the building fabric, which requires routine inspection and regular maintenance. Efforts should thus be focused on preventive measures to ensure the long-term conservation of these important paintings.
YS contributed to sample and data analysis, interpretation and manuscript writing. AN was involved in the sample analysis and manuscript revision. FG, XZ, JG and QL were involved in the initial concept of the experiments and collected the data used in this paper. SW supplied the results of Py-GC/MS. All authors read and approved the final manuscript.
The authors would like to thank the Jokhang temple Management Committee for supplying the wall painting samples and historical background. The authors also acknowledge Dr. Qinglin Ma for his good advice in paper writing, and Dr. Bo Xiao for the technical help of THM-Py-GC/MS.
The authors declare that they have no competing interests.
Availability of data and materials
Ethics approval and consent to participate
The paper presented is the work made by our independent research. All data cited in the paper were from publicly available datasets and published literatures. In addition to the content of particular references, this paper does not contain any work that has been published or written by any other individual or group. Individuals, who have made important contributions to the study of this paper, have been clearly demonstrated in the acknowledgements.
This research was supported by “Basic research funds of Chinese Academy of Cultural Heritage”. Award Number: 2016-JBKY-13. Grant Recipient: Yan Song.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
- 1.Fu CL. History of Lhasa. Beijing: China Social Sciences Press; 1994 (in Chinese).Google Scholar
- 2.Cultural Relics management committee of Tibet autonomous region, Lhasa cultural relics, Xianyang: Xianyang printing plant. 1985 (in Chinese). Google Scholar
- 3.Sonam. The biography of the king of Tibet. Beijing: The Ethnic Publishing House; 2000 (in Chinese).Google Scholar
- 4.Ngawang Lobsang Gyatso. The fifth Dalai Lama biography. Beijing: China Tibetology Press; 2006 (in Chinese).Google Scholar
- 5.Lobsang TuDan. The Eighth Dalai Lama biography. Beijing: China Tibetology Press; 2006 (in Chinese).Google Scholar
- 6.Dai ZM. Wishful rattan: Sakyamuni Biography. Chengdu: SiChuan Ethnic Publishing House; 1998 (in Chinese).Google Scholar
- 7.Tinley. Tibetan customs. Lhasa: The Tibet people’s Publishing House; 2007 (in Chinese).Google Scholar
- 8.Su B. Archaeology of Tibetan buddhist monastery. Beijing: Cultural Relics Press; 1996 (in Chinese).Google Scholar
- 9.Yang CB. Jokhang temple resplendent on the roof of the world. China’s Tibet. 1994;6:11–2 (in Chinese).Google Scholar
- 10.Wang Y, Chen QY. Tibetan history and culture dictionary. Lhasa: The Tibet People’s Publishing House; 1998 (in Chinese).Google Scholar
- 11.Sonan. The biography of Tibetan king’s servants. Lhasa: Tibet People’s Publishing House; 1985 (in Chinese).Google Scholar
- 12.Lhasa literature and history group. History of the Jokhang temple. Tibet Res. 1981;00:36–50 (in Chinese).Google Scholar
- 13.Jackson D. History of Tibetan painting. Lhasa: Tibet people’s Publishing House; 2001 (in Chinese).Google Scholar
- 14.Zhang YS. History of Tibetan art. Beijing: Central University for Nationalities Press; 2006 (in Chinese).Google Scholar
- 15.Gozengdan. Tibetan unique art. Lanzhou: Gansu National Publishing House; 2001 (in Chinese).Google Scholar
- 16.Ye XS. Mural painting of Tibet Jokhang temple. Collections. 2010;1:116–9 (in Chinese).Google Scholar
- 17.Tucci G. Tibet, land of snows. London: Oxford & IBH Publishing Co.; 1967.Google Scholar
- 19.Singh AK. Trans-Himalayan wall paintings: 10th to 13th century AD. Delhi: Agam Kala Prakashan; 1985.Google Scholar
- 20.Xiang JT. Study of the murals on the Jokhang temple pilgrimage-corridor walls, Doctoral Dissertation of Minzu University of China. 2007. (in Chinese).Google Scholar
- 21.Wang LL, Li ZM, Zhang XT, et al. Studies on wall painting techniques at Jokhang temple, Lhasa, Tibet, China. Sci Conserv Archaeol. 2014;26(4):84–92 (in Chinese).Google Scholar
- 22.Li ZM, Wang LL, Zhang XT, et al. Study on field analysis of mural pigments by portable x-ray fluorescence: to the Jokhang temple murals as an example. China Cult Heritage Sci Res. 2013;4:64–7 (in Chinese).Google Scholar
- 23.Wang Y, Zhang XT, Wu N. Raman spectroscopic analysis of wall painting pigments at Jokhang temple, Lhasa, Tibet, China. J Light Scatt. 2017;29(1):39–43 (in Chinese).Google Scholar
- 24.Wang WF, Ma ZF, Yu ZR. An analysis on the materials of murals in Potala Palace, Norbuglinkha and Sakya Monastery, Tibetan. Dunhuang Res. 2002;6:78–84 (in Chinese).Google Scholar
- 25.Yu ZR, Zhao LY, Li YF. Analysis of the paint of the Horseshoe temple, TianTiShan and BingLing temple. Dunhuang Res. 2005;4:67–70 (in Chinese).Google Scholar
- 26.Chen GL. Analysis of pigments and clay of the polychrome statue and wall paintings in the No. 9 Tiantishan Grotto. Sci Conserv Archaeol. 2010;22(4):91–6 (in Chinese).Google Scholar
- 27.Wang XQ, Wang CS, Yang JL. Analysis of wall painting pigments in Fenghui tomb using HREM and Raman spectroscopy. J Instrum Anal. 2004;23(3):1–4 (in Chinese).Google Scholar
- 28.Zhang SX, Zhu J, Wang CS. The wall-painting pigments in A-Er-Zhai of Inner-Mongolia were analyzed by Raman microscopy. Relics South. 2009;1:109–12 (in Chinese).Google Scholar
- 29.Wang JY, Wang M, Liu L. Raman spectroscopy in archaeology. Chin J Light Scatt. 2006;18(2):130 (in Chinese).Google Scholar
- 30.Xia Y, Guo H, Wang JH. A study of the mural pigments of A-er-zhai Grottos, Inner Mongolia. Sci Conserv Archaeol. 2007;19(2):41–6 (in Chinese).Google Scholar
- 34.Yu XD. History of Tibetan Buddhist Painting. Nanjing: Jiangsu Arts Publishing House; 2006 (in Chinese).Google Scholar
- 35.Kelsang Yeshi. Tibetan art history. Chengdu: Sichuan National Publishing House; 2005 (in Chinese).Google Scholar
- 36.Dambar. A brief history of Tibetan art. Lhasa: The Tibet people’s Publishing House. 2003. (in Chinese).Google Scholar
- 39.He QJ, Li T, Shi JL. Non-destructive in situ characterization of pigments on a portrait of Chinese Taoism figure. Sci Conserv Archaeol. 2010;03(22):61–8 (in Chinese).Google Scholar
- 41.Xia Y. Exploring Chinese historical pigments by optical microscopy. Relics Museol. 2009;6:342–6 (in Chinese).Google Scholar
- 42.Cheng XL, Yang Q. Micro-Raman spectroscopy study of three green pigments containing copper and arsenic. Sci Conserv Archaeol. 2015;27(3):84–9 (in Chinese).Google Scholar
- 43.Wang JY. Study of artificial ultramarine in Dunhuang grottoes. Dunhuang Res. 2010;1:76–81 (in Chinese).Google Scholar
Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated.