The bacterial community significantly promotes cast iron corrosion in reclaimed wastewater distribution systems
Currently, the effect of the bacterial community on cast iron corrosion process does not reach consensus. Moreover, some studies have produced contrasting results, suggesting that bacteria can either accelerate or inhibit corrosion.
The long-term effects of the bacterial community on cast iron corrosion in reclaimed wastewater distribution systems were investigated from both spatial (yellow layer vs. black layer) and temporal (1-year dynamic process) dimensions of the iron coupon-reclaimed wastewater microcosm using high-throughput sequencing and flow cytometry approaches. Cast iron coupons in the NONdisinfection and UVdisinfection reactors suffered more severe corrosion than did those in the NaClOdisinfection reactor. The bacterial community significantly promoted cast iron corrosion, which was quantified for the first time in the practical reclaimed wastewater and found to account for at least 30.5% ± 9.7% of the total weight loss. The partition of yellow and black layers of cast iron corrosion provided more accurate information on morphology and crystal structures for corrosion scales. The black layer was dense, and the particles looked fusiform, while the yellow layer was loose, and the particles were ellipse or spherical. Goethite was the predominant crystalline phase in black layers, while corrosion products mainly existed as an amorphous phase in yellow layers. The bacterial community compositions of black layers were distinctly separated from yellow layers regardless of disinfection methods. The NONdisinfection and UVdisinfection reactors had a more similar microbial composition and variation tendency for the same layer type than did the NaClOdisinfection reactor. Biofilm development can be divided into the initial start-up stage, mid-term development stage, and terminal stable stage. In total, 12 potential functional genera were selected to establish a cycle model for Fe, N, and S metabolism. Desulfovibrio was considered to accelerate the transfer of Fe0 to Fe2+ and speed up weight loss.
The long-term effect of disinfection processes on corrosion behaviors of cast iron in reclaimed wastewater distribution systems and the hidden mechanisms were deciphered for the first time. This study established a cycle model for Fe, N, and S metabolism that involved 12 functional genera and discovered the significant contribution of Desulfovibrio in promoting corrosion.
KeywordsCorrosion Reclaimed wastewater High-throughput sequencing Bacterial community Desulfovibrio
Drinking water distribution system
Extracellular polymeric substance
Sodium hypochlorite treated
Without disinfection treatment
Reclaimed wastewater distribution system
Wastewater reclamation and reuse is an effective way to relieve the dilemma of water resource shortages. Reclaimed wastewater can be used for irrigation, industrial consumption, and supplementation of ecological water, i.e., artificial wetlands and rivers. Cast iron pipes have been widely used in water distribution systems for more than 150 years because of their high mechanical strength and cost effectiveness . In contrast to the corrosion of drinking water distribution systems (DWDS), which has attracted the attention of many researchers due to its serious effect of “red water” or “colored water” on people’s daily life [2, 3, 4, 5, 6, 7], only a few studies have investigated corrosion in reclaimed wastewater distribution systems (RWDS). Reclaimed wastewater contains a much higher concentration of organic matter than does drinking water, which could result in the consumption of more disinfectants and promote the regrowth of more abundant and diverse bacteria . The above features of reclaimed wastewater might lead to more severe corrosion of cast iron pipes and to consequent pipeline burst, resulting in loss of reclaimed wastewater. Additionally, considering scientific issues, the corrosion mechanism in RWDS may be strikingly different from that in DWDS. Corrosion is a synergistic interaction among the metal surface, abiotic corrosion products, bacterial cells, and their metabolites . It can be affected by various factors, such as water quality, disinfection method, and microbial community structure . Alkalinity and calcium hardness have been found to inhibit corrosion . Among disinfectants, it is generally accepted that sodium hypochlorite and its residuals increase corrosion rates [11, 12].
Currently, the effect of microorganisms on the cast iron corrosion process has not reached consensus. Some studies have produced contrasting results, suggesting that microorganisms can either accelerate or inhibit corrosion . In general, the main bacterial species related to metal transformation in terrestrial and aquatic habitats are sulfate-reducing bacteria (SRBs), sulfur-oxidizing bacteria (SOBs), iron-oxidizing bacteria (IOBs), and iron-reducing bacteria (IRBs) . Numerous studies have investigated the impact of pure or artificially mixed culture bacteria on cast iron corrosion in water distribution pipelines. Sulfate-reducing bacteria are usually related to anaerobic iron corrosion , and artificially mixed cultures verified that the promotion of corrosion by SRBs can be diminished in the presence of Pseudomonas aeruginosa (denitrifying bacterium) . Sulfur-oxidizing bacteria are believed to accelerate corrosion because of their ability to produce acid . The presence of IOBs rapidly inhibited corrosion on cast iron coupons due to the formation of a passive layer in the early stage (approximately the first 20 days) and accelerated corrosion with the decrease in passive layer adhesion . Iron-reducing bacteria can enhance corrosion by the reduction of Fe3+ corrosion products, which are easily dissolved to expose the metal surface to the corrosive medium again. However, IRBs can also inhibit corrosion by developing biofilms at the metal surface and producing the extracellular polymeric substance (EPS) as a protective layer . It should be noted that in natural environments and engineered systems, microbial biofilms are always composed of multifarious bacteria and not merely a single bacterium or several types of bacteria. Therefore, the effect of the microbial community on cast iron corrosion has attracted increasing attention. Some researchers believe that the effect of biofilm on cast iron corrosion in RWDS changes over time. In a 30-day experiment, Teng et al.  verified that biofilm accelerated corrosion within 7 days but inhibited corrosion after 7 days. The major reason for this result was the abundance transition of IOBs and IRBs. Wang et al.  considered that corrosion-inducing bacteria, including the IRB Shewanella sp., the IOB Sediminibacterium sp., and the SOB Limnobacter thiooxidans, promoted iron corrosion by synergistic interactions in the primary period. Nevertheless, when IRBs became the dominant bacteria, they could prevent further corrosion via the formation of protective layers. Some studies have demonstrated that the existence of biofilm in reclaimed wastewater significantly promoted corrosion . However, it was suggested that biofilm could protect metal from corrosion by preventing the diffusion of oxygen . Other researchers did not reach a clear conclusion but rather speculated that bacterial communities could at least promote the layering process and the formation of corrosion tubercles .
Whether microbes inhibit or promote corrosion, their remarkable effect on corrosion has been affirmed, especially the impact of anaerobic bacteria existing close to the base of cast iron. Nevertheless, previous studies did not distinguish the anaerobic layer from the aerobic layer when investigating the effect of the microbial community on cast iron corrosion in RWDS. Furthermore, no information is available on the relationship between the dynamics of the bacterial community composition of different layers and the corrosion behaviors in RWDS over time, especially in the long term. With the rapid development of high-throughput sequencing technology, the dynamics of microbial community structure and its effect on corrosion could be disclosed with high resolution and high accuracy .
Considering the above research gaps, the questions that we wish to address in this study are summarized as follows. (i) Do different disinfection processes (NaClOdisinfection and UVdisinfection) affect the corrosion behaviors of cast iron in reclaimed wastewater in the long term compared to nondisinfection process (NONdisinfection)? (ii) Does the bacterial community promote or inhibit corrosion of cast iron? (iii) Are there some key bacterial species contributing to corrosion inhibition or promotion? (iv) How do functional microorganisms drive the iron element cycle in the interface microcosm of cast iron-reclaimed wastewater?
Laboratory-scale reactor setup
Three laboratory-scale reactors were set up to simulate RWDS (Additional file 1: Figure S1) and were placed in the dark to prevent the growth of phototrophic microorganisms at the Xili reclaimed wastewater plant (RWP) in Shenzhen, Guangdong Province, China. Xili RWP uses a BIOSTYR® biological active filter and an ACTIFLO® high-density settling basin (Veolia Water, France) as the main treatment process with a treatment capacity of 50,000 m3/d. NaClOdisinfection, UVdisinfection and NONdisinfection reclaimed wastewaters were pumped into the three reactors to compare the effect of disinfecting methods on the corrosion of cast iron coupons. Both NONdisinfection and NaClOdisinfection reclaimed wastewaters were collected from the secondary sedimentation tank effluent, and the latter was obtained by adding sodium hypochlorite (NaClO) with 5 mg/L free chlorine. The UVdisinfection reclaimed wastewater was collected from the UV disinfection tank directly. Three types of reclaimed wastewater were pumped into three 1000 L storage tanks and then discharged horizontally through the pipeline system at a rate of 0.2 m/s . Ductile cast iron coupons (QT450), with C (3.4 ~ 3.9%), Si (2.2 ~ 2.8%), Mn (< 0.5%), P (< 0.07%), S (< 0.03%), Mg (0.03 ~ 0.06%), and Re (0.02 ~ 0.04%) were used in this study. Prior to the experiment, the coupons were first rinsed with deionized water thrice, degreased with acetone, sterilized by immersion in 70% ethanol for 8 h, and then dried aseptically in a laminar flow cabinet. Finally, the coupons were exposed to UV light for 30 min before they were weighed . All water quality parameters were measured according to the standard methods  (see Additional file 1: Text S1). The detailed water quality of NaClOdisinfection, NONdisinfection, and UVdisinfection reclaimed wastewaters is summarized in Additional file 1: Table S1.
Sample collection and preparation
To investigate the diversity and dynamics of the bacterial community on cast iron coupons, samples were collected from three reactors weekly for the first month and then every 3 weeks for the next 11 months, with a total of 20 sampling times during the entire experimental period. Sampling time points are shown in Additional file 1: Table S2. All samples were transported to the laboratory within 2 h for subsequent pretreatment and analysis. All analyses were conducted within 24 h. To distinguish the effect of metabolic bacterial activity on corrosion under aerobic and anaerobic conditions, biofilms in cast iron coupons were divided into two layers according to their color (Additional file 1: Figure S2). The surface layer was aerobic and yellow, while the inner layer was anaerobic and black. To obtain sufficient biomass on different layers, four pieces of cast iron coupons were collected each time, the surface layer and inner layer of each piece were separately sampled, and the same layers were mixed together. The surface layer, namely, the yellow layer, was flushed slightly with ultrapure water and finally collected a total of 500 mL of suspension liquid. To detach bacteria from the inner layer, i.e., the black layer, the cast iron coupons on which the yellow layer had already been removed were treated by ultrasonic processing (42 kHz) three times for 5 min each, and a total of 500 mL of suspension liquid was obtained [24, 25]. The potential biases of bacterial viability and adenosine triphosphate (ATP) measurement resulting from ultrasonic processing were excluded based on the preliminary experiment (see Additional file 1: Text S2). Four milliliters of obtained suspension liquid was used for further adenosine triphosphate (ATP) measurement and flow cytometry cell counting, and the other 496 mL was used for DNA extraction. The corrosion rate was determined by the weight loss method [10, 22]. The corrosive cast iron coupons were lyophilized for 24 h and gently divided into yellow layer and black layer by a sterile metal spatula. The crystalline phase of the yellow layer and black layer was characterized using an X-ray powder diffractometer (XRD; RIGAKU D/max2500/PC, Japan). The micrograph of the cast iron corrosion scale was examined by scanning electron microscopy operating at 15.0 kV (SU8010, HITACHI, Japan). In addition, polarization curves were also measured by an electrochemical workstation (CHI750e, Chenhua, Shanghai, China).
Adenosine triphosphate measurement
To allow the bacteria to be adequately released from the iron rust, 0.25 mL of 0.5 mm glass beads was added into the suspension liquid obtained above. After a 60 s × 3 vortex pretreatment, supernatant was collected via centrifugation for 2 min at 600g  for ATP measurement using the BacTiter-Glo™ reagent (Promega Corporation, Madison, USA) and a luminometer (SpectraMax i3, Molecular Devices, USA) . The data were collected as relative light units and converted to ATP (nM) by a calibration curve established with a known rATP standard (Promega).
Flow cytometry measurement
To count viable/dead bacteria simultaneously, bacterial suspensions (1 mL) were stained with 10 μL/mL SYBR Green I (1:100 dilution in DMSO; Invitrogen) and 6 μM propidium iodide, which only stains damaged bacteria, and incubated in the dark for 25 min at room temperature before measurement. If necessary, samples were diluted to lower than 2 × 105 cells/mL by cell-free Milli-Q water before measurement. Flow cytometry measurement was performed using FACSCalibur (BD, USA), emitting at a fixed wavelength of 488 nm and volumetric counting hardware. The signals of SYBR Green I and propidium iodide were respectively collected in the FL1 channel (520 nm) and the FL3 channel (615 nm), all data were processed with BD CellQuest™ Pro, and electronic gating with the software was used to separate positive signals from noise [27, 28].
DNA extraction, PCR amplification, and Illumina sequencing
Microbial biomass was harvested from suspension liquid using 0.22 μm nitrocellulose membrane filters (47 mm diameter, Millipore, Billerica, MA, USA) . Genomic DNA from the biomass in the black layer and yellow layer was separately extracted using a FastDNA® SPIN Kit for soil (MP Biomedicals, France) following the manufacturer’s instructions. The concentration and purity of DNA were determined using a NanoDrop 2000 spectrophotometer (Thermo Fisher Scientific, USA). The extracted DNA was stored at − 20 °C for subsequent use. For PCR amplification, the hypervariable V4 region of the bacterial 16S rRNA gene was amplified using a forward primer (5′-TATGGTAATTGTGTGCCAGCMGCCGCGGTAA-3′) and reverse primer (5′-AGTCAGTCAGCCGGACTACHVGGGTWTCTAAT-3′). Barcode was added at the 5′ end of the forward and reverse primers to allow for sample multiplexing during sequencing , resulting in a fragment size of 333 bp that was sequenced in a paired ends fashion, with read length of 250 bp per read-mate. PCR solutions contained 25 μL of ExTaq™ premix (Takara, China), 2 μL of 10 μM forward and reverse primers, 1 μL of 20 ng/μL DNA, and 22 μL of RNA-free H2O. The thermocycling steps for PCR were set as follows: initial denaturation at 95 °C for 5 min; 28 cycles at 95 °C for 30 s, 55 °C for 30 s, and 72 °C for 1 min; and a final extension step at 72 °C for 5 min. PCR products were purified using the MiniBEST DNA Fragment Purification Kit Ver. 4.0 (Takara, Japan) and then visualized on an agarose gel. Purified PCR amplicons were quantified by NanoDrop 2000 and mixed to achieve equal mass concentrations for paired-end 250 bp sequencing on a HiSeq 2500 platform.
All the raw sequencing data of the 16S rRNA amplicons were processed in Mothur v. 1.39.5 . Briefly, sequences were first demultiplexed, quality trimmed, aligned, and finally checked with chimera.uchime to remove chimeric sequences, following the standard pipeline in the Mothur manual. Then, the clear sequences were normalized by randomly extracting 40,000 clean sequences from each sample dataset to fairly compare all samples at the same sequencing depth . Next, the normalized sequences from all samples were clustered into operational taxonomic units (OTUs) at an identity threshold of 97%, which approximately corresponds to the taxonomic levels of species for bacteria. OTUs with an abundance of less than 10 sequences were removed from the OTU table. Representative sequences of OTUs were extracted and submitted to the Ribosomal Database Project (RDP) Classifier for taxonomy annotation at an 80% threshold. The diversity index and evenness were calculated using PAST 3 . The taxonomic dendrogram was visualized by Cytoscape 3.6.0  to obtain an overall view of the bacterial community structure. All sample similarities and pairwise comparisons between different layers were computed as weighted UniFrac distances  and were visualized by principal coordinate analysis (PCoA) using “vegan” and “ggplot2” packages in R studio.
Results and discussion
Corrosion process and corrosion scale characterization under different disinfection conditions
Corrosion process monitoring
Polarization curves are frequently used to characterize electrochemical reactions at the metal/biofilm interface and the formation of corrosion and biofilms [15, 36]. In this study, the polarization curves (Additional file 1: Figure S3) of the corroded coupons in the corresponding water were measured to analyze the change in the corrosion current density. Corrosion current density did not exhibit significant discrepancy before the 19th week in the three reactors (P > 0.05, paired t test), while it was significantly higher in the NONdisinfection and UVdisinfection reactors than in the NaClOdisinfection reactor after the 19th week. The electrochemical results agreed with the weight loss results and confirmed that cast iron coupons suffered much more serious corrosion in the NONdisinfection and UVdisinfection reactors than did those in the NaClOdisinfection reactor in the mid-late experiment period.
Morphology and crystal structures of the corrosion scale
To decipher why the cast iron coupons in the UVdisinfection and NONdisinfection reactors suffered more serious corrosion than did those in the NaClOdisinfection reactor, water quality parameters, microbial quantity, microbial activity, and community composition were comprehensively analyzed. Among all the water quality parameters detected, the concentrations (or values) of TN, TP, TOC, hardness, soluble iron, and pH in the NaClOdisinfection, UVdisinfection, and NONdisinfection reactors were highly similar (Additional file 1: Table S1). However, the ORP, free chlorine and total chlorine concentrations in the NaClOdisinfection reactor were much higher than those in the UVdisinfection and NONdisinfection reactors due to the addition of NaClO (Additional file 1: Table S1). Oxidation-reduction potential, representing the oxidizing ability of water, was up to 473.2 ± 62.9 mv in the NaClOdisinfection reactor, which was much higher than that in the NONdisinfection (290.8 ± 87.1 mv) and UVdisinfection (282.0 ± 80.4 mv) reactors, respectively. Theoretical Eh (volts) values for Fe2+–γ-goethite couples, Fe2+–α-goethite couples, Fe2+–Fe3O4 couples, and Fe–Fe2+ couples were 88 mv, 274 mv, 314 mv, and 440 mv at circumneutral pH, respectively . These values were all less than the ORP of the NaClOdisinfection water. The existence of ClO− can promote the transition from Fe2+ to Fe3+ . In summary, greater ORP and the existence of ClO− were beneficial for oxidizing Fe2+ to Fe3+ and Fe–Fe2+, which could have caused more severe corrosion. Nevertheless, cast iron coupons in the NaClOdisinfection reactor after the 19th week exhibited weaker corrosion than did the coupons placed in the NONdisinfection and UVdisinfection reactors. Therefore, it seems that water parameters are not the main factors resulting in differences in corrosion behavior. Instead, microbial quantity, microbial activity, or community composition might be responsible for the corrosion difference.
Microbial quantity and activity under different disinfection conditions
A flow cytometer was used extensively to count the cell numbers due to its high accuracy [27, 28]. The amounts of live, dead, and total bacteria in the biofilm in black and yellow layers over time were measured separately in the present study. Dead bacteria in the yellow layers of the NaClOdisinfection, NONdisinfection and UVdisinfection reactors were always at a low quantity (1.33 × 105 ~ 1.29 × 107 cells/cm2) throughout the entire experimental period regardless of different disinfection method. Interestingly, the quantity of dead bacteria in the black layers of these three reactors was much higher than that in the corresponding yellow layers (Additional file 1: Figure S8a and d). At the beginning of the experiment (i.e., the first 4–7 weeks for the black layer and the first 10–13 weeks for the yellow layer), the live bacteria in the cast iron biofilm in the NONdisinfection and UVdisinfection reactors maintained a much more rapid growth rate than did those in the NaClOdisinfection reactor. During the initial 22 weeks, the quantity of live microbes in the black layer in the NONdisinfection and UVdisinfection reactors was also significantly higher than that in the NaClOdisinfection reactor (P < 0.01, paired t test). After the 22nd week, the quantity of viable microbes in the black layer in these three reactors reached the same level and maintained a relatively steady state throughout the whole experimental period (Additional file 1: Figure S8b). For the yellow layers, the quantity of live microbes was higher in the NONdisinfection and UVdisinfection reactors than in the NaClOdisinfection reactor for the initial 10 weeks instead of 22 weeks (P < 0.05, paired t test, Additional file 1: Figure S8e). The variation in the quantity of total microbial cells over time was similar to that of live microbial cells (Additional file 1: Figure S8c and f).
As shown in Additional file 1: Figure S9, the variation in ATP, which represents microbial activity [24, 27, 39], was highly consistent with the variation in the quantity of live bacteria (Additional file 1: Figure S8b, e). This phenomenon was quite reasonable because ATP reflected the microbial activity of the live cells.
Diversity and microbial community compositions
α-Diversity and β-diversity analyses
In total, 5719 OTUs remained after removing OTUs with an abundance of less than 10 sequences for all 120 samples. The OTU diversity index was expressed by the Chao1 index, Shannon index, and Simpson index (Additional file 1: Figure S10). Chao 1 indexes indicated that, compared to the corresponding black layers in three different reactors, yellow layers had significantly higher OTU richness throughout the entire experimental period (P < 0.01, paired t test, Additional file 1: Figure S10a). Similar to the Chao1 indexes, the Shannon indexes of the yellow layers were always significantly higher (P < 0.01, paired t test) than those of the corresponding black layers in the UVdisinfection and NONdisinfection reactors (Additional file 1: Figure S10b). However, for the NaClOdisinfection reactor, black layer samples underwent a drastic diversity increase from 1.78 to 4.37, and the Shannon indexes of the black layer samples began to surpass those of the yellow layer samples after the 10th week. In addition, the Simpson index (Additional file 1: Figure S10c) and Evenness index (Additional file 1: Figure S10d) shared the same trends except, for in the black layer in the NaClOdisinfection reactor, where these values suffered a drastic increase during the entire experiment.
It should be noted that both Shannon and Simpson indices of the NaClOdisinfection-B samples, especially the samples collected after the 7–10 weeks, exhibited higher values as compared to those of UVdisinfection-B and NONdisinfection-B samples. It is possible that the chlorination pressure exerted on bacteria in the NaClOdisinfection-B samples decreased with the increase of corrosion layer thickness because of less contact between bacteria and hypochlorite. This suggested that the NaClOdisinfection-B samples collected after the 7–10 weeks were under an intermediate pressure level caused by the attenuate chlorination. According to the classical intermediate disturbance hypothesis theory, diversity might reach maximum at intermediate levels of disturbance or pressure . In the present study, the attenuate NaClO disinfection for the NaClOdisinfection-B samples collected after the 7–10 weeks may act as intermediate disturbance.
A two-dimensional PCoA plot showed the bacterial community differences among the samples in the yellow layers and black layers under different disinfection methods. (Additional file 1: Figure S11). Samples of the black layer were distinctly separated from those of the yellow layer regardless of the disinfection method. One possible reason could be related to the oxygen availability, that is, the yellow layer belongs to the aerobic environment while the black layer might be anaerobic. In addition, compared to the NaClOdisinfection reactor, the NONdisinfection and UVdisinfection reactors had much more similar microbial compositions and variation tendencies over time for the same layer type. The dynamic change in the microbial community also followed a regular tendency and will be discussed in detail in subsection “Community temporal trajectories and identification of differential bacterial genera during biofilm development.”
Characterization of microbial community compositions
As shown in Additional file 1: Figure S12, Proteobacteria was the most abundant phylum in all the samples collected from both the yellow layers and black layers, accounting for 53.8 ~ 94.2% of the total bacterial community. This is consistent with the analytical results of the bacterial community in the cast iron corrosion scale of RWDS  and DWDS , in which Proteobacteria accounted for 56.7% and 64.0% on average. Another interesting phenomenon is that the relative abundance of Proteobacteria in black layers was significantly higher than that in the corresponding yellow layers under different disinfection conditions. In contrast to Proteobacteria, Acidobacteria is a dominant phylum without significant differences among NaClOdisinfection (black layer 4.55% ± 1.80%, yellow layer 5.16% ± 2.17%), NONdisinfection (black layer 4.84% ± 2.08%, yellow layer 5.98% ± 1.46%), and UVdisinfection (black layer 4.59% ± 1.96%, yellow layer 5.67% ± 1.21%) reactors (P > 0.05, paired t test). The relative abundance of Bacteroidetes in the NaClOdisinfection reactor (black layer 5.87% ± 2.26%, yellow layer 8.22% ± 4.92%) was significantly (P < 0.01, paired t test) higher than that in the NONdisinfection (black layer 3.27% ± 2.11%, yellow layer 4.60% ± 2.22%) and UVdisinfection (black layer 3.27% ± 2.02%, yellow layer 4.65% ± 2.64%) reactors. Additionally, the relative abundance of Bacteroidetes decreased with time, especially in the NaClOdisinfection reactor. Bacteroidetes are known to produce EPS , which can act as a protective mechanism for bacteria in an adverse or stressful environment and contribute to the formation of biofilms. This should be the possible reason for the abundant Bacteroidetes in the NaClOdisinfection reactor due to the existence of chlorination oxidation stress. Nevertheless, according to the two-month preliminary experiment, we found that it was impracticable to measure the EPS content in the present study because the amount of EPS was not sufficient for the subsequent measurement of protein and polysaccharide, and thus, the contribution of EPS for biofilm formation is difficult to determine. Nitrospirae was much more abundant in the NONdisinfection yellow layer (5.75% ± 3.78%) and UVdisinfection yellow layer (5.93% ± 3.57%) than in the corresponding black layers (0.49% ± 0.31%; 0.58% ± 0.38%), which may be related to its aerobic property. Moreover, it seems that Nitrospirae should be very sensitive to chlorination disinfection because its relative abundance in the NaClOdisinfection yellow layer was much lower than that in the yellow layers of the NONdisinfection and UVdisinfection reactors. Similar to Nitrospirae, Actinobacteria was also much more abundant in the NONdisinfection yellow layer (2.15% ± 1.04%) and UVdisinfection yellow layer (2.32% ± 1.44%) than in the corresponding black layers (0.76% ± 0.38%; 0.78% ± 0.51%).
At the genus level, Additional file 1: Figure S13 shows the relative abundance distribution of the top 50 genera in all black and yellow samples. Azospira, Sediminibacterium, Geothrix, and Nitrospira presented notable differences between the yellow and black layers under different disinfection methods. These potential functional bacteria responsible for corrosion will be discussed in detail in subsection “Identification of crucial genera responsible for promoting cast iron corrosion and establishment of a cycle model for Fe, N and S metabolism.”
It should be noted that, the diversity in NaClOdisinfection-black layer illustrated in Additional file 1: Figure S12 seems like lower than that in the yellow layer, which is contrast to the Shannon and Simpson indices trend (Additional file 1: Figure S10). The apparent contradiction is explicable and reasonable because Shannon and Simpson indices were calculated based on OTUs (identity threshold of 97%) results, while Additional file 1: Figure S12 was presented at phylum level.
Abundant and persistent bacteria during the biofilm development process
Among the 390 OTUs in the black layer, 45 AP-type OTUs accounted for 85.0% ± 5.6% of the total bacterial abundance. One OTU, 52 OTUs, and 292 OTUs were classified as AI, RI, and RP, respectively. These 45 AP-type OTUs belonged mainly to the six phyla of Acidobacteria, Actinobacteria, Bacteroidetes, Nitrospirae, Ignavibacteriae, and Proteobacteria. Among the 742 OTUs screened in the yellow layer, 74 AP-type OTUs belonging to eight phyla accounted for 72.1% ± 11.0% of the total bacterial abundance. These AP-type OTUs were classified to 8 phyla, including the 6 phyla mentioned above and Planctomycetes and Verrucomicrobia. Except for AP-type OTUs, 6 OTUs, 93 OTUs, and 569 OTUs were classified into AI, RI, and RP types, respectively. It should be noted that there were no AT-type or RT-type OTUs in either the black or yellow layer samples.
Among the four classes of Proteobacteria, branches of β-Proteobacteria had 51% and 51.4% of AP-type OTUs, irrespective of being from black or yellow layer samples (red dots in Fig. 4). It is worth mentioning that in six out of eight OTUs belonging to Desulfovibrio, one type of well-known SRB genus  was AP-type OTU in the black layer. In the yellow layer, four OTUs derived from Nitrospira responsible for nitrite oxidizing were all AP-type OTUs. Other functional genera will be discussed in detail in subsection “Identification of crucial genera responsible for promoting cast iron corrosion and establishment of a cycle model for Fe, N and S metabolism.”
Community temporal trajectories and identification of differential bacterial genera during biofilm development
Community temporal trajectories and biofilm development stage divide
Identification of differential bacterial genera during biofilm development
During stage II, seven genera, i.e., Bradyrhizobium, Azospira, Sediminibacterium, Myxococcaceae, Desulfovibrio, Thermomonas, and Dechloromonas, differed significantly between the black layers in the NaClOdisinfection and NONdisinfection reactors (Fig. 6a). This was very similar to the comparison between the black layers in the NaClOdisinfection and UVdisinfection reactors, apart from the addition of Micrococcineae (Additional file 1: Figure S14a). For the yellow layer, 11 genera, including Bradyrhizobium, Sphingomonas, Novosphingobium, Dongia, Micrococcineae, Nitrospira, Sediminibacterium, Hyphomicrobium, Nitrosomonas, Undibacterium, and Geothrix, manifested significant differences between the NaClOdisinfection and NONdisinfection reactors (Fig. 6c). In addition to the above genera, Opitutus and Aquabacterium also exhibited significant differences between the NONdisinfection and UVdisinfection reactors (Additional file 1: Figure S14c). With an effect size ≥ 0.75 recommended by Parks et al. , no genus significantly differed between the NONdisinfection and UVdisinfection reactors, regardless of being from the black or yellow layers.
During stage III, ten genera, including Desulfovibrio, Dechloromonas, Nitrospira, Sediminibacterium, Terrimonas, Bradyrhizobium, Aquabacterium, Myxococcaceae, Geothrix, and Micrococcineae, differed significantly in the black layers between the NaClOdisinfection and NONdisinfection reactors (Fig. 6b). Except for Micrococcineae, the other nine genera differed significantly between the black layers in the NaClOdisinfection and UVdisinfection reactors (Additional file 1: Figure S14b). With regard to the comparison of the yellow layers in the NaClOdisinfection and NONdisinfection reactors (Fig. 6d), 11 genera, i.e., Bradyrhizobium, Hyphomicrobium, Corynebacterineae, Frankineae, Burkholderia, Pseudolabrys, Pirellula, Terrimonas, Sphingomonas, Undibacterium, and Sediminibacterium, showed distinct differences. However, 13 genera, including Bradyrhizobium, Nitrospira, Pirellula, Hyphomicrobium, Corynebacterineae, Gaiellaceae, Sediminibacterium, Sphingomonas, Melioribacter, Burkholderia, Frankineae, Terrimonas, and Undibacterium, displayed statistically significant differences between the NaClOdisinfection and UVdisinfection reactors (Additional file 1: Figure S14d). Two group tests between the NONdisinfection and UVdisinfection reactors indicated that only one genus displayed a significant difference, i.e., Azospira corresponding to the black layer and Frankineae corresponding to the yellow layer.
Identification of crucial genera responsible for promoting cast iron corrosion and establishment of a cycle model for Fe, N and S metabolism
IOBs and IRBs
The total relative abundance of IOBs, i.e., Azospira, Aquabacterium, Geobacter, and Sediminibacterium, increased distinctly in all black layers over time and decreased in yellow layers (Additional file 1: Figure S15a). Azospira is able to oxidize iron (II) using nitrate as an electron acceptor instead of oxygen . The decrease in the total relative abundance of IOBs in the yellow layer was caused by Sediminibacterium, which suffered a gradual reduction in all yellow layer samples regardless of disinfection method (Additional file 1: Figure S15e). Sediminibacterium is always isolated from sediment and activated sludge . It tends to grow under aggregation conditions to protect bacteria against oxidative stress , and this aggregation property may be responsible for its high relative abundance in the initial stage due to contributing to the formation of biofilms. The decreased relative abundance of Sediminibacterium over time may be caused by an increasingly complex microbial community structure, which leads to fiercer interspecific competition. Geobacter was found to be the first microorganism with the ability to oxidize organic compounds and metals, including iron. One Geobacter species, Geobacter metallireducens, has the ability to oxidize Fe(II) using nitrate as electron acceptor and generate ammonium , which demonstrated that nitrite (NO2−) and nitrogen gas (N2) were not the sole end products of nitrate reduction. In the present study, the relative abundance of Geobacter remained less than 0.2% before the 25th week and then increased unstably (Additional file 1: Figure S15f). Geothrix, as an IRB [51, 52], was widespread in any layer and fluctuated slightly during the entire experimental period (Additional file 1: Figure S15b).
NOBs and NRBs
Nitrite-oxidizing bacteria, such as Nitrospira, carried out two obvious ascend phases in the yellow layers of the NONdisinfection and UVdisinfection reactors (Additional file 1: Figure S15c), while the relative abundance of NOBs in the yellow layer of the NaClOdisinfection reactor remained relatively stable before the 31st week and then increased continuously. Nitrate-reducing bacteria spread across multiple prokaryotic phyla with diverse physiologies . Five genera belonging to NRBs with significant relative abundance differences were filtered out by STAMP analysis. The total relative abundance did not significantly differ in the three reactors regardless of the black or yellow layers (Additional file 1: Figure S15d).
Where WLNON represents the weight loss of the cast iron coupon in the NONdisinfection reactor, WLNaClO represents the weight loss of the cast iron coupon in the NaClOdisinfection reactor and WO represents the original weight of the cast iron coupon.
Cycle model for Fe, N, and S metabolism
Nitrate-dependent IRBs, such as Geobacter, Sediminibacterium, and Azospira, can oxidize Fe2+ to Fe3+ accompanied by the reduction of nitrate to nitrite [38, 49], and then, the nitrite is oxidized by NOBs to generate nitrate. Iron-reducing bacteria, such as Geothrix, can reduce Fe3+ to Fe2+. Iron-oxidizing bacteria/NRB, IOBs/NRBs, IRBs, and NOBs constituted a cycle model for Fe, N, and S metabolism (Fig. 7b) to drive the transition between NO3− and NO2–, Fe2+, and Fe3+. The redox transition between Fe2+ and Fe3+ did not contribute to the weight loss, while only the dissolution of Fe to Fe2+ increased the weight loss. Oxygen can be used as an electron acceptor to oxidize Fe to Fe2+ by galvanic effect, which was the primary pathway to dissolve Fe in the initial experimental stage in all three reactors. However, the ability of oxygen penetration was limited by the increased corrosion layer thickness. Our previous study found that oxygen was blocked effectively, and anaerobic conditions could be created when the corrosion layer thickness of cast iron was greater than ~ 8 mm . When the corrosive layer blocked oxygen penetration, it also created an appropriate environment for anaerobic bacteria at the same time. Sulfate-reducing bacteria are anaerobic , and their survival depends on the corrosion layer, which prevents oxygen from entering. The corrosion layer was thinner in the NaClOdisinfection reactor (Additional file 1: Figure S2a) than in the NONdisinfection reactor (Additional file 1: Figure S2b). The thinner corrosion layer was insufficient to inhibit oxygen definitely; thus, only a few Desulfovibrio could survive in the black layer, which resulted in slight or negligible microbiology-induced corrosion. NaClO could oxidize Fe2+ to Fe3+ in the NaClOdisinfection reactor. Even if the relative abundance of IOBs in the NaClOdisinfection reactor was lower than that in the NONdisinfection and UVdisinfection reactors in the initial stage, the reaction of Fe2+ to Fe3+ also existed in the corrosion scale of the NaClOdisinfection reactor (Fig. 3 and Additional file 1: Figure S6). Overall, although the disinfection of NaClO theoretically enhanced the electrochemical corrosion of cast iron, it inhibited the microbiology-induced corrosion simultaneously by influencing the thickness of the corrosion layer and different microbiology compositions.
Nevertheless, this circle model mainly takes into account some bacteria with known functions related to Fe, N, and S metabolism and possessing significant relative abundance differences between the NaClOdisinfection and NONdisinfection reactors. In addition, a large portion of the effective bacterial sequences in this study could not be assigned to the genus level. Overall, it is not sufficient to construct the above conceptual model and predicate the effect of SRBs based on 16S rRNA gene annotation results alone. If a more accurate mechanism hypothesis is established, it is suggested to confirm the gene abundance variation and expression levels involving Fe, N, and S metabolisms using metagenomics and metatranscriptomics approaches. Moreover, the protection function of EPS which might play a possible role in inhibiting corrosion should also be considered in the future study.
The long-term effect of disinfection processes on the corrosion behaviors of cast iron in RWDS and the related hidden mechanisms were deciphered in the present study. The cast iron coupons in the NONdisinfection and UVdisinfection reactors suffered more serious corrosion than did those in the NaClOdisinfection reactor, while there was no significant difference in corrosion behaviors between the NONdisinfection and UVdisinfection reactors. Bacterial community composition was considered the principal factor resulting in the different corrosion behaviors, and the corrosion induced by the bacterial community accounted for 30.5% ± 9.7% of the total weight loss in the NONdisinfection reactor. The partition of the yellow layer and black layer of the cast iron corrosion scales provided more specific and accurate information on the morphology, crystal structures, and bacterial community compositions for corrosion scales. Proteobacteria was the most abundant phylum, accounting for 53.8 ~ 94.2% of the total bacterial community in the corrosion scale samples, followed by Acidobacteria, Bacteroidetes, and Nitrospirae. Core bacterial community, i.e., AP-type OTUs, existed during the 1-year dynamic period, with relative abundance accounting for 85.0% ± 5.6% and 72.1% ± 11.0% of the total bacterial relative abundance in the black and yellow layers, respectively. Twelve functional genera, including four IOBs, one IRB, five NRBs, one NOB, and one SRB, were selected to establish a cycle model for Fe, N, and S metabolism. Iron-oxidizing bacteria, NRBs, IRBs, and NOBs drove the transition between NO3− and NO2–, Fe2+, and Fe3+. Oxygen acted as an electron acceptor to oxidize Fe to Fe2+ by galvanic effect, which was the primary pathway to dissolve Fe in all three reactors. Except for the above electrochemical corrosion process, Desulfovibrio was considered to accelerate the transfer of Fe0 to Fe2+ and thus result in more serious corrosion in the NONdisinfection and UVdisinfection reactors.
The authors wish to thank Mr. Kexin Guo from Xili RWP in Shenzhen for providing the constant support on the experimental space and reactor setup.
This work was financially supported by the National Natural Science Foundation of China (No. 51478238) and the Development and Reform Commission of Shenzhen Municipality (Urban Water Recycling and Environment Safety Program).
Availability of data and materials
The 16S rRNA gene sequences have been submitted to the National Centre for Biotechnology information (NCBI) Sequence Read Archive (SRA) under the accession number PRJNA486058.
GJZ, BL, and YTG designed this study. GJZ, JL, and MQL conducted the experiments. GJZ, JL, LY, KY, and XTJ analyzed the data. GJZ, BL, and YTG contributed to drafting the initial manuscript, and all co-authors revised, read, and approved the final manuscript.
Ethics approval and consent to participate
The manuscript does not report data collected from humans or animals.
Consent for publication
The manuscript does not contain any individual person’s data in any form.
The authors declare that they have no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
- 1.Mohebbi H, Li CQ. Experimental investigation on corrosion of cast iron pipes. Int J Corros. 2011;1:383–9.Google Scholar
- 4.Qi B, Cui C, Yuan Y. Effects of iron Bacteria on cast iron pipe corrosion and water quality in water distribution systems. Int J Electrochem Sci. 2015;10:545–58.Google Scholar
- 16.Olli HT, Tariq MB, Jerry MB, et al. Oxidative dissolution of Arsenopyrite by mesophilic and moderately thermophilic Acidophilest. Appl Environ Microbiol. 1994;60(9):3268–74.Google Scholar
- 23.Ministry of Environmental Protection, China. Analysis method for water and wastewater. 4th ed. Beijing: Press of Chinese Environmental Science; 2002.Google Scholar
- 31.Schloss PD, Westcott SL, Ryabin T, Hall JR, Hartmann M, Hollister EB, Lesniewski RA, Oakley BB, Parks DH, Robinson CJ, Sahl JW, Stres B, Thallinger GG, Van Horn DJ, Weber CF. Introducing Mothur: open-source, platform-independent, community-supported software for describing and comparing microbial communities. Appl Environ Microbiol. 2009;75(23):7537–41.PubMedPubMedCentralCrossRefGoogle Scholar
- 33.Hammer O, Davis AT, Harper, Paul DR. PAST: Paleontological Statistics Software Package for education and data analysis. Palaeontol Electron. 2001;4(1):1–9.Google Scholar
- 44.Zhou J, He Q, Hemme CL, Mukhopadhyay A, Zhou A, He Z, Van Nostrand J, Hazen TC, Stahl DA, Wall JD, Arkin AP. How sulphate-reducing microorganisms cope with stress: lessons from systems biology. Nat Rev Microbiol. 2011;9:452–66.Google Scholar
- 45.Parks DH, Tyson GW, Hugenholtz P, Beiko RG. STAMP: statistical analysis of taxonomic and functional profiles. Bioinformatics. 2014;30(21):3123–4.Google Scholar
Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated.