Abstract
The thermal behavior of antiferromagnets FeBO3 and Fe3BO6 is investigated according to the low-temperature powder X-ray diffraction data. Unit cell parameters were refined by the Rietveld method. The coefficients of thermal expansion are calculated. The interrelation between the expansion and crystal structure is described.
Similar content being viewed by others
REFERENCES
Sokolov, B.Yu., Effect of low-symmetry mechanical stresses on the magnetic properties of iron borate, Tech. Phys., 2006, vol. 51, no. 5, pp. 589–594.
Buchel’nikov, V.D., Dan’shin, N.K., Dolgushin, D.M., Izotov, A.I., Shavrov, V.G., Tsymbal, L.T., and Takagi, T., Specific features of magnetoacoustic waves in Fe3BO6, Phys. Solid State, 2005, vol. 47, no. 10, pp. 1886–1891.
Potapkin, V., Chumakov, A.I., Smirnov, G.V., Celse, J.P., Ruffer, R., McCammon, C., and Dubrovinsky, L., The 57Fe synchrotron mossbauer source at the ESRF, J. Synchrotr. Rad., 2012, vol. 19, pp. 559–569.
Tian, J., Wang, B., Zhao, F., Ma, X., Liu, Y., Liu, H.K., and Huang, Zh., Highly active Fe3BO6 as an anode material for sodium-ion batteries, Chem. Commun., 2017, vol. 53, pp. 4698–4701.
Yagupov, S., Strugatsky, M., Seleznyova, K., Mogilenec, Yu., Milyukova, E., Maksimova, E., Nauhatsky, I., Drovosekov, A., Kreines, N., and Kliava, J., Iron borate films: synthesis and characterization, J. Magn. Magn. Mater., 2016, vol. 417, no. 1, pp. 338–343.
Li, Sh., Xu, L., Zhai, Ya., and Yu, H., Co-pyrolysis synthesis of Fe3BO6 nanorods as high performance anodes for lithium-ion batteries, RSC Adv., 2014, vol. 4, pp. 8245–8249.
Ram, S., Kumari, K., and Kotnala, R.K., Synthesis of norbergite Fe3BO6 of single crystallites from a borate glass, Trans. Indian Ceram. Soc., 2010, vol. 69, no. 3, pp. 165–170.
Diehl, R., Crystal structure refinement of ferric borate, FeBO3, Solid State Commun., 1975, vol. 17, pp. 743–745.
White, J.G., Miller, A., and Nielsen, R.E., Fe3BO6, a borate isostructural with the mineral norbergite, Acta Crystallogr., 1965, vol. 19, no. 1, pp. 1060–1061.
Biryukov, Ya.P., Bubnova, R.S., Filatov, S.K., and Goncharov, A.G., Synthesis and thermal behavior of Fe3O2(BO4) oxoborate, Glass Phys. Chem., 2016, vol. 42, no. 2, pp. 202–206.
Bubnova, R.S., Firsova, V.A., Filatov, S.K., and Volkov, S.N., Rietveldtotensor: Program for processing powder X-ray diffraction data under variable conditions, Glass Phys. Chem., 2018, vol. 44, no. 1, pp. 33–40.
Momma, K. and Izumi, F., VESTA 3 for three-dimensional visualization of crystal, volumetric and morphology data, J. Appl. Crystallogr., 2011, vol. 44, pp. 1272–1276.
Bubnova, R.S. and Filatov, S.K., Self-assembly and high anisotropy thermal expansion of compounds consisting of TO3 triangular radicals, Struct. Chem., 2016, vol. 27, no. 6, pp. 1647–1662.
ACKNOWLEDGMENTS
The X-ray diffraction experiments were performed at the Centre for X-ray Diffraction Studies (Saint Petersburg State University).
The authors are grateful to Dr. M.G. Krzhizhanovskaya (Institute of Earth Sciences, Department of Crystallography, Saint Petersburg State University) for conducting the high-temperature X-ray powder diffraction experiment.
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated by D. Marinin
Rights and permissions
About this article
Cite this article
Biryukov, Y.P., Bubnova, R.S., Dmitrieva, N.V. et al. Thermal Behavior of Antiferromagnets FeBO3 and Fe3BO6 at Negative Temperatures. Glass Phys Chem 45, 147–149 (2019). https://doi.org/10.1134/S1087659619020032
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1087659619020032