Abstract
The possibilities of improving the strength characteristics of alloys based on aluminum and niobium are studied. It is established that the use of scandium allows finely dispersed hardening intermetallide phases to be obtained. The maximum effect of dispersion hardening is observed upon annealing an alloy with the composition Al 99.0 at %, Nb 0.7 at %, and Sc 0.3 at % for 54 h at 300°С.
Similar content being viewed by others
REFERENCES
E. F. Kazakova, N. E. Dmitrieva, and S. F. Dunaev, Mosc. Univ. Chem. Bull. 70, 34 (2015).
N. E. Dmitrieva, E. F. Kazakova, and S. F. Dunaev, in Proceedings of the 3rd International Symposium on Nanomaterials and Environment, Moscow, Russia, June 8–10, 2016.
V. V. Zakharov, V. I. Elagin, Yu. A. Filatov, et al., Tekhnol. Legkikh Splavov, No. 4, 20 (2006).
B. G. Korshunov, A. M. Reznik, and S. A. Semenov, Scandium (Metallurgiya, Moscow, 1987), p. 184 [in Russian].
V. I. Dobatkin and V. I. Elagin, Granulated Aluminium Alloys (Metallurgiya, Moscow, 1981), p. 190 [in Russian].
E. M. Sokolovskaya, E. F. Kazsakova, V. K. Portnoi, et al., Moscow Univ. Chem. Bull. 49 (3), 43 (1994).
Yu. I. Rusnyak, E. F. Kazakova, and T. P. Loboda, Metalloved. Term. Obrab. Met., No. 9, 25 (2009).
ACKNOWLEDGMENTS
This work was supported by the Russian Science Foundation, project no. 14-50-00126.
Author information
Authors and Affiliations
Corresponding authors
Additional information
Translated by L. Mosina
Rights and permissions
About this article
Cite this article
Kazakova, E.F., Dmitrieva, N.E. & Kustov, L.M. Formation of Finely Dispersed Structures in Aluminum Alloys with Niobium in the Presence of Scandium. Russ. J. Phys. Chem. 92, 2362–2367 (2018). https://doi.org/10.1134/S003602441812018X
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S003602441812018X