Abstract
The main aim of this work is to evaluate the effects of the plasma nitriding process on AISI M2 tool steel. In previous work, treatment time and temperature were varied to identify the treatment conditions for good wear behaviour. In the present work, the treatment time was fixed while temperature and gas pressure were varied. Samples were characterised by glow discharge optical spectroscopy, scanning electron microscopy, X‐ray diffraction, surface microhardness and wear test. The specimens nitrided at 400 and 900 Pa showed the best wear performance, which is possibly due to reduction of the friction coefficient and the low adhesive wear observed. Samples processed at 200 Pa showed spalling during the wear test, indicating a brittle surface.
Similar content being viewed by others
References
H.J. Brading, P.H. Morton and T. Bell, Surf. Eng. 3 (1992) 206.
H.Y. Chen, H.R. Stock and P. Mayr, Surf. Coat. Technol. 64 (1964) 139.
J. Lanagan, Transactions of the Institute of Metal Finishing 62(2) (1991) 50.
G. Krauss,Steels: Heat Treatment and Processing Principles (ASM International, 1990).
B. Edenhofer, Heat Treat. Metals 2 (1974) 59.
M. Tier, A. Bloyce, T. Bell and T.R. Strohaecker, in:Surface Modification Technologies XI, eds. T.S. Sudarshan, M. Jeandin and K.A. Khor (IOM Communications Ltd., London, 1998) p. 887.
B. Edenhofer, Heat Treat. Metals 1 (1974) 23.
C. Ruset, Heat Treat. Metals 3 (1991) 81.
A. Leyland, K.F. Fancey, A.S. James and A. Matthews, Surf. Coat. Technol. (1990) 41.
M.A. Pessin, A.S. Rocha, M.D. Tier and T.R. Strohaecker, in:2nd Int. Congr. Metallurgy and Materials Technology (CD-ROM annals), São Paulo, Brazil, October 1997.
Y. Sun and T. Bell, Mater. Sci. Eng. A 140 (1991) 419.
M.D. Tier, T.R. Strohaecker, T. Bell and M.A. Pessin, IV Seminário de Desgaste ABM (annals), Sáo Paulo, Brazil, July 1998, p. 443.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Pessin, M., Tier, M., Strohaecker, T. et al. The effects of plasma nitriding process parameters on the wear characteristics of AISI M2 tool steel. Tribology Letters 8, 223–228 (2000). https://doi.org/10.1023/A:1019199604963
Issue Date:
DOI: https://doi.org/10.1023/A:1019199604963