Abstract
The microstructure and mechanical properties of MMC-MMC and Al2O3-MMC joints (MMC is metal matrix composite) produced at a bonding temperature of 853 K using copper foils ranging in thickness from 10 to 30 μm were examined. The particle segregation tendency during transient liquid-phase (TLP) bonding of aluminium-based MMC material markedly increases when the aluminium-based composite material contains large number of small radius (less than 10 μm) reinforcing particles. Also, the particle segregation tendency is much greater in dissimilar Al2O3-MMC joining since the rate of solid-liquid interface movement is much slower and the time required for completing the isothermal solidification during TLP bonding is much longer. The particle segregation tendency during MMC-MMC and Al2O3-MMC bonding can be counteracted using a combination of a short (1 min) holding time at the bonding temperature (853 K) and subsequent post-weld heat treatment at 773 K for 4 h. This TLP-bonding-heat-treatment cycle removes the retained eutectic phase present at the joint centreline.
Similar content being viewed by others
References
Y ZHOU, W. F. GALE and T. H. NORTH, Int. Mater. Rev. 40 (1996) 181.
Z. LI, Y. ZHOU and T. H. NORTH, J. Mater. Sci. 30 (1995) 1075.
Z. LI, W. FEARIS and T. H. NORTH, Mater. Sci. Technol. 11 (1995) 363.
Y. ZHAI, T. H. NORTH and J. SERRATO-RODRIGUES, J. Mater. Sci. 32 (1997) 1393.
A. A. McFAYDEN, R. R. KAPOOR and T. W. EAGAR, Weld. J. 11 (1990) 339s.
T. ENJO, K. IKEUCHI, Y. MARAKAMI and N. SUZUKI, Trans. Japanese Welding Research Institute 16 (1987) 286.
D. SHANGUUAN, S. AHUJA and D. M. STEFANESCU, Metall. Trans. A 23 (1989) 669.
R. SASIKUMAR, T. R. RAMAMOHAN and B. C. PAI, Acta Metall. 39 (1989) 2085.
R. SASIKUMAR, B. K. DHINDAW, S. A. KACAR and A. MOITRA, Metall. Trans. A 39 (1991) 517.
D. M. STEFANESCU, B. K. DHINDAW, S. A. KACAR and A. MOITRA, ibid. 19 (1988) 2847.
T. SHINODA, H. LIU and Y. MISHIMA, Mater. Sci. Technol. A 146 (1991) 91.
I. TUAH-POKU, M. DOLLAR and T. B. MASSALSKI, Metall. Trans. A 19 (1988) 675.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
ZHAI, Y., NORTH, T.H. Counteracting particulate segregation during transient liquid-phase bonding of MMC-MMC and Al2O3-MMC joints. Journal of Materials Science 32, 5571–5575 (1997). https://doi.org/10.1023/A:1018624507922
Published:
Issue Date:
DOI: https://doi.org/10.1023/A:1018624507922