Abstract
Al2O3 matrix composites with unidirectionally oriented high-purity Al2O3 fibre with and without carbon coating, were fabricated by the filament-winding method, followed by hot-pressing at 1573–1773 K. The composite with non-coated Al2O3 fibre exhibited a bending strength (594 MPa) comparable to that of monolithic Al2O3 (589 MPa). While the composite with a carbon-coated fibre had lower strength (477 MPa), it showed improved fracture toughness (6.5 MPa m1/2) compared to the composite with an uncoated fibre (4.5 MPa m1/2) and monolithic Al2O3 (5.5 MPa m1/2). This toughness enhancement was explained based on the increased crack extension resistance caused by the fibre pull-out observed by SEM at the notch tip.
Similar content being viewed by others
References
L. C. LEV and A. S. ARGON, Ceram. Eng. Sci. Proc. 15 (1994) 743.
N. IWASHITA, Y. SAWADA, K. SHIMIZU, S. SHINKE and H. SHIOYAMA, Carbon 33 (1995) 405.
Chemical Society of Japan (ed.), “Kagaku Binran”, 3rd Edn (Maruzen, Tokyo, 1984) p. II–92.
S. M. WIEDERHORN, in “Fracture Mechanics of Ceramics”, Vol. 2, edited by R. C. Bradt, D. P. H. Hasselman and F. F. Lange (Plenum Press, New York, 1974) pp. 613–46.
A. G. EVANS, J. Mater. Sci 7 (1972) 1137.
S. M. WIEDERHORN, B. J. HOCKEY and D. E. ROBERTS, Philos. Mag. 28 (1973) 783.
H. HUBNER and W. JILLEK, J. Mater. Sci. 12 (1977) 117.
J. J. BRENNAN and K. M. PREWO, ibid. 17 (1982) 2371.
D. C. PHILLIPS, ibid. 7 (1972) 1175.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
UENO, K., INOUE, T. & MITSUHATA, T. Preparation and mechanical properties of high-purity Al2O3 fibre/Al2O3 matrix composite. Journal of Materials Science 32, 2031–2035 (1997). https://doi.org/10.1023/A:1018506301909
Published:
Issue Date:
DOI: https://doi.org/10.1023/A:1018506301909