Journal of Materials Science

, Volume 32, Issue 18, pp 4991–4997 | Cite as

Structural effects of interaction between lanthanum cuprate and cerium dioxide

  • I. E Mukovozov
  • A. M Ezerets
  • A. V Vishniakov
  • L Forni
  • C Oliva
Article

Abstract

In the present work the structural effects of La2CuO4 doping with CeO2, or of supporting the former on the latter, have been investigated. It was found that lanthanum oxide possesses a very good solubility in cerium dioxide in the presence of copper oxide, forming a solid solution. According to our experimental data, at 1050 °C and in the presence of copper oxide (over 1.5% mass), the boundary for the existence of the Ce1-zLazO2-z/2-δ phase falls between z = 0.398 and z = 0.462. Copper oxide itself has a very low, but appreciable solubility in this system. The excess of CuO strongly increases the rate of formation of the solid oxides solution, due to its relatively low melting point.

Keywords

Solid Solution Electron Paramagnetic Resonance Lanthanum Copper Oxide Electron Paramagnetic Resonance Signal 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    N. MIZUNO, Catalysis Today 8 (1990) 221.CrossRefGoogle Scholar
  2. 2.
    N. MIZUNO, M. YAMATO, M. TANAKA and M. MISONO, J. Catal. 132 (1991) 560.CrossRefGoogle Scholar
  3. 3.
    Y. TOKURA, H. TAKAGI and S. UCHIDA, Nature 337 (1989) 345.CrossRefGoogle Scholar
  4. 4.
    G. H. KWEI, S.-W. CHEONG, Z. FISK, F. H. GARZON, J. A. GOLDSTONE and J. D. THOMPSON, Phys. Rev. B40 (1989) 9370.CrossRefGoogle Scholar
  5. 5.
    K. TABATA, I. MATSUMOTO, S. KOHIKI and M. MISONO, J. Mater. Sci. 22 (1987) 4031.CrossRefGoogle Scholar
  6. 6.
    R. DOSHI, C. B. ALCOCK, N. GUNASEKARAN and J. J. CARBERRY, J. Catal. 140 (1993) 557.CrossRefGoogle Scholar
  7. 7.
    P. G. HARRISON, D. A. CREASER, B. A. WOLFINDALE, K. C. WAUGH, M. A. MORRIS and W. C. MACKRODT, in “Catalysis and surface characterisation”, edited by T. J. Dines, C. H. Rochester and J. T. Thomson. (The Royal Society of Chemistry, Special Publication no. 114, Cambridge, 1992) p. 76.Google Scholar
  8. 8.
    Selected powder diffraction data, Vols. 1-40. JCPDS, Swarthmore, PA, 1974-1992.Google Scholar
  9. 9.
    J. A. ANDERSON and J. L. G. FIERRO, J. Solid State Chem. 108 (1994) 305.CrossRefGoogle Scholar

Copyright information

© Chapman and Hall 1997

Authors and Affiliations

  • I. E Mukovozov
    • 1
  • A. M Ezerets
    • 2
  • A. V Vishniakov
  • L Forni
  • C Oliva
  1. 1.D. I. Mendeleev University of Chemical Technology of RussiaMoscowRussia
  2. 2.Dipartimento di Chimica Fisica ed ElettrochimicaUniversita di MilanoMilanoItaly

Personalised recommendations