Microstructure and Hardness of T250 Maraging Steel in Heat Affected Zone

  • De-feng Mo
  • Zheng-fei Hu
  • Shu-juan Chen
  • Chun-xu Wang
  • Guo-qiu He
Article

Abstract

Electron-beam (EB) welding was used in T250 maraging steel, microstructures of both base material and heat affected zone (HAZ) were investigated by optical microscopy (OM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM), and microhardness was tested. The results showed that during EB welding, the HAZ of T250 maraging steel exhibited a continuous gradient structure. The microstructure of the entire HAZ, from fusion line, could be divided into four zones: fusion zone, overheated zone, transition zone, and hardened zone. The microhardness showed a distinct regularity in each area. The softest region was the fusion zone, whereas the hardest was the hardened zone. In the overheated zone, the hardness increased as the grain size decreased. Furthermore, in the transition zone, the hardness level dropped noticeably. The peak temperature during the thermal cycle had a great influence on the formation of reverted austenite and dissolution of the precipitated particles, which contributed a lot to the microstructure and hardness of this material.

Key words

T250 maraging steel electron-beam weld microstructure microhardness 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    Pardal J M, Tavares S S M, Terra V F, et al. Modeling of Precipitation Hardening During the Aging and Overaging of 18Ni-Co-Mo-Ti Maraging 300 Steel [J]. Journal of Alloys and Compounds, 2005, 393(1–2): 109.CrossRefGoogle Scholar
  2. [2]
    Fathy Ayman, Mattar Taha. Mechanical Properties of New Low-Nickel Cobalt-Free Maraging Steels [J]. Steel Research, 2002, 73(12): 549.CrossRefGoogle Scholar
  3. [3]
    ZHANG Jian-guo, SHI Yan-ling, ZHENG Shu-li. Research and Applications of Cobalt-Free Maraging Steels [J]. Heat Treatment of Metals, 2007, 32(2): 7 (in Chinese).Google Scholar
  4. [4]
    Akhtar F, Lian Y D, Islam S H, et al. A New Kind of Age Hardenable Martensitic Stainless Steel With High Strength and Toughness [J]. Ironmaking and Steelmaking, 2007, 34(4): 285.CrossRefGoogle Scholar
  5. [5]
    Shamantha C R, Narayanan R, Iyer K J L, et al. Microstructural Changes During Welding and Subsequent Heat Treatment of 18Ni (250-Grade) Maraging Steel [J]. Materials Science and Engineering, 2000, 287A(1): 43.CrossRefGoogle Scholar
  6. [6]
    Banas G, Elsayed-Ali H E. Laser Shock-Induced Mechanical and Microstructural Modification of Welded Maraging Steel [J]. Journal of Applied Physics, 1990, 67(5): 2380.CrossRefGoogle Scholar
  7. [7]
    Sinha P P, Sivakumar D. Austenite Reversion in 18 Ni Co-Free Maraging Steel [J]. Steel Research, 1995, 66(11): 490.CrossRefGoogle Scholar
  8. [8]
    Reddy G Madhusudhan, Mohandas T, Rao A Sambasiva, et al. Influence of Welding Processes on Microstructure and Mechanical Properties of Dissimilar Austenitic-Ferritic Stainless Steel Welds [J]. Materials and Manufacturing Processes, 2005, (20): 147.CrossRefGoogle Scholar
  9. [9]
    Prasad Rao K, Venkitakrishnan P V. Electron Beam Welding of M-250 Grade Maraging Steel [J]. Praktische Metallographie, 1993, 30(3): 129.Google Scholar
  10. [10]
    CHEN Xiao-feng, LI Jia-han, LI Zhong-ku, et al. Study on Local Heat Transfer of 18Ni Maraging Steel After Electron Beam Welding [J]. Steel Research, 1994, 65(12): 557.CrossRefGoogle Scholar
  11. [11]
    HU Zheng-fei, MO De-feng, WANG Chun-xu, et al. Different Behavior in Electron Beam Welding of 18 Ni Co-Free Maraging Steels [J]. Journal of Materials Engineering and Performance, 2007, 17(5): 767.CrossRefGoogle Scholar
  12. [12]
    MA Cheng-yong, TIAN Zhi-ling, DU Ze-yu, et al. Characterization of the Microstructure and Hardness of the HAZ in a 800 MPa Grade RPC Steel [J]. China Welding, 2005, 14(1): 48.Google Scholar

Copyright information

© China Iron and Steel Research Institute Group 2009

Authors and Affiliations

  • De-feng Mo
    • 1
  • Zheng-fei Hu
    • 1
  • Shu-juan Chen
    • 1
  • Chun-xu Wang
    • 2
  • Guo-qiu He
    • 1
  1. 1.School of Material Science and EngineeringTongji UniversityShanghaiChina
  2. 2.Central Iron and Steel Research InstituteBeijingChina

Personalised recommendations