The wear behavior and mechanism of TC11 (pins) and AISI M2 (disks) under different test conditions were studied. The results show that tribo-layers formed on the worn surfaces of both TC11 alloy and AISI M2 steel. As for TC11 alloys at 25 °C, the wear rate increased to high values with an increase in the load; and abrasive wear and adhesive wear prevailed. However, at 600 °C, the wear rate decreased sharply and oxidative wear prevailed. As for AISI M2 steels, at 25 and 600 °C, the wear rates were relatively low. The wear mechanisms at 25 and 600 °C were abrasive wear and oxidative wear, respectively. The wear rates of AISI M2 steel were lower than those of TC11 alloy at 25 and 600 °C. The wear performance of the tribo-pair was noticed to be closely related to their mutual contact mode except for the test conditions and the pin and disk materials, and the intermittent contact mode reduced wear of AISI M2 steel.
Similar content being viewed by others
References
D.A. Rigney, Wear 152 (1992) 187–192.
W.M. Ke, F.C. Zhang, Z.N. Yang, M. Zhang, Mater. Charact. 82 (2013) 120–129.
E. Marui, N. Hasegawa, H. Endo, K. Tanaka, T. Hattori, Wear 205 (1997) 186–199.
M.J. Ghazali, W.M. Rainforth, H. Jones, Tribol. Int. 40 (2007) 160–169.
Z.R. Yang, M.X. Wei, Y.T. Zhao, S.Q. Wang, Trans. Nonferrous Met. Soc. China 11 (2011) 2584-2591.
E.M. Abdel-Wahab, Mater. Sci. Eng. A 473 (2008) 330–335.
H.W. Song, S.H. Zhang, M. Cheng. J. Alloy. Compd. 480 (2009) 922–927.
M.V. Berdin, L.A. Karavaeav, L.A. Syutina, S.K. Nurieva, Met. Sci. Heat Treat. 46 (2004) 54–60.
Y. Gu, F.H. Gu, Y.L. Qi, C.Q. Xia, X. Xiong, Mater. Sci. Eng. A 575 (2013) 74–85.
D.H. Lu, M.Y. Gu, Z.L. Shi, Tribol. Lett. 6 (1999) 57–61.
D.A. Rigney, Wear 245 (2000) 1–9.
J.L. Young Jr, D. Kuhlmann-Winsdorf, R. Hull, Wear 246 (2000) 74–90.
G. Straffelini, A. Molinari, Wear 236 (1999) 328–338.
A. Molinari, G. Straffelini, B. Tesi, T. Bacci, Wear 208 (1997) 105–112.
M. Qiu, Y.Z. Zhang, J.H. Yang, J. Zhu, Mater. Sci. Eng. A 434 (2006) 71–75.
M. Qiu, Y.Z. Zhang, J.H. Yang, J. Zhu, Tribology 23 (2006) 203–207.
Y.S. Mao, L. Wang, K.M. Chen, S.Q. Wang, X.H. Cui, Wear 297 (2013) 1032–1039.
X.H. Cui, Y.S. Mao, M.X. Wei, S.Q. Wang, Tribol. Trans. 55 (2012) 185–190.
L. Wang, S.Q. Wang, H.Y. Ding, A.H. Liu, Tribology 36 (2016) 592–598.
L. Wang, H.Y. Ding, A.H. Liu, S.Q. Wang, Rare Met. Mater. Eng. 46 (2017) 2449–2454.
M.O. Alam, A.S.M.A. Haseeb, Tribol. Int. 35 (2002) 357–362.
R.S. Magaziner, V.K. Jain, S. Mall, Wear 267 (2009) 368–373.
M.C. Gui, S.B. Kang, J.M. Lee, Wear 240 (2000) 186–198.
A. Pauschitza, M. Roy, F. Franek, Tribol. Int. 41 (2008) 584–602.
P.J. Blau, Tribol. Int. 43 (2010) 1203–1208.
M.X. Wei, S.Q. Wang, L. Wang, X.H. Cui, K.M. Chen, J. Iron Steel Res. Int. 19 (2012) No. 5, 50–57.
M.J. Ghazali, W.M. Rainforth, M.Z. Omar, J. Mater. Process. Technol. 201 (2008) 662–668.
S.Q. Wang, M.X. Wei, Y.T. Zhao, Wear 269 (2010) 424–434.
Q.Y. Zhang, S.Q. Wang, L. Wang, Appl. Mech. Mater. 331 (2013) 559–562.
M.X. Wei, S.Q. Wang, K.M. Chen, X.H. Cui, Wear 272 (2011) 110–121.
Acknowledgements
This work is financially supported by Jiangsu Provincial Key Laboratory for Interventional Medical Devices (No. jr1506) and the initial fund of Jiangsu University Senior Talent (No. 15JDG076) is gratefully acknowledged.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Wang, L., Yang, Jh., Li, Y. et al. Wear behavior of TC11 and AISI M2 in pin–disk tribo-system. J. Iron Steel Res. Int. 26, 490–500 (2019). https://doi.org/10.1007/s42243-019-00246-6
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s42243-019-00246-6