Comparison of shear bond strengths between a mica-based glass-ceramic and human dentin using three different resin cements

  • Research
  • Published:
Journal of the Australian Ceramic Society Aims and scope Submit manuscript

Abstract

Three resin cements, RelyX™ Ultimate, Panavia F2.0 and RelyX™ U200, were evaluated for their bond strengths between a mica glass-ceramic and human dentin. This research shows that a self-etch dental cement resin system, Panavia F2.0 provided the best bond strength. The glass-ceramic was produced and phases analysed. Biaxial flexural strength and hardness were measured and found to be comparable to that of human enamel and dentin. Bond strength was measured before and after thermocycling. Thermocycling was found to reduce the bond strength. Thermocycling reduced the shear bond strengths of all adhesives by 50–60%. The two-way ANOVA test was used to analyse the data (p = 0.05). Failure modes were analysed, showing failure predominately at the cement/glass-ceramic and dentin/resin cement interfaces. Failure modes changed after thermocycling. The resin cement bond between the dentin and mica glass-ceramics interfaces was examined for failure by optical microscopy (OM) and scanning electron microscopy (SEM).

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7

Similar content being viewed by others

References

  1. Richard, V.N.: All-ceramic restorative: high-strength core ceramics. In: Alison, T., Fiona, C. (eds.) Introduction to dental materials, pp. 205–208. Mosby, Elsevier Inc., London (2013)

    Google Scholar 

  2. Rosenblum, M.A., Schulman, A.: A review of all-ceramic restorations. J. Am. Dent. Assoc. 128(3), 297–307 (1997). https://doi.org/10.14219/jada.archive.1997.0193

    Article  Google Scholar 

  3. Stephen, R., Martin, L., Junhei, F.: Tooth preparation for all-ceramic restorations. In: John, D., Courtney, S. (eds.) Contemporary fixed prosthodontics, pp. 262–271. Mosby, Elsevier Inc., China (2006)

    Google Scholar 

  4. Ozer, A., Soygun, K., Bolayir, G.: The surface and phase analysis studies on dental bioceramics subjected to different mouthrinse solutions. J Aust Ceram Soc. (2018). https://doi.org/10.1007/s41779-018-0174-7

  5. El-Meliegy, E., Noort, R.V.: Machinable Mica dental glass-ceramics. In: El-Meliegy, E., Noort, R.V. (eds.) Glasses and glass ceramics for medical applications, pp. 193–208. Springer, New York (2012)

    Chapter  Google Scholar 

  6. Bai, J., Chaysuwan, D.: Nucleation, crystallization and characterization of mica-based glass-ceramics with fluorapatite. Adv Mater Res. 936, 164–169 (2014)

    Article  Google Scholar 

  7. Bai, J., Chaysuwan, D.: Development of mica-based glass-ceramic with 4 Mol% of fluorapatite. Adv Mater Res. 1077, 8–13 (2015)

    Google Scholar 

  8. Chaysuwan, D., Sirinukunwattana, K., Kanchanatawewat, K., Heness, G., Yamashita, K.: Machinable glass-ceramics forming as a restorative dental material. Dent Mater J. 30(3), 358–367 (2011)

    Article  Google Scholar 

  9. Srichumpong, T., Suputtamongkol, K., Chinpanuwat, W., Nampachoke, P., Bai, J., Angkulpipat, S., Prasertwong, S., Chaysuwan, D.: Effect of heat treatment time on properties of mica-based glass-ceramics for restorative dental materials. Key Eng Mater. 702, 23–27 (2016)

    Article  Google Scholar 

  10. Wei, W., Yong, L., Tan, Y., Grover, L., Guo, Y., Bowei, L.: A mica/nepheline glass-ceramic prepared by melting and powder metallurgy at low temperatures. Mater. Today Commun. 11(Supplement C), 87–93 (2017). https://doi.org/10.1016/j.mtcomm.2017.02.007

    Article  Google Scholar 

  11. ISO 6872:2015. Dentistry—ceramic materials. Geneva, Switzerland: International Organization for Standardization. (2015)

  12. ASTM C1327-08. Standard test method for Vickers indentation hardness of advanced ceramics. West Conshohocken, PA: American Society for Testing and Materials. (2008)

  13. Kim, B.-K., Bae, H.E.-K., Shim, J.-S., Lee, K.-W.: The influence of ceramic surface treatments on the tensile bond strength of composite resin to all-ceramic coping materials. J Prosthet Dent. 94(4), 357–362 (2005). https://doi.org/10.1016/j.prosdent.2005.08.012

    Article  Google Scholar 

  14. Nagayassu, M.P., Shintome, L.K., Uemura, E.S., Araujo, J.E.: Effect of surface treatment on the shear bond strength of a resin-based cement to porcelain. Braz Dent J. 17(4), 290–295 (2006)

    Article  Google Scholar 

  15. Holderegger, C., Sailer, I., Schuhmacher, C., Schlapfer, R., Hammerle, C., Fischer, J.: Shear bond strength of resin cements to human dentin. Dent Mater. 24(7), 944–950 (2008). https://doi.org/10.1016/j.dental.2007.11.021

    Article  Google Scholar 

  16. Altintas, S., Eldeniz, A.U., Usumez, A.: Shear bond strength of four resin cements used to lute ceramic core material to human dentin. J Prosthodont. 17(8), 634–640 (2008). https://doi.org/10.1111/j.1532-849X.2008.00348.x

    Article  Google Scholar 

  17. Kumbuloglu, O., Lassila, L.V., User, A., Toksavul, S., Vallittu, P.K.: Shear bond strength of composite resin cements to lithium disilicate ceramics. J Oral Rehabil. 32(2), 128–133 (2005). https://doi.org/10.1111/j.1365-2842.2004.01400.x

    Article  Google Scholar 

  18. Kanchanavasita, W., Rungnava, P., Mat-Ran, S.: Microtensile bond strength between a lithium disilicateglass-ceramic or a Y-TZP zirconia ceramic bonded to dentin when using two self-etch, self-adhesive resin cements compared with an adhesive resin cement. Mahidol. Dent. J. 33(2), 65–72 (2013)

    Google Scholar 

  19. Denry, I.L., Holloway, J.A., Nakkula, R.J., Walters, J.D.: Effect of niobium content on the microstructure and thermal properties of fluorapatite glass-ceramics. J. Biomed. Mater. Res. B. Appl. Biomater. 75(1), 18–24 (2005). https://doi.org/10.1002/jbm.b.30295

    Article  Google Scholar 

  20. Chun, K.J., Choi, H.H., Lee, J.Y.: Comparison of mechanical property and role between enamel and dentin in the human teeth. J Dent Biomech. 5, 1–5 (2014). https://doi.org/10.1177/1758736014520809

    Google Scholar 

  21. Chen, H., Liu, Y.: Chapter 2 - teeth. In: James, Z.S., Tomaž, K. (eds.) Advanced ceramics for dentistry, pp. 5–21. Butterworth-Heinemann, Oxford (2014)

    Chapter  Google Scholar 

  22. Carvalho, A.O., Ayres, A.P., de Almeida, L.C., Briso, A.L., Rueggeberg, F.A., Giannini, M.: Effect of peroxide bleaching on the biaxial flexural strength and modulus of bovine dentin. Eur. J. Dent. 9(2), 246–250 (2015). https://doi.org/10.4103/1305-7456.156845

    Article  Google Scholar 

  23. Blatz, M.B., Sadan, A., Arch, G.H., Lang, B.R.: In vitro evaluation of long-term bonding of Procera AllCeram alumina restorations with a modified resin luting agent. J Prosthet Dent. 89(4), 381–387 (2003). https://doi.org/10.1067/mpr.2003.89

    Article  Google Scholar 

  24. Ozcan, M., Kerkdijk, S., Valandro, L.F.: Comparison of resin cement adhesion to Y-TZP ceramic following manufacturers’ instructions of the cements only. Clin Oral Investig. 12(3), 279–282 (2008). https://doi.org/10.1007/s00784-007-0151-y

    Article  Google Scholar 

  25. Özcan, M., Mese, A.: Adhesion of conventional and simplified resin-based luting cements to superficial and deep dentin. Clin Oral Investig. 16(4), 1081–1088 (2012). https://doi.org/10.1007/s00784-011-0594-z

    Article  Google Scholar 

  26. Gürol, O., Funda, Y., Dilek, T., Nuran, O., Mustafa, O.: Shear bond strength of composite resin cements to ceramics. J. Marmara Univ. Dent. Fac. 2, 61–66 (2013)

    Google Scholar 

  27. Sirimongkolwattana, S., Phanpaisan, P., Jittidecharaks, S., Tagami, J.: Bond strength between self-adhesive cement and dentin using self-etch bonding. CM Dent. J. 36(2), 81–88 (2015)

    Google Scholar 

  28. Lee, S.-E., Bae, J.-H., Choi, J.-W., Jeon, Y.-C., Jeong, C.-M., Yoon, M.-J., Huh, J.-B.: Comparative shear-bond strength of six dental self-adhesive resin cements to zirconia. Materials. 8(6), 3306–3315 (2015). https://doi.org/10.3390/ma8063306

    Article  Google Scholar 

  29. Secilmis, A., Ustun, O., Kecik Buyukhatipoglu, I.: Evaluation of the shear bond strength of two resin cements on different CAD/CAM materials. J Adhes Sci Technol. 30(9), 983–993 (2016). https://doi.org/10.1080/01694243.2015.1134866

    Article  Google Scholar 

  30. Chen, C., He, F., Burrow, M., Xie, H., Zhu, Y., Zhang, F.: Bond strengths of two self-adhesive resin cements to dentin with different treatments. J. Med. Biol. Eng. 31, 73–77 (2011). https://doi.org/10.5405/jmbe.681

    Article  Google Scholar 

  31. Stawarczyk, B., Hartmann, R., Hartmann, L., Roos, M., Ozcan, M., Sailer, I., Hammerle, C.H.: The effect of dentin desensitizer on shear bond strength of conventional and self-adhesive resin luting cements after aging. Oper Dent. 36(5), 492–501 (2011). https://doi.org/10.2341/10-292-l

    Article  Google Scholar 

  32. Henriques, B., Gonçalves, S., Soares, D., Silva, F.S.: Shear bond strength comparison between conventional porcelain fused to metal and new functionally graded dental restorations after thermal–mechanical cycling. J. Mech. Behav. Biomed. Mater. 13(Supplement C), 194–205 (2012). https://doi.org/10.1016/j.jmbbm.2012.06.002

    Article  Google Scholar 

  33. Amornporncharoen, M., N, A., Sirimongkolwa, S.: Surface treatment of all-ceramic crown. CM Dent. J. 30, 15–22 (2009)

    Google Scholar 

  34. Jain, G., Narad, A., Boruah, L.C., Rajkumar, B.: Comparative evaluation of shear bond strength of three resin based dual-cure core build-up materials: an in-vitro study. J Conserv Dent. 18(4), 337–341 (2015). https://doi.org/10.4103/0972-0707.159754

    Article  Google Scholar 

  35. Rodrigues, R.F., Ramos, C.M., Francisconi, P.A.S., Borges, A.F.S.: The shear bond strength of self-adhesive resin cements to dentin and enamel: an in vitro study. J Prosthet Dent. 113(3), 220–227 (2015). https://doi.org/10.1016/j.prosdent.2014.08.008

    Article  Google Scholar 

  36. Hiraishi, N., Yiu, C.K., King, N.M., Tay, F.R.: Effect of pulpal pressure on the microtensile bond strength of luting resin cements to human dentin. Dent Mater. 25(1), 58–66 (2009). https://doi.org/10.1016/j.dental.2008.05.005

    Article  Google Scholar 

Download references

Acknowledgments

The authors would like to thank the Graduate School, Kasetsart University Research and Development Institute (KURDI) and Faculty of Engineering, Kasetsart University for research funding and a student scholarship, as well as the Faculty of Dentistry, Mahidol University, Bangkok, for providing analytical instruments and workspace.

Author information

Authors and Affiliations

  1. Department of Materials Engineering, Faculty of Engineering, Kasetsart University, Bangkok, 10900, Thailand

    Thapanee Srichumpong, Sukanda Angkulpipat, Sahadsaya Prasertwong, Greg Heness & Duangrudee Chaysuwan

  2. Department of Prosthodontics, Faculty of Dentistry, Mahidol University, Bangkok, 10400, Thailand

    Kallaya Suputtamongkol, Noparat Thongpun & Pimnida Phokhinchatchanan

  3. Department of Engineering “Enzo Ferrari”, University of Modena and Reggio Emilia, 41125, Modena, Italy

    Giovanni Bolelli, Paolo Veronesi & Cristina Leonelli

  4. Faculty of Science, University of Technology Sydney, Broadway, Ultimo, 2007, Australia

    Greg Heness

Authors
  1. Thapanee Srichumpong
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Kallaya Suputtamongkol
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Noparat Thongpun
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Pimnida Phokhinchatchanan
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Sukanda Angkulpipat
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Sahadsaya Prasertwong
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Giovanni Bolelli
    View author publications

    You can also search for this author in PubMed Google Scholar

  8. Paolo Veronesi
    View author publications

    You can also search for this author in PubMed Google Scholar

  9. Cristina Leonelli
    View author publications

    You can also search for this author in PubMed Google Scholar

  10. Greg Heness
    View author publications

    You can also search for this author in PubMed Google Scholar

  11. Duangrudee Chaysuwan
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Duangrudee Chaysuwan.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Srichumpong, T., Suputtamongkol, K., Thongpun, N. et al. Comparison of shear bond strengths between a mica-based glass-ceramic and human dentin using three different resin cements. J Aust Ceram Soc 55, 47–55 (2019). https://doi.org/10.1007/s41779-018-0209-0

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s41779-018-0209-0

Keywords

Search

Navigation