The Effect of Vanadium Content on Microstructure and Impact Toughness of Forged High Alloy Steel X96CrMo12-1

  • Vukoje Vukojević
  • Aleksandar Sedmak
  • Srdjan Jović
  • Blagoje Nedeljković
  • Ivo Blačić
Article
  • 22 Downloads

Abstract

The aim of this research was to examine the influence of vanadium on the structure and impact toughness of the forged high alloy steel X96CrMo12-1. It is known that vanadium affects the process of solidification of this alloy by narrowing the temperature interval of crystallization. Vanadium, as an alloying element, moves liquids and solidus lines toward higher temperatures, approximately for 25–30 °C. In addition, vanadium forms V6C5 carbides, which are partly distributed between the present phases in the steel, carbide (Cr,Fe)7C3 and austenite. The presence of vanadium enables the formation of (Cr,Fe)23C6 carbide and its precipitation into austenite during the cooling process. In local areas around fine carbide particles, austenite is transformed into martensite, i.e., vanadium reduces remained austenite and improves quenching process. Studies have shown that as the content of vanadium increases up to 5%, the impact toughness of this steel is significantly increased. The steel X96CrMo12-1 contains remarkably less carbon than high alloyed Cr–Mo ledeburite steels and does not contain a eutectic microconstituent in the structure. So it can be treated by forging process thus provide a more compact and tougher structure. The basic problem in the application of high alloyed Cr–Mo steels is to increase their impact toughness, while sustain a relatively high value of hardness. Studies have shown that vanadium strongly increases toughness while retaining high hardness, which is a requirement for wear-resistant steels.

Keywords

vanadium impact toughness hardness microstructure 

References

  1. 1.
    A. Todić, D. Čikara, T. Todić, B. Pejović, M. Mišić, I. Čamagić, The effect of vanadium content on mechanical properties and structure of self-hardening steel X160CrMo12-1. J. Mech. Eng. Autom. 3, 168–172 (2013)Google Scholar
  2. 2.
    N. Yamanaka, K. Kusaka, Influence of vanadium and molybdenum on the properties of air-hardening die steel containing 1.5% Carbon and 12% Chromium. Iron Steel Inst. Jpn. 41(6), 613–620 (1955)CrossRefGoogle Scholar
  3. 3.
    D. Čikara, M. Rakin, D. Čikara-Anič, Quality optimization of steel milling balls, in Proceedings of 18th International Conference on Material Handling, Constructions and Logistics, Belgrade, pp. 131–138 (2006)Google Scholar
  4. 4.
    A. Todić, D. Čikara, T. Todić, B. Pejović, I. Čamagić, V. Vukojević, The influnce of the vanadium content on the toughness and hardness of wear resistant high-alloyed Cr-Mo steel. FME Trans. 45(1), 130–134 (2017)CrossRefGoogle Scholar
  5. 5.
    M. Filipović, Ž. Kamberović, M. Korać, Uticaj termičke obrade na žilavost i otpornost na habanje Fe-C-Cr-Nb legura. J. Metall. 14(4), 243–252 (2008)Google Scholar
  6. 6.
    M. Filipović, Uticaj sadržaja vanadijuma i brzine hlađenja na stereološke parametre faza u strukturi Fe-C-Cr-V legura. J. Metall. 10(2), 127–138 (2004)Google Scholar

Copyright information

© American Foundry Society 2018

Authors and Affiliations

  • Vukoje Vukojević
    • 1
  • Aleksandar Sedmak
    • 2
  • Srdjan Jović
    • 1
  • Blagoje Nedeljković
    • 1
  • Ivo Blačić
    • 3
  1. 1.Faculty of Technical SciencesUniversity of Priština in Kosovska MitrovicaKosovska MitrovicaSerbia
  2. 2.Faculty of Mechanical EngineeringUniversity of BelgradeBelgradeSerbia
  3. 3.Military Technical Institute BelgradeBelgradeSerbia

Personalised recommendations